CN104073076A - 一种氟磷乳胶漆 - Google Patents

一种氟磷乳胶漆 Download PDF

Info

Publication number
CN104073076A
CN104073076A CN201410221749.9A CN201410221749A CN104073076A CN 104073076 A CN104073076 A CN 104073076A CN 201410221749 A CN201410221749 A CN 201410221749A CN 104073076 A CN104073076 A CN 104073076A
Authority
CN
China
Prior art keywords
parts
raw material
mentioned
emulsion
fluorine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410221749.9A
Other languages
English (en)
Inventor
李世跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410221749.9A priority Critical patent/CN104073076A/zh
Publication of CN104073076A publication Critical patent/CN104073076A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氟磷乳胶漆,它是由下述重量份的原料组成的:苯丙乳液40-50、磷酸钙1-2、氟磷灰石3-4、N-乙酰基乙二胺1-2、羟乙磺酸酯1-2、肉豆蔻酸异丙酯0.3-1、羟乙基纤维素2-3、山梨醇1-2、双乙酸钠1-2、轻质碳酸钙30-40、成膜助剂5-8、去离子水32-40;本发明的乳胶漆漆膜具有较高的表面硬度,耐擦洗和抗划伤性强,对基材的保护效果好,遮盖力好,耐候性强。

Description

一种氟磷乳胶漆
 
技术领域
    本发明主要涉及涂料领域,尤其涉及一种氟磷乳胶漆。
背景技术
以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料,它是以合成树脂乳液为基料,填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点,如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等;水溶性内墙乳胶漆无污染、无毒、无火灾隐患,易于涂刷、干燥迅速,漆膜耐水、耐擦洗性好,色彩柔和。水溶性内墙乳胶漆,以水作为分散介质,无有机溶剂性毒气体带来的环境污染问题,透气性好,避免了因涂膜内外温度压力差而导致的涂膜起泡弊病,适合未干透的新墙面涂装。
发明内容
本发明目的就是提供一种氟磷乳胶漆。
本发明是通过以下技术方案实现的:
一种氟磷乳胶漆,它是由下述重量份的原料组成的:
苯丙乳液40-50、磷酸钙1-2、氟磷灰石3-4、N-乙酰基乙二胺1-2、羟乙磺酸酯1-2、肉豆蔻酸异丙酯0.3-1、羟乙基纤维素2-3、山梨醇1-2、双乙酸钠1-2、轻质碳酸钙30-40、成膜助剂5-8、去离子水32-40;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液21-30、聚乙二醇1000 3-5、植物甾醇1-2、羟丙基瓜尔胶2-3、氨基酸螯合镁 1-2、聚乙烯吡咯烷酮1-2、硼酸0.1-0.2;
将上述聚乙二醇1000加热到38-40℃,加入氨基酸螯合镁 ,搅拌至常温,加入硼酸,搅拌混合均匀;
取上述醋丙乳液重量的40-50%与羟丙基瓜尔胶混合,在50-60℃下保温搅拌10-15分钟,加入植物甾醇,搅拌至常温;
将上述处理后的各原料与剩余各原料混合,200-300转/分搅拌混合20-30分钟,即得所述成膜助剂。
一种氟磷乳胶漆的制备方法,包括以下步骤:
(1)将上述氟磷灰石700-800℃下煅烧1-2小时,冷却后与磷酸钙、轻质碳酸钙混合,加入羟乙磺酸酯,球磨均匀;
(2)将上述处理后的各原料剩余与各原料混合,1800-2000转/分搅拌分散30-40分钟,即得所述乳胶漆。
本发明的优点是:
    本发明的乳胶漆不仅施工效果好、遮盖能力好、环保、味清新,无毒、成本较低,而且使用的时间长久,不会发生霉变,能达到高雅、清新、自然的装修效果。
具体实施方式
实施例1
一种氟磷乳胶漆,它是由下述重量份(公斤)的原料组成的:
苯丙乳液50、磷酸钙1、氟磷灰石3、N-乙酰基乙二胺2、羟乙磺酸酯1-2、肉豆蔻酸异丙酯0.3、羟乙基纤维素2、山梨醇2、双乙酸钠1、轻质碳酸钙40、成膜助剂8、去离子水40;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液30、聚乙二醇1000 3、植物甾醇1、羟丙基瓜尔胶3、氨基酸螯合镁 1、聚乙烯吡咯烷酮1、硼酸0.2;
将上述聚乙二醇1000加热到40℃,加入氨基酸螯合镁 ,搅拌至常温,加入硼酸,搅拌混合均匀;
取上述醋丙乳液重量的50%与羟丙基瓜尔胶混合,在60℃下保温搅拌15分钟,加入植物甾醇,搅拌至常温;
将上述处理后的各原料与剩余各原料混合,300转/分搅拌混合30分钟,即得所述成膜助剂。
一种氟磷乳胶漆的制备方法,包括以下步骤:
(1)将上述氟磷灰石800℃下煅烧2小时,冷却后与磷酸钙、轻质碳酸钙混合,加入羟乙磺酸酯,球磨均匀;
(2)将上述处理后的各原料剩余与各原料混合,2000转/分搅拌分散40分钟,即得所述乳胶漆。
性能测试:
漆膜外观平整、无硬块、手感好、光泽度好;
耐洗刷性试验:5000 次通过,漆膜无破损;
耐人工老化性试验:2000小时不起泡、不剥落、无裂纹;
耐水性:140h漆膜无破损;
耐碱性:120h漆膜无破损。

Claims (2)

1.一种氟磷乳胶漆,其特征在于它是由下述重量份的原料组成的:
苯丙乳液40-50、磷酸钙1-2、氟磷灰石3-4、N-乙酰基乙二胺1-2、羟乙磺酸酯1-2、肉豆蔻酸异丙酯0.3-1、羟乙基纤维素2-3、山梨醇1-2、双乙酸钠1-2、轻质碳酸钙30-40、成膜助剂5-8、去离子水32-40;
所述的成膜助剂是由下述重量份的原料组成的:
醋丙乳液21-30、聚乙二醇1000 3-5、植物甾醇1-2、羟丙基瓜尔胶2-3、氨基酸螯合镁 1-2、聚乙烯吡咯烷酮1-2、硼酸0.1-0.2;
将上述聚乙二醇1000加热到38-40℃,加入氨基酸螯合镁 ,搅拌至常温,加入硼酸,搅拌混合均匀;
取上述醋丙乳液重量的40-50%与羟丙基瓜尔胶混合,在50-60℃下保温搅拌10-15分钟,加入植物甾醇,搅拌至常温;
将上述处理后的各原料与剩余各原料混合,200-300转/分搅拌混合20-30分钟,即得所述成膜助剂。
2.一种如权利要求1所述的氟磷乳胶漆的制备方法,其特征在于包括以下步骤:
(1)将上述氟磷灰石700-800℃下煅烧1-2小时,冷却后与磷酸钙、轻质碳酸钙混合,加入羟乙磺酸酯,球磨均匀;
(2)将上述处理后的各原料剩余与各原料混合,1800-2000转/分搅拌分散30-40分钟,即得所述乳胶漆。
CN201410221749.9A 2014-05-23 2014-05-23 一种氟磷乳胶漆 Pending CN104073076A (zh)