CN104088130A - Preparation process of chromotropic heat-insulating textiles - Google Patents
Preparation process of chromotropic heat-insulating textiles Download PDFInfo
- Publication number
- CN104088130A CN104088130A CN201410300582.5A CN201410300582A CN104088130A CN 104088130 A CN104088130 A CN 104088130A CN 201410300582 A CN201410300582 A CN 201410300582A CN 104088130 A CN104088130 A CN 104088130A
- Authority
- CN
- China
- Prior art keywords
- coating
- heat
- cloth
- temperature
- textiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation process of chromotropic heat-insulating textiles. The preparation process comprises the following processing steps: A, pretreatment of base cloth; B, coating of a heat-insulating paint; C, drying of the cloth coated with the heat-insulating paint; D, coating of thermosensitive chromotropic paint; E, drying of the cloth coated with the thermosensitive chromotropic paint; F, baking, namely baking the cloth obtained in the step E. The preparation process disclosed by the invention is easy in production process, the produced textiles are light, thin and soft, have good heat-insulating performance, also have a function of predicting the temperature, and can show different colors according to different temperature ranges, so that a decorative effect of new vision is achieved, people can also make judgment or take corresponding measures according to different temperatures, and the safety coefficient can also be increased while work is facilitated.
Description
Technical field
The present invention relates to present according to temperature difference the preparation technology of the textiles with heat-proof quality of different colours.
Background technology
The generation of heat-barrier material, gives and needs the people of at high temperature operation that the protection of security is provided, and can see their shadow in daily life everywhere, from curtain umbrella to proximity gloves, uses heat-barrier material safer, comfortable to our life.Thermosensitive chromotropic material is applied to textile industry and also brings new experience, also diversity increasingly of the kind of thermo-sensitive material, multi-component compound variable temperatures scope-20-200 DEG C, color is multiple, but current heat-barrier material is often a kind of heat insulation simple function, there is no the function of pre-temp. displaying function, this also makes people in the situation that not understanding temperature range, do the judgement or the operation that make mistake, thereby causes damage or even threat to life.
Summary of the invention
For the technical problem of above-mentioned existence, the object of the invention is: the preparation technology who has proposed to present according to temperature difference the textiles with heat-proof quality of different colours.
Technical solution of the present invention is achieved in that the preparation technology of the heat insulation textiles of variable color, and its processing step is as follows:
The pre-treatment of A, base cloth: textiles is carried out to pre-treatment work, for subsequent use as base cloth;
B, coating insulating moulding coating: insulating moulding coating on ready base cloth surface-coated in A;
C, oven dry: the base cloth with insulating moulding coating in B is dried, and bake out temperature is 140-150 DEG C, and the time is 2-8 minute;
D, coating temperature-sensitive allochroic paint: on the cloth obtaining in C, be coated with temperature-sensitive allochroic paint, described heat-sensitive variable colour coating is coated on insulating moulding coating;
E, oven dry: the cloth making in D is dried, and bake out temperature is 80-90 DEG C;
F, bake: the cloth obtaining in E is baked, and baking temperature is 140-150 DEG C, and the time is 3-10 minute.
Preferably, described insulating moulding coating is nanometer heat isolation paint.
Due to the utilization of technique scheme, the present invention compared with prior art has following advantages:
The preparation technology of the heat insulation textiles of variable color of the present invention, manufacture craft is simple, the textiles of producing is frivolous, softness, has good heat-proof quality, and indicates in addition the effect of temperature, can demonstrate different colors according to different temperature ranges, the decorative effect of existing new vision, people can judge or corresponding measure according to different temperature again, also can increase safety coefficient when convenient work.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described.
The preparation technology of the heat insulation textiles of variable color of the present invention, its processing step is as follows:
The pre-treatment of A, base cloth: textiles is carried out to pre-treatment work, for subsequent use as base cloth;
B, coating insulating moulding coating: in A, ready base cloth surface adds insulating moulding coating in coating; Described insulating moulding coating is nanometer heat isolation paint;
C, oven dry: the base cloth with insulating moulding coating in B is dried, and bake out temperature is 150 DEG C, and the time is 2 minutes;
D, coating temperature-sensitive allochroic paint: on the cloth obtaining in C, be coated with temperature-sensitive allochroic paint, described heat-sensitive variable colour coating is coated on insulating moulding coating; Described heat-sensitive variable colour coating belongs to color reversible heat-sensible allochroic paint, and a kind of coating that can be single uses, and also can mix use by multiple heat-sensitive variable colour coating; Wherein heat-sensitive variable colour coating is made up of two kinds of equivalent first, second, and the demonstration look of first is purple, and temperature is 50-60 DEG C; The demonstration look of second is red, and temperature is 80-90 DEG C;
E, oven dry: the cloth making in D is dried, and bake out temperature is 80 DEG C;
F, bake: the cloth obtaining in E is baked, and baking temperature is 150 DEG C, and the time is 5 minutes.
The cloth softness of selecting nanometer heat isolation paint to make, good hand touch; Heat-sensitive variable colour coating is that reversible heat-sensible allochroic paint can be realized independent assortment, shows different colors in different temperature ranges, in the time that the heating temperature of described heat insulation cloth reaches 50 DEG C, is shown as purple, when temperature shown in red during higher than 80 DEG C.
Above-described embodiment is only explanation technical conceive of the present invention and feature; its object is to allow person skilled in the art can understand content of the present invention and be implemented; can not limit the scope of the invention with this; all equivalences that Spirit Essence is done according to the present invention change or modify, and all should be encompassed in protection scope of the present invention.
Claims (2)
1. the preparation technology of the heat insulation textiles of variable color, is characterized in that: processing step is as follows:
The pre-treatment of A, base cloth: textiles is carried out to pre-treatment work, for subsequent use as base cloth;
B, coating insulating moulding coating: in A, ready base cloth surface adds insulating moulding coating in coating;
C, oven dry: the base cloth with insulating moulding coating in B is dried, and bake out temperature is 140-150 DEG C, and the time is 2-8 minute;
D, coating temperature-sensitive allochroic paint: on the cloth obtaining in C, be coated with temperature-sensitive allochroic paint, described heat-sensitive variable colour coating is coated on insulating moulding coating;
E, oven dry: the cloth making in D is dried, and bake out temperature is 80-90 DEG C;
F, bake: the cloth obtaining in E is baked, and baking temperature is 140-150 DEG C, and the time is 3-10 minute.
2. the preparation technology of the heat insulation textiles of variable color according to claim 1, is characterized in that: described insulating moulding coating is nanometer heat isolation paint.