CN104042003A - Colorful gemstone prepared by high-temperature melting method - Google Patents
Colorful gemstone prepared by high-temperature melting method Download PDFInfo
- Publication number
- CN104042003A CN104042003A CN201410284922.XA CN201410284922A CN104042003A CN 104042003 A CN104042003 A CN 104042003A CN 201410284922 A CN201410284922 A CN 201410284922A CN 104042003 A CN104042003 A CN 104042003A
- Authority
- CN
- China
- Prior art keywords
- gemstone
- jewel
- colorful
- melting
- high melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a colorful gemstone prepared by a high-temperature melting method. Under an ultraviolet lamp, when the temperature is 3000 DEG C, a catalyst is added according to a needed ratio of a colored gemstone or an artificial synthetic gemstone, automatic blending is carried out according to a color system represented by a melted gemstone; the melting of different color systems of the gemstone is carried out and the obtained gemstone after melting integrates all the colors. According to the colorful gemstone, a high-temperature melting technology is adopted and the colored gemstone or the artificial synthetic gemstone which can not be connected is fused by high-temperature melting according to different requirements; the fused gemstone is firm; meanwhile, the property of a single color of the previous gemstone is changed to realize colorful matching of the gemstone, so that jewelries are varied; the colorful gemstone has good economical efficiency and can be widely applied to all fields of the jewelries.
Description
Technical field
The present invention relates to high melt technology, particularly high melt legal system is for colorful jewel.
Background technology
Jewel has
broad sensewith
narrow senseminute,
broad sense's
jewelmake a general reference all
beautifuland
precious's
building stones, China
scholarwith " expensive U.S. stone " word, substitute,
narrow sense's
jewelspecially finger can be used for making valuable
jewellery's
building stones, it is generally acknowledged that it should have
magnificent,
rarewith
durablethree characteristics.On current jewellery market, use
diamond materialcan be divided into six kinds by the difference of manpower intervention degree: real
natural gemstone, through artificial modified
natural gemstone,
synthetic gem,
synthetic cut stone, simulation
jewelwith bonding
jewel(as synthetic in glass).The single color of jewel is jewelry industry insoluble problem always, at present can only by mosaic technology make it variation, increased like this with golden cost and change stiff.
Summary of the invention
The object of the present invention is to provide a kind of firm high melt legal system without fracture for colorful jewel.
For achieving the above object, the invention provides following technical scheme:
High melt legal system is for colorful jewel, under uviol lamp, when temperature reaches 3000 ℃, add catalyst be colored gemstone or the artificial required ratio of synthetic gem according to melting after the jewel colour system that will present independently allocate, carry out the melting of the different colour systems of jewel, the jewel after melting merges shades of colour.
As the further scheme of the present invention: the circuit of described high melt comprises industrial computer IPC and Programmable Logic Controller PLC, described Programmable Logic Controller PLC is connected with current transducer, voltage transmitter, frequency transmitter, phase place transmitter respectively, the other end is connected with industrial computer IPC by Ethernet, and described Programmable Logic Controller PLC controls high temperature melting furnace speedup, slows down, adds machine, subtracts machine etc. according to necessary requirement setting program.
Compared with prior art, the invention has the beneficial effects as follows: adopt high melt technology, the colored gemstone that itself can not be connected and artificial synthetic gem, according to difference require high melt together and merge after jewel can be more firm, by destructive test 100% nothing fracture, change the characteristic of original jewel single color simultaneously, realize the colorful collocation of jewel, jewellery are changed more various.The present invention has good economy, can be widely used in the every field of bullion.
Accompanying drawing explanation
Fig. 1 is high melt schematic block circuit diagram.
The specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
In the embodiment of the present invention, high melt legal system is for colorful jewel, under uviol lamp, when temperature reaches 3000 ℃, add catalyst be colored gemstone or the artificial required ratio of synthetic gem according to melting after the jewel colour system that will present independently allocate, carry out the melting of the different colour systems of jewel, the jewel after melting merges shades of colour.The present invention according to difference, require high melt together and merge after jewel can be more firm, by destructive test 100% nothing fracture, change the characteristic of original jewel single color simultaneously, also changed and only had the method that realizes the colorful collocation of jewel by embedding technique, can realize the colorful collocation of jewel, jewellery are changed more various, there is good economy, can be widely used in the every field of bullion.
In the embodiment of the present invention, high melt legal system is for colorful jewel, the circuit of described high melt comprises industrial computer IPC and Programmable Logic Controller PLC, described Programmable Logic Controller PLC is connected with current transducer, voltage transmitter, frequency transmitter, phase place transmitter respectively, the other end is connected with industrial computer IPC by Ethernet, and described Programmable Logic Controller PLC controls high temperature melting furnace speedup, slows down, adds machine, subtracts machine etc. according to necessary requirement setting program.
In order further to set forth the present invention, refer to following embodiment.
Embodiment 1
Purple gem, black onyx and topaz are obtained merging the colorful jewel of purple black yellow three kinds of colors by high melt according to mass ratio 1:3:5.
Embodiment 2
Purple gem, black onyx and topaz are obtained merging the colorful jewel of purple black yellow three kinds of colors by high melt according to mass ratio 1:3:3.
Embodiment 3
Purple gem, white stone and topaz are obtained merging the colorful jewel of purple Bai Huangsan kind color by high melt according to mass ratio 1:5:1.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the situation that not deviating from spirit of the present invention or essential characteristic, can realize the present invention with other concrete form.Therefore, no matter from which point, all should regard embodiment as exemplary, and be nonrestrictive, scope of the present invention is limited by claims rather than above-mentioned explanation, is therefore intended to include in the present invention dropping on the implication that is equal to important document of claim and all changes in scope.
In addition, be to be understood that, although this description is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of description is only for clarity sake, those skilled in the art should make description as a whole, and the technical scheme in each embodiment also can, through appropriately combined, form other embodiments that it will be appreciated by those skilled in the art that.
Claims (2)
1. high melt legal system is for colorful jewel, it is characterized in that, under uviol lamp, when temperature reaches 3000 ℃, add catalyst be colored gemstone or the artificial required ratio of synthetic gem according to melting after the jewel colour system that will present independently allocate, carry out the melting of the different colour systems of jewel, the jewel after melting merges shades of colour.
2. high melt legal system according to claim 1 is for colorful jewel, it is characterized in that, the circuit of described high melt comprises industrial computer IPC and Programmable Logic Controller PLC, described Programmable Logic Controller PLC is connected with current transducer, voltage transmitter, frequency transmitter, phase place transmitter respectively, the other end is connected with industrial computer IPC by Ethernet, and described Programmable Logic Controller PLC controls high temperature melting furnace speedup, slows down, adds machine, subtracts machine etc. according to necessary requirement setting program.