CN104073094B - A kind of quick-drying floor paint - Google Patents
A kind of quick-drying floor paint Download PDFInfo
- Publication number
- CN104073094B CN104073094B CN201410274389.9A CN201410274389A CN104073094B CN 104073094 B CN104073094 B CN 104073094B CN 201410274389 A CN201410274389 A CN 201410274389A CN 104073094 B CN104073094 B CN 104073094B
- Authority
- CN
- China
- Prior art keywords
- parts
- quick
- polyvinyl acetate
- acetate emulsion
- floor paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of quick-drying floor paint, its raw materials by weight portion proportioning is as follows: polyvinyl acetate emulsion 100 parts；NC Nitroncellulose 15 25 parts；Polyvinyl acetate emulsion 40 50 parts；Tricresyl phosphate 35 parts；Quartz sand 45 55 parts；Oleum Ricini 20 30 parts；Deionized water 15 25 parts；Cement 60 80 parts；Pigment 5 15 parts；Tripolycyanamide 30 40 parts；Cyclohexanone peroxide 1 10 parts；10 30 parts of acetone；Plasticizer 10 20 parts；N-butyl alcohol 35 45 parts；Cobalt naphthenate 28 parts；Dimethylbenzene 50 60 parts；Wear Resistance is good, 1000 0.004 0.008g/cm2 of reciprocating testing machine；Surface drying time 0.5 1.5h, soaks non-foaming, not shedding after 11 15d in 20 DEG C of water；5 7d are soaked without exception in saturated calcium hydroxide；Film is firmly and not crisp, smooth bright and clean, good decorative property, can be with the widespread production not division of history into periods for current material.
Description
Technical field
The application belongs to paint field, particularly relates to a kind of quick-drying floor paint.
Background technology
Coating, at the entitled paint of Chinese tradition.So-called coating is to be coated in be protected or filled
The body surface of decorations, and can be with the continuous film of coated article formation firm attachment, it is common that with tree
Fat or oil or emulsion are main, add or without pigment, filler, add corresponding additive,
With the formulated thick liquid of organic solvent or quartz sand.China's coating circle is more authoritative
" coating process " book is defined such that " coating is a kind of material, and this material is permissible
Be coated in object surface by different construction technologies, formed adhere to firmly, have some strength,
Continuous print solid film.The film common name film so formed, also known as paint film or coating." coating
Cover with paint, lacquer, colour wash, etc. and can very well bond with matrix material in body surface and form complete and tough and tensile protecting film
Material, referred to as coating.Coating and paint are the identicals concept.Paint is people's habits used for a long time
Used title, after introducing China, utilizes in building trade the most always.The effect of coating can be general
Including is three aspects: protective effect, decoration function, specific function effect.General group of coating
Become: comprise film forming matter, color stuffing, solvent, auxiliary agent.Floor paint is for Indoor environment ground
The floor coating of finishing coat facing.Use floor paint facing cost low, from heavy and light, maintenance renewal
Convenience and good integrity.
Coating refers to be applied to body surface and can form the general name of the material of tough and tensile protecting film, builds
Building coating is an important class in coating, in China, typically will be used for inner wall of building,
Exterior wall, ceiling, ground, the coating of toilet is referred to as building coating.Polyvinyl acetate emulsion,
A kind of conventional white glue with vinyl, be mainly used in timber, decorative panel, sheet processing, without traditional thread binding door,
Leather goods, the wooden and bonding of cement products and printing and dyeing sticking agent etc., nothing easy to use, nontoxic
Smelly, corrosion-free piece, point D505 type, I type, II type and four kinds of models of III type, solid content 18-45%.
The major function of floor coating is decoration and protection flooring, makes floor cleaning attractive in appearance,
Hydraulic type indoor environment is together created with other ornament materials.In order to obtain good decoration effect
Really, floor coating should have the following characteristics that alkali resistance is good, cohesive force strong, water-tolerant, resistance to
Good, the anti-impact force of mill property is strong, brushing easy construction and reasonable price etc.；Floor coating typically may be used
Being divided into paint of wooden floor and cement mortar surface coating, cement mortar surface coating is divided into thin matter to be coated with
Material (point solvent-borne type and emulsion type) and thick coating (point solvent-borne type and emulsion type).And along with
Popularizing of humanity concept, and the composition of novel harmonious society, a kind of fast drying of design is wear-resisting
Property, the excellent quick-drying floor paint of resistance to water and resistant to chemical media is very important.
Summary of the invention
Solve the technical problem that:
The application is for above-mentioned technical problem, it is provided that a kind of quick-drying floor paint, solves existing quick-drying
Floor paint resistance to water and resistant to chemical media is poor, be dried slowly, the not technical problem such as rub resistance.
Technical scheme:
A kind of quick-drying floor paint, the raw materials by weight portion proportioning of described quick-drying floor paint is as follows:
Polyvinyl acetate emulsion 100 parts；NC Nitroncellulose 15-25 part；Polyvinyl acetate emulsion 40-50
Part；Tricresyl phosphate 3-5 part；Quartz sand 45-55 part；Oleum Ricini 20-30 part；Go from
Sub-water 15-25 part；Cement 60-80 part；Pigment 5-15 part；Tripolycyanamide 30-40 part；
Cyclohexanone peroxide 1-10 part；Acetone 10-30 part；Plasticizer 10-20 part；N-butyl alcohol 35-45
Part；Cobalt naphthenate 2-8 part；Dimethylbenzene 50-60 part.
As a preferred technical solution of the present invention: the raw material of described quick-drying floor paint is by weight
Number proportioning is as follows: polyvinyl acetate emulsion 100 parts；NC Nitroncellulose 20 parts；Poly-acetic acid
Vac emulsion 45 parts；Tricresyl phosphate 4 parts；Quartz sand 50 parts；Oleum Ricini 25 parts；
Deionized water 20 parts；Cement 70 parts；Pigment 10 parts；Tripolycyanamide 35 parts；Peroxidating ring
Hexanone 5 parts；20 parts of acetone；Plasticizer 15 parts；N-butyl alcohol 40 parts；Cobalt naphthenate 5 parts；
Dimethylbenzene 55 parts.
As a preferred technical solution of the present invention: described pigment uses iron oxide red.
As a preferred technical solution of the present invention: described plasticizer uses phthalic acid two
Butyl ester.
Beneficial effect:
The quick-drying floor paint of one of the present invention uses above technical scheme compared with prior art,
Have following technical effect that 1, Wear Resistance good, reciprocating testing machine 1000 times
0.004-0.008g/cm2；2, surface drying time 0.5-1.5h, soaks 11-15d in 20 DEG C of water
The most non-foaming, not shedding；3, in saturated calcium hydroxide, 5-7d is soaked without exception；4, it is coated with
Film is firmly and not crisp, smooth bright and clean, good decorative property, can be with the widespread production not division of history into periods for existing material
Material.
Detailed description of the invention
Embodiment 1:
A kind of quick-drying floor paint, its raw materials by weight portion proportioning is as follows: polyvinyl acetate emulsion
100 parts；NC Nitroncellulose 15 parts；Polyvinyl acetate emulsion 40 parts；Tricresyl phosphate 3
Part；Quartz sand 45 parts；Oleum Ricini 20 parts；Deionized water 15 parts；Cement 60 parts；Oxidation
Iron oxide red 5 parts；Tripolycyanamide 30 parts；Cyclohexanone peroxide 1 part；10 parts of acetone；Adjacent benzene two
Formic acid dibutyl ester 10 parts；N-butyl alcohol 35 parts；Cobalt naphthenate 2 parts；Dimethylbenzene 50 parts.
Dimethylbenzene is added after deionized water dissolves, add iron oxide red, quartz sand, use ball
Grinding machine ball milling 30min, add cyclohexanone peroxide, polyvinyl acetate emulsion, NC Nitroncellulose,
Polyvinyl acetate emulsion, tricresyl phosphate and Oleum Ricini, ball milling 30min, add cement and
Surplus stock, filters with gauze after ball milling 1h and both obtains finished product.
Product is at 1000 0.008g/cm of reciprocating testing machine2；Surface drying time 1.5h, at 20 DEG C
Water soaks non-foaming, not shedding after 11d；5d is soaked without exception in saturated calcium hydroxide.
Embodiment 2:
A kind of quick-drying floor paint, its raw materials by weight portion proportioning is as follows: polyvinyl acetate emulsion
100 parts；NC Nitroncellulose 25 parts；Polyvinyl acetate emulsion 50 parts；Tricresyl phosphate 5
Part；Quartz sand 55 parts；Oleum Ricini 30 parts；Deionized water 25 parts；Cement 80 parts；Oxidation
Iron oxide red 15 parts；Tripolycyanamide 40 parts；Cyclohexanone peroxide 10 parts；30 parts of acetone；Adjacent benzene
Dibutyl carboxylic acid 20 parts；N-butyl alcohol 45 parts；Cobalt naphthenate 8 parts；Dimethylbenzene 60 parts.
Dimethylbenzene is added after deionized water dissolves, add iron oxide red, quartz sand, use ball
Grinding machine ball milling 30min, add cyclohexanone peroxide, polyvinyl acetate emulsion, NC Nitroncellulose,
Polyvinyl acetate emulsion, tricresyl phosphate and Oleum Ricini, ball milling 30min, add cement and
Surplus stock, filters with gauze after ball milling 1h and both obtains finished product.
Product is at 1000 0.006g/cm of reciprocating testing machine2；Surface drying time 1h, at 20 DEG C
Water soaks non-foaming, not shedding after 13d；6d is soaked without exception in saturated calcium hydroxide.
Embodiment 3:
A kind of quick-drying floor paint, its raw materials by weight portion proportioning is as follows: polyvinyl acetate emulsion
100 parts；NC Nitroncellulose 20 parts；Polyvinyl acetate emulsion 45 parts；Tricresyl phosphate 4
Part；Quartz sand 50 parts；Oleum Ricini 25 parts；Deionized water 20 parts；Cement 70 parts；Oxidation
Iron oxide red 10 parts；Tripolycyanamide 35 parts；Cyclohexanone peroxide 5 parts；20 parts of acetone；Adjacent benzene
Dibutyl carboxylic acid 15 parts；N-butyl alcohol 40 parts；Cobalt naphthenate 5 parts；Dimethylbenzene 55 parts.
Dimethylbenzene is added after deionized water dissolves, add iron oxide red, quartz sand, use ball
Grinding machine ball milling 30min, add cyclohexanone peroxide, polyvinyl acetate emulsion, NC Nitroncellulose,
Polyvinyl acetate emulsion, tricresyl phosphate and Oleum Ricini, ball milling 30min, add cement and
Surplus stock, filters with gauze after ball milling 1h and both obtains finished product.
Product is at 1000 0.004g/cm of reciprocating testing machine2；Surface drying time 0.5h, at 20 DEG C
Water soaks non-foaming, not shedding after 15d；7d is soaked without exception in saturated calcium hydroxide.
Compositions all components in above example all can be commercially available.
Above-described embodiment is only intended to be illustrated present disclosure rather than limit, because of
This any change in the implication suitable with claims of the present invention and scope, all should
It is considered to be included within the scope of the claims.
Claims (1)
1. a quick-drying floor paint, it is characterised in that the raw material of described quick-drying floor paint is by weight
Number proportioning is as follows: polyvinyl acetate emulsion 100 parts；NC Nitroncellulose 20 parts；Poly-acetic acid
Vac emulsion 45 parts；Tricresyl phosphate 4 parts；Quartz sand 50 parts；Oleum Ricini 25 parts；
Deionized water 20 parts；Cement 70 parts；Pigment 10 parts；Tripolycyanamide 35 parts；Peroxidating ring
Hexanone 5 parts；20 parts of acetone；Plasticizer 15 parts；N-butyl alcohol 40 parts；Cobalt naphthenate 5 parts；
Dimethylbenzene 55 parts；
Described pigment uses iron oxide red；
Described plasticizer uses dibutyl phthalate.