CN104046134B - 一种用桃胶制作微尘粉笔的方法 - Google Patents
一种用桃胶制作微尘粉笔的方法 Download PDFInfo
- Publication number
- CN104046134B CN104046134B CN201410297898.3A CN201410297898A CN104046134B CN 104046134 B CN104046134 B CN 104046134B CN 201410297898 A CN201410297898 A CN 201410297898A CN 104046134 B CN104046134 B CN 104046134B
- Authority
- CN
- China
- Prior art keywords
- grams
- peach gum
- chalk
- peach
- micronic dust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种用桃胶制作微尘粉笔的方法。将6~9克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡24~48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的碱溶液调整其pH值为9~11，在温度为90℃下水解搅拌反应10~12小时，待桃胶溶液充分水解后进行抽滤，制得桃胶水解液；将熟石膏粉和滑石粉按照质量比为1:0.10~0.35混合均匀制得混合粉料；取60~90克混合粉料，向其中加入10~20克桃胶水解液、5~7克甘油和60~80克50~60℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却5~10分钟后脱模，取出晾干，即制得微尘粉笔。本发明方法具有生产工艺简单，制作成本低，所制得的微尘粉笔书写和擦拭时粉尘少，表面光滑不沾手等优点。
Description
技术领域
本发明属于粉笔制作技术领域，特别涉及一种用桃胶制作微尘粉笔的方法。。
背景技术
粉笔是日常教学中必不可少的文化用品，其以字体清晰直观、易写易擦、价格低廉等优点而被广泛使用。石膏粉是制造粉笔用得最广泛的一种原料，它本身既是粉笔的白色基料，同时又是粉笔成型的粘结剂。但由于石膏粉笔内含有气孔、轻松、密度小（0.8-1.0 g/cm3），用于制备普通粉笔在使用过程中粉尘飞扬很大，严重地危害着广大师生的身体健康，又影响环境卫生。
为改善教学环境和改进粉笔的使用性能，目前国内外已广泛采用无尘粉笔，以解决粉尘污染的问题。同时，开发出多品种的无尘粉笔，也有许多相关专利的报道。例如文林报道了“可湿擦、湿写型无尘粉笔及其制造方法”(CN 1068069A)，主要采用石膏粉、聚乙二醇、各种颜料制成无尘粉笔; 谢子育用熟石膏粉、滑石粉、海藻酸钠、氯化铵、甘油和水混合，经浇注制得一种湿性无尘粉笔（CN 1077472A），该粉笔具有无粉尘飞扬、书写流畅、不粘手等优点；王子健报道了“一种无尘粉笔的制作方法”（CN 1868768A），以CaCO3、Ca(HCO3)2、石蜡和乙醇为原料，制得无尘粉笔；王力报道了“一种无尘粉笔及其制造工艺”（CN 1868768A），主要是以水溶性石蜡、甘油与钛白粉、滑石粉、水混合制得表面光滑不粘手、无尘健康型粉笔。张挥文等报道了“易擦型彩色无尘粉笔” （CN 1142520A），以石蜡、液体油、凡士林、钛白粉、颜料和碳酸钙经浇注成型制得一种易擦型彩色无尘粉笔；张立军在“新型无尘粉笔的研究”一文（承德民族师专学报，1997年2期）中，用石膏粉、OP乳化剂、聚乙烯醇缩甲醛为原料，开发出一种不起尘，不吸潮的无尘粉笔。此外，还有有关无尘粉笔制作方法的报道。
事实上，由于粉笔板书是靠粉尘的覆盖而呈字迹，无尘粉笔在擦黑板的过程中，或多或少还是有粉尘出现的，只是粉尘量与普通粉笔相比大大减少而已，因此，粉笔要做到绝对无尘是不可能的，充其量只能称为微尘粉笔。目前，国内外粉笔的降尘途径主要有两个方面：(1)增加粉末重量；(2)增加粉笔的耐磨度（减少摩擦量）。虽然这些方法在一定程度上，对降低粉笔粉尘飞扬问题有一定成效。但是到目前为止，粉笔粉尘及打滑现象等问题，还没有得到根本解决。
桃胶是一种蔷薇科李属树种树干的渗出物，商品化的桃胶主要来源于中国的亚热带和温带地区。桃胶属弱酸性大分子多糖，其分子结构为以半乳糖、葡萄糖醛酸和阿拉伯糖为主多支链的复杂分子结构，相对分子质量为568万，桃胶水解后可获得D−半乳糖、L−阿拉伯糖、D−葡萄糖醛酸、L−鼠李糖、D−甘露糖。桃胶在常温下难溶于水，随着温度的升高溶解度上升，但冷却至室温时，仍能稳定地保持溶解前的状态，无沉淀，不胶凝，胶液的浓度愈大粘度愈大。桃胶有较大的医用、药用和食用价值；可以用作涂料和印染工业保护胶体的助剂；可以用作书画薪裱的胶粘剂，附着力强。
用桃胶制作微尘粉笔的方法未见文献报道。
发明内容
本发明的目的是提供一种用桃胶制作微尘粉笔的方法。
本发明的思路：以熟石膏粉、滑石粉、水解桃胶溶液等为主要原料，经热水调匀后冷却凝固化，即制得微尘粉笔。
具体步骤为：
(1)将6~9克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡24~48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的碱溶液调整其pH值为9~11，在温度为90℃下水解搅拌反应10~12小时，待桃胶溶液充分水解后进行抽滤，即制得桃胶水解液。
(2)将熟石膏粉和滑石粉按照质量比为1:0.10~0.35混合均匀制得混合粉料。
(3)取60~90克步骤(2)制得的混合粉料，向其中加入10~20克步骤(1)制得的桃胶水解液、5~7克甘油和60~80克50~60℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却5~10分钟后脱模，取出晾干，即制得微尘粉笔。
所述碱溶液为氢氧化钠溶液、氢氧化钾溶液、氢氧化钙溶液和碳酸钠溶液中的一种或多种。
本发明方法具有以下优点：
(1)本发明方法使用的原料来源广泛，价格低，环境污染小。
(2)本发明方法制备工艺较简单，制作成本低，适合较大规模生产及推广。
(3)本发明方法制得的微尘粉笔具有字迹清晰、强度高、易写易擦、粉尘不飞扬以及表面光滑不沾手等优点。
具体实施方式
以下实施例制备微尘粉笔所用的主要原料：熟石膏粉(工业级)，滑石粉(工业级)，甘油(工业级)，原桃胶（桂林本地桃树上收集获得）。
实施例
1
：
(1)将6克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的氢氧化钠溶液调整其pH值为10，在温度为90℃下水解搅拌反应12小时，待桃胶溶液充分水解后进行抽滤，即制得桃胶水解液。
(2)将熟石膏粉和滑石粉按照质量比为1:0.25混合均匀制得混合粉料。
(3)取60克步骤(2)制得的混合粉料，向其中加入10克步骤(1)制得的桃胶水解液、5克甘油和60克60℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却8分钟后脱模，取出晾干，即制得微尘粉笔。
实施例
2
：
(1)将7克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的氢氧化钠溶液调整其pH值为11，在温度为90℃下水解搅拌反应12小时，待桃胶溶液充分水解后进行抽滤，即制得桃胶水解液。
(2)将熟石膏粉和滑石粉按照质量比为1:0.25混合均匀制得混合粉料。
(3)取70克步骤(2)制得的混合粉料，向其中加入12克步骤(1)制得的桃胶水解液、5克甘油和70克55℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却7分钟后脱模，取出晾干，即制得微尘粉笔。
实施例
3
：
(1)将9克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的氢氧化钠溶液调整其pH值为11，在温度为90℃下水解搅拌反应12小时，待桃胶溶液充分水解后进行抽滤，即制得桃胶水解液。
(2)将熟石膏粉和滑石粉按照质量比为1:0.20混合均匀制得混合粉料。
(3)取90克步骤(2)制得的混合粉料，向其中加入16克步骤(1)制得的桃胶水解液、6克甘油和80克50℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却6分钟后脱模，取出晾干，即制得微尘粉笔。
Claims (1)
1.一种用桃胶制作微尘粉笔的方法，其特征在于具体步骤为：
(1)将6~9克原桃胶进行清洗、除杂，然后在400毫升去离子水中浸泡24~48小时，使其充分溶胀后得到桃胶分散液；再用1摩尔/升的碱溶液调整其pH值为9~11，在温度为90℃下水解搅拌反应10~12小时，待桃胶溶液充分水解后进行抽滤，即制得桃胶水解液；
(2)将熟石膏粉和滑石粉按照质量比为1:0.10~0.35混合均匀制得混合粉料；
(3)取60~90克步骤(2)制得的混合粉料，向其中加入10~20克步骤(1)制得的桃胶水解液、5~7克甘油和60~80克50~60℃的热水，搅拌均匀后，倒入表面涂有脱模剂的粉笔模具中，冷却5~10分钟后脱模，取出晾干，即制得微尘粉笔；
所述碱溶液为氢氧化钠溶液、氢氧化钾溶液、碳酸钠溶液中的一种或多种。