CN104005298A - 一种高品质抗破度好的水松纸原纸及其制备方法 - Google Patents

一种高品质抗破度好的水松纸原纸及其制备方法 Download PDF

Info

Publication number
CN104005298A
CN104005298A CN201410237155.7A CN201410237155A CN104005298A CN 104005298 A CN104005298 A CN 104005298A CN 201410237155 A CN201410237155 A CN 201410237155A CN 104005298 A CN104005298 A CN 104005298A
Authority
CN
China
Prior art keywords
parts
water
slurry
tipping paper
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410237155.7A
Other languages
English (en)
Other versions
CN104005298B (zh
Inventor
黄幼兵
杜威
牛和建
郭杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou Cigarette Materials Factory
Original Assignee
Chuzhou Cigarette Materials Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chuzhou Cigarette Materials Factory filed Critical Chuzhou Cigarette Materials Factory
Priority to CN201410237155.7A priority Critical patent/CN104005298B/zh
Publication of CN104005298A publication Critical patent/CN104005298A/zh
Application granted granted Critical
Publication of CN104005298B publication Critical patent/CN104005298B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高品质抗破度好的水松纸原纸,其特征在于,由下列重量份的原料制备制成:松树浆45-48、绒毛浆53-56、梧桐树皮4-6、白树1-2、聚乙烯吡咯烷酮2-3、明矾1-2、碳酸钙2-3、沸石分子筛2-4、硅橡胶1-3、β-胡萝卜素0.8-1、锌钡白1-2、羧甲基纤维素2-3、助剂1-2、水适量;本发明将现制的植物梧桐树皮纤维加入造纸浆料中,产品纤维洁白,纤维分布均匀,纸张结实耐用,抗破度好,平滑细腻,油墨流平性能好,添加助剂,具有一定的吸附功效,而且香味怡人,能够改善烟气的辛辣味道。

Description

一种高品质抗破度好的水松纸原纸及其制备方法
技术领域
本发明涉及香烟技术领域,特别是一种高品质抗破度好的水松纸原纸及其制备方法。
背景技术
现有过滤烟嘴由于过滤原理单一、过滤过程没有按烟气的具体情况考虑,无法达到充分理想的过滤效果。如一次性过滤烟嘴太过于简单化,使之大部分有害物质不能清除掉。又如专利号为ZL200920112618.1的"多节除焦油烟嘴"专利,虽具有滤烟道长,除焦油效果好,但忽视了一个重要环节,相同结构的除焦器,在滤烟烟道长时,会出现烟气堵塞,抽上几支烟后会更加堵塞,导致最终不能使用。现在就希望发明一种水松纸包裹在过滤嘴外层,能够起到过滤吸附作用,既不会堵塞,又能清楚掉有害物质。水松纸不仅要具有良好的强度、匀度及一定的透气度,还要有一定的施胶度、良好的印刷性以及可切性;纸张纤维组织均匀,色泽一致;水松原纸的纤维分布均匀,厚度、紧度、透气度等指标波动小、可保证加工过程中涂料吸收均匀,减少色差;为了保证包接卷烟过滤嘴时不易断裂,伸长率必须要大。
发明内容
本发明的目的是提供一种高品质抗破度好的水松纸原纸及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种高品质抗破度好的水松纸原纸,由下列重量份的原料制备制成:松树浆45-48、绒毛浆53-56、梧桐树皮4-6、白树1-2、聚乙烯吡咯烷酮2-3、明矾1-2、碳酸钙2-3、沸石分子筛2-4、硅橡胶1-3、β-胡萝卜素0.8-1、锌钡白1-2、羧甲基纤维素2-3、助剂1-2、水适量;
所述助剂由以下重量份的原料制成:桔皮冻干粉4-5、菠萝冻干粉2-4、多孔淀粉2-3、麦饭石3-5、薄荷精油1-2、吐温-20 0.8-1、水适量;制备方法是将桔皮冻干粉、菠萝冻干粉、多孔淀粉、麦饭石混合粉碎成60-80目的粉末,然后加入薄荷精油、少量水进行研磨,研磨20-30分钟后加水稀释成固含量为10-15%的溶液,最后加入吐温-20搅拌均匀,得到悬浊液即得。
本发明所述一种高品质抗破度好的水松纸原纸,由以下具体步骤制成:
(1)将梧桐树皮加入2-3倍的水进行煎煮,过滤,滤液待用,取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时,加热至沸腾,小火蒸煮 2小时,然后水洗不溶物至无色,再用浓度为5%的盐酸和浓度为 4%的碳酸钠水溶液反复洗涤,直至不溶物的 pH 值为 7±0.2,然后干燥不溶物,即得植物纤维。
(2)将植物纤维、松树浆、绒毛浆放入水力碎浆机碎解,再经打浆机,打浆浓度控制在3.6-4.5%,打浆度在67~740SR,制得浆料;
(3)将碳酸钙、沸石分子筛、锌钡白混合均匀,研磨成40-60目的粉末,加入聚乙烯吡咯烷酮、羧甲基纤维素,搅拌25-30分钟制成混合料,然后在50-60℃烘干1-1.5小时待用;
(4)将混合料加入浆料中,加入除助剂以外的其余剩余成分,搅拌均匀,加入步骤(1)中滤液以及适量的水调浆至固含量为2.8-3.5%,加热至64-72℃,将调好的浆料经网部及压榨部脱水成形,湿纸页进入前干阶段,在表面均匀涂刷助剂;
(5)在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水,然后电热鼓风干燥5-6min,最后在光机上进行压光,取出后即得水松纸原纸。
本发明的有益效果是:本发明将现制的梧桐树皮纤维加入造纸浆料中,产品纤维洁白,纤维分布均匀,纸张结实耐用,抗破度好,平滑细腻,油墨流平性能好,添加助剂,具有一定的吸附功效,而且香味怡人,能够改善烟气的辛辣味道。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种高品质抗破度好的水松纸原纸,由下列重量份(公斤)的原料制备制成:松树浆45、绒毛浆53、梧桐树皮4、白树1、聚乙烯吡咯烷酮2、明矾1、碳酸钙2、沸石分子筛2、硅橡胶1、β-胡萝卜素0.8、锌钡白1、羧甲基纤维素2、助剂1、水适量;
所述助剂由以下重量份(公斤)的原料制成:桔皮冻干粉4、菠萝冻干粉2、多孔淀粉2、麦饭石3、薄荷精油1、吐温-20 0.8、水适量;制备方法是将桔皮冻干粉、菠萝冻干粉、多孔淀粉、麦饭石混合粉碎成60-80目的粉末,然后加入薄荷精油、少量水进行研磨,研磨20-30分钟后加水稀释成固含量为10-15%的溶液,最后加入吐温-20搅拌均匀,得到悬浊液即得。
本发明所述一种高品质抗破度好的水松纸原纸,由以下具体步骤制成:
(1)将梧桐树皮加入2-3倍的水进行煎煮,过滤,滤液待用,取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时,加热至沸腾,小火蒸煮 2小时,然后水洗不溶物至无色,再用浓度为5%的盐酸和浓度为 4%的碳酸钠水溶液反复洗涤,直至不溶物的 pH 值为 7±0.2,然后干燥不溶物,即得植物纤维。
(2)将植物纤维、松树浆、绒毛浆放入水力碎浆机碎解,再经打浆机,打浆浓度控制在3.6-4.5%,打浆度在67~740SR,制得浆料;
(3)将碳酸钙、沸石分子筛、锌钡白混合均匀,研磨成40-60目的粉末,加入聚乙烯吡咯烷酮、羧甲基纤维素,搅拌25-30分钟制成混合料,然后在50-60℃烘干1-1.5小时待用;
(4)将混合料加入浆料中,加入除助剂以外的其余剩余成分,搅拌均匀,加入步骤(1)中滤液以及适量的水调浆至固含量为2.8-3.5%,加热至64-72℃,将调好的浆料经网部及压榨部脱水成形,湿纸页进入前干阶段,在表面均匀涂刷助剂;
(5)在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水,然后电热鼓风干燥5-6min,最后在光机上进行压光,取出后即得水松纸原纸。
经检测,本发明制得的水松纸原纸的纵向抗张强度为1.7KN/m,透气度为66CU。

Claims (2)

1.一种高品质抗破度好的水松纸原纸,其特征在于,由下列重量份的原料制备制成:松树浆45-48、绒毛浆53-56、梧桐树皮4-6、白树1-2、聚乙烯吡咯烷酮2-3、明矾1-2、碳酸钙2-3、沸石分子筛2-4、硅橡胶1-3、β-胡萝卜素0.8-1、锌钡白1-2、羧甲基纤维素2-3、助剂1-2、水适量;
所述助剂由以下重量份的原料制成:桔皮冻干粉4-5、菠萝冻干粉2-4、多孔淀粉2-3、麦饭石3-5、薄荷精油1-2、吐温-20 0.8-1、水适量;制备方法是将桔皮冻干粉、菠萝冻干粉、多孔淀粉、麦饭石混合粉碎成60-80目的粉末,然后加入薄荷精油、少量水进行研磨,研磨20-30分钟后加水稀释成固含量为10-15%的溶液,最后加入吐温-20搅拌均匀,得到悬浊液即得。
2.根据权利要求1所述一种高品质抗破度好的水松纸原纸,其特征在于,由以下具体步骤制成:
(1)将梧桐树皮加入2-3倍的水进行煎煮,过滤,滤液待用,取滤渣加入16倍重量份的浓度为1%的氢氧化钠浸泡8小时,加热至沸腾,小火蒸煮 2小时,然后水洗不溶物至无色,再用浓度为5%的盐酸和浓度为 4%的碳酸钠水溶液反复洗涤,直至不溶物的 pH 值为 7±0.2,然后干燥不溶物,即得植物纤维;
(2)将植物纤维、松树浆、绒毛浆放入水力碎浆机碎解,再经打浆机,打浆浓度控制在3.6-4.5%,打浆度在67~740SR,制得浆料;
(3)将碳酸钙、沸石分子筛、锌钡白混合均匀,研磨成40-60目的粉末,加入聚乙烯吡咯烷酮、羧甲基纤维素,搅拌25-30分钟制成混合料,然后在50-60℃烘干1-1.5小时待用;
(4)将混合料加入浆料中,加入除助剂以外的其余剩余成分,搅拌均匀,加入步骤(1)中滤液以及适量的水调浆至固含量为2.8-3.5%,加热至64-72℃,将调好的浆料经网部及压榨部脱水成形,湿纸页进入前干阶段,在表面均匀涂刷助剂;
(5)在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水,然后电热鼓风干燥5-6min,最后在光机上进行压光,取出后即得水松纸原纸。
CN201410237155.7A 2014-05-30 2014-05-30 一种高品质抗破度好的水松纸原纸及其制备方法 Active CN104005298B (zh)