CN104031543A - Laminated metal protection coating and metal material - Google Patents
Laminated metal protection coating and metal material Download PDFInfo
- Publication number
- CN104031543A CN104031543A CN201410265671.0A CN201410265671A CN104031543A CN 104031543 A CN104031543 A CN 104031543A CN 201410265671 A CN201410265671 A CN 201410265671A CN 104031543 A CN104031543 A CN 104031543A
- Authority
- CN
- China
- Prior art keywords
- protection coating
- metal protection
- organic compound
- metal
- lamination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a laminated metal protection coating which comprises a transitional metal compound, an organic compound, an accelerant, a silane coupling agent and a Ti compound, wherein the organic compound has two or more functional groups selected from hydroxyl, carboxyl, phosphonate group, phosphate group and sulfo group; and the accelerant is selected from at least one of pyrrolidone, N-methylpyrrolidone and N-ethylpyrrolidone. According to the laminated metal protection coating and a metal material, the corrosion resistance and the heat resistance of the metal material can be effectively improved, the production cost of the laminated metal protection coating and the metal material is reduced, the economic benefit is increased, and the product quality is improved.
Description
Technical field
The present invention relates to a kind of metal protection field, be specifically related to a kind of lamination metal protection coating and metallic substance.
Background technology
Hot-dip metal plated material, comprises hot-dip galvanized metal material and hot-dip aluminizing zinc metallic substance, in order to prevent corrosion, and all can be at the surface of hot-dip metal plated material coating layer of metal protective coating to form protective film.Thereby the performance of metal protection coating is very important for the rust protection of hot-dip metal plated material.Solidity to corrosion and the thermotolerance of the protective film that metal protection coating forms are still poor.
Summary of the invention
For the problems referred to above, main purpose of the present invention is to provide a kind of solidity to corrosion and thermotolerance good lamination metal protection coating and metallic substance.
The present invention is achieved by the following technical solutions: a kind of lamination metal protection coating is provided, comprises transistion metal compound and organic compound, promotor, silane coupling agent and Ti compound; Wherein, described organic compound has 2 two or more functional groups being selected from above in hydroxyl, carboxyl, phosphonate group, phosphate and sulfonic group in same a part; Described promotor is at least one in pyrrolidone, N-Methyl pyrrolidone and N-ethyl pyrrolidone.
Preferably, the molecular weight of described organic compound is more than 100 and below 1000, and the shared weight percent of described organic compound is respectively: 30.5%-50.5%.
Preferably, in the quality of described organic compound and described promotor, the mass ratio of metal is 0.05～0.6.
Preferably, described silane coupling agent is selected from wherein a kind of of urethane resin, epoxy resin, acrylic resin, resol, polyester resin or polyvinyl resin.
Preferably, described metal protection coating also comprises a kind of in Zr, Ti, V, Mo or Nb.
The present invention also provides a kind of metallic substance, and metal protection coating described above is coated to lamination metallic surface.
A kind of lamination metal protection coating of the present invention and metallic substance, can effectively improve solidity to corrosion and the thermotolerance of metallic substance, reduces the production cost of lamination metal protection coating and metallic substance simultaneously, increases economic efficiency, and improves product quality.
Embodiment
For making the object, technical solutions and advantages of the present invention clearer, those skilled in the art can understand other advantages of the present invention and effect easily by the disclosed content of this specification sheets.The present invention can also be implemented or be applied by other different embodiment, and the every details in this specification sheets also can be based on different viewpoints and application, carries out various modifications or change not deviating under spirit of the present invention.
The invention provides a kind of lamination metal protection coating, comprise transistion metal compound and organic compound, promotor, silane coupling agent and Ti compound; Wherein, described organic compound has 2 two or more functional groups being selected from above in hydroxyl, carboxyl, phosphonate group, phosphate and sulfonic group in same a part; Described promotor is at least one in pyrrolidone, N-Methyl pyrrolidone and N-ethyl pyrrolidone.
In the present embodiment, the molecular weight of described organic compound is more than 100 and below 1000, and the shared weight percent of described organic compound is respectively: 30.5%-50.5%.
Wherein, in the quality of described organic compound and described promotor, the mass ratio of metal is 0.05～0.6.
In addition, described silane coupling agent is selected from wherein a kind of of urethane resin, epoxy resin, acrylic resin, resol, polyester resin or polyvinyl resin.
Described metal protection coating also comprises a kind of in Zr, Ti, V, Mo or Nb.
The present invention also provides a kind of metallic substance, and metal protection coating described above is coated to metal material surface.
A kind of lamination metal protection coating of the present invention and metallic substance, can effectively improve solidity to corrosion and the thermotolerance of metallic substance, reduces the production cost of lamination metal protection coating and metallic substance simultaneously, increases economic efficiency, and improves product quality.
Above-mentioned explanation illustrates and has described some preferred embodiments of the present invention, but as previously mentioned, be to be understood that the present invention is not limited to disclosed form herein, should not regard the eliminating to other embodiment as, and can be used for various other combinations, modification and environment, and can, in invention contemplated scope described herein, by technology or the knowledge of above-mentioned instruction or association area, change.And the change that those skilled in the art carry out and variation do not depart from the spirit and scope of the present invention, all should be in the protection domain of claims of the present invention.
Claims (6)
1. a lamination metal protection coating, is characterized in that, comprises transistion metal compound and organic compound, promotor, silane coupling agent and Ti compound; Wherein, described organic compound has 2 two or more functional groups being selected from above in hydroxyl, carboxyl, phosphonate group, phosphate and sulfonic group in same a part; Described promotor is at least one in pyrrolidone, N-Methyl pyrrolidone and N-ethyl pyrrolidone.
2. lamination metal protection coating according to claim 1, is characterized in that, the molecular weight of described organic compound is more than 100 and below 1000, and the shared weight percent of described organic compound is respectively: 30.5%-50.5%.
3. lamination metal protection coating according to claim 1, is characterized in that, in the quality of described organic compound and described promotor, the mass ratio of metal is 0.05～0.6.
4. lamination metal protection coating according to claim 1, is characterized in that, described silane coupling agent is selected from wherein a kind of of urethane resin, epoxy resin, acrylic resin, resol, polyester resin or polyvinyl resin.
5. according to the lamination metal protection coating described in any one in claim 1～4, it is characterized in that, described metal protection coating also comprises a kind of in Zr, Ti, V, Mo or Nb.
6. a metallic substance, is characterized in that, the metal protection coating described in any one in claim 1～5 is coated to lamination metallic surface.