CN104059332A - Plant fiber toy and artwork as well as preparation method thereof - Google Patents
Plant fiber toy and artwork as well as preparation method thereof Download PDFInfo
- Publication number
- CN104059332A CN104059332A CN201410262972.8A CN201410262972A CN104059332A CN 104059332 A CN104059332 A CN 104059332A CN 201410262972 A CN201410262972 A CN 201410262972A CN 104059332 A CN104059332 A CN 104059332A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- artwork
- toy
- melamine
- tankage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plant fiber toy and artwork as well as a preparation method of the toy and the artwork. The preparation raw materials consist of bamboo and wood fiber powder, amino moulding plastics, offals of melamine products, water and toners, wherein the bamboo and wood fiber powder is a cellulose fiber powder which is extracted from offals of bamboo and wood processing manufacturers; the offals of melamine products are leftover materials of melamine product manufacturers; the plant fiber toy and artwork can be prepared by vulcanizing the raw materials at a high temperature of 140-170 DEG C and a pressure of 50-200 tons for 2.5-10 minutes. The preparation method of the plant fiber toy and artwork has the advantages of being capable of simultaneously recycling and using wastes of bamboo and wood processing factories and melamine product factories, low in costs of raw materials and devices, simple in technological process and short in production cycle; the prepared products have the advantages of no toxin and odor, high hardness, relatively strong durability, a great possibility of dyeing, impact resistance, corrosion resistance, high-temperature resistance and low-temperature resistance and can be used in a variety of daily necessities.
Description
Technical field
The invention of this reality relates to toy and artwork processing and manufacturing field, specifically, relates to a kind of toy and artwork that utilizes vegetable fibre to manufacture.
Background technology
Along with improving constantly of people's living standard, demand and the requirement of people to various artworks, goods of furniture for display rather than for use, gift box etc. is also more and more higher, and this must cause raw-material a large amount of consumption such as bamboo wood.Therefore, utilize waste product to make novel material, improve the utilization ratio of waste and old resource, become future developing trend.
At present, existing manufacturing technology generally can not realize the recycling to refuse, although existing prior art can be recycled vegetable fibre and make product, but the product ubiquity hardness of producing is poor, easy coloring and easily break short-life problem into pieces not, product application scope is narrow, not yet proposes effective solution.
Summary of the invention
, not easy coloring and break short-life problem poor for the product hardness of utilizing waste and old resource to produce in existing correlation technique, the present invention proposes a kind of vegetable fibre toy and artwork and manufacture method thereof.
For realizing above-mentioned technical purpose, technical scheme of the present invention is achieved in that
A kind of vegetable fibre toy and artwork, it is made raw material and comprises bamboo and woods fiber powder, amino film plastics, melamine goods tankage, water and toner composition, wherein bamboo and woods fiber is a kind of cellulosic fibre powder extracting from bamboo wood processing producer offal, melamine goods tankage are the scrap stock of melamine goods producer, wherein, in formula, each raw material weight per-cent is:
Bamboo and woods fiber powder 1-70%;
Amino film plastics 1-80%;
Water 0.1-10%;
Melamine goods tankage 2-95%;
Appropriate toner (selecting according to actual needs to add).
Above-mentioned vegetable fibre toy and the making method of artwork comprise the following steps:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order;
(2) take raw material by proportioning raw materials, above-mentioned raw materials is put into homogenizer in proportion and stir 4-6 minute;
(3) by compound according to the actual quantitative weighing that carries out of product, quantitative compound is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and vulcanized, wherein, grinding tool is divided into upper and lower two moulds, the temperature of upper and lower two moulds is all controlled at 140-170 degree, pressure is 50-200 ton, and curing time is 2.5-10 minute;
(4) after sulfuration, take out, be vegetable fibre toy and artwork.
Beneficial effect of the present invention: the waste material of Zhu Mu source mill and melamine products factory is carried out to resource simultaneously and reclaim and utilize, raw material and equipment cost are low, and technological process is simple, with short production cycle; Prepared product has nonpoisonous and tasteless, and hardness is stronger, has stronger wearing quality, easy coloring, resistance toly collide with, the advantage such as corrosion-resistant, high temperature resistant, low temperature resistant, can be applicable in multiple daily living article.
Embodiment
Embodiment 1:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order.
(2) take raw material:
Bamboo and woods fiber powder 1kg
Amino mould material 1kg
Water 0.02kg
Melamine goods tankage 2kg
Putting into homogenizer stirs 4 minutes.
The compound that 120g is mixed is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and is vulcanized, and wherein, patrix temperature is 150 degree, and counterdie temperature is 140 degree, and pressure is 200 tons.Curing time is 6 minutes, vulcanizates rear taking-up product.
Embodiment 2:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order.
(2) take raw material:
Bamboo and woods fiber powder 70kg
Amino mould material 80kg
Water 10kg
Melamine goods tankage 95kg
Toner 50g
Putting into homogenizer stirs 6 minutes.
(3) compound 1500g being mixed is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and is vulcanized, and wherein, patrix temperature is 170 degree, and counterdie temperature is 160 degree, and pressure is 200 tons.Curing time is 10 minutes,
(4) vulcanizate rear taking-up product.
Embodiment 3:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order.
(2) take raw material:
Bamboo and woods fiber powder 8kg
Amino mould material 3kg
Water 1kg
Melamine goods tankage 15kg
Putting into homogenizer stirs 4 minutes.
(3) compound 180g being mixed is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and is vulcanized, and wherein, patrix temperature is 170 degree, and counterdie temperature is 160 degree, and pressure is 100 tons.Curing time is 4.5 minutes,
(4) vulcanizate rear taking-up product.
Embodiment 4:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order.
(2) take raw material:
Bamboo and woods fiber powder 6kg
Amino mould material 5.5kg
Water 1.5kg
Melamine goods tankage 10kg
Putting into homogenizer stirs 4 minutes.
(3) compound 159g being mixed is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and is vulcanized, and wherein, patrix temperature is 165 degree, and counterdie temperature is 155 degree, and pressure is 100 tons.Curing time is 4.5 minutes,
(4) vulcanizate rear taking-up product.
Embodiment 5:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order.
(2) take raw material:
Bamboo and woods fiber powder 8kg
Amino mould material 6kg
Water 1kg
Melamine goods tankage 15kg
Putting into homogenizer stirs 4 minutes.
(3) compound 210g being mixed is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and is vulcanized, and wherein, patrix temperature is 170 degree, and counterdie temperature is 160 degree, and pressure is 150 tons.Curing time is 4.5 minutes,
(4) vulcanizate rear taking-up product.
Claims (2)
1. a vegetable fibre toy and artwork, it is characterized in that, it is made raw material and comprises bamboo and woods fiber powder, amino film plastics, melamine goods tankage, water and toner, wherein bamboo and woods fiber is a kind of cellulosic fibre powder extracting from bamboo wood processing producer offal, melamine goods tankage are the scrap stock of melamine goods producer, and the weight percent of each raw material is as follows: bamboo and woods fiber powder 1-70%, amino film plastics 1-80%, water 0.1-10%, melamine goods tankage 2-95% and appropriate toner.
2. the making method of vegetable fibre toy claimed in claim 1 and artwork, is characterized in that, comprises the following steps:
(1) bamboo wood corner and melamine goods tankage are all crushed to 40-100 order;
(2) take raw material by proportioning raw materials, above-mentioned raw materials is put into homogenizer in proportion and stir 4-6 minute;
(3) by compound according to the actual quantitative weighing that carries out of product, quantitative compound is poured in the grinding tool chamber that is placed in hydraulic pressure vulcanizing machine inside and vulcanized, wherein, grinding tool is divided into upper and lower two moulds, the temperature of upper and lower two moulds is all controlled at 140-170 degree, pressure is 50-200 ton, and curing time is 2.5-10 minute;
(4) after sulfuration, take out, be vegetable fibre toy and artwork.