CN104004390B - A kind of tire pyrolysis carbon black post-treatment equipment and treatment process - Google Patents
A kind of tire pyrolysis carbon black post-treatment equipment and treatment process Download PDFInfo
- Publication number
- CN104004390B CN104004390B CN201410192151.1A CN201410192151A CN104004390B CN 104004390 B CN104004390 B CN 104004390B CN 201410192151 A CN201410192151 A CN 201410192151A CN 104004390 B CN104004390 B CN 104004390B
- Authority
- CN
- China
- Prior art keywords
- carbon black
- feed bin
- screw machine
- powder
- hopper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of finishing apparatus of tire pyrolysis gained carbon black, it comprises storage bin, storage bin is connected with feed bin with gas blower by air delivery pipe, feed bin is connected with transfer hopper with blower fan by air delivery pipe, transfer hopper is connected pulverizing mill respectively by screw machine I with screw machine II with below dedusting feed bin, pulverizing mill is connected with powder hopper, powder hopper is connected with powder packets vanning and tablets press respectively by screw machine III and screw machine IV, described tablets press is connected with dryer, described dryer connects granule packaging case, carbon black post-treatment equipment of the present invention adopts pipeline and wind model by the aftertreatment opposing seal of carbon black, the cost of equipment is carried lower than carrier bar, and the environment of sealing makes the environmental pollution of this equipment and process little, secondly, provide a kind of finishing apparatus and technique thereof of carbon black, carbon black post-treatment is come true by theory, improve the recycle value of carbon black, add the benefit of company.
Description
Technical field
The present invention relates to carbon black treatment facility and treatment process thereof, more specifically a kind of finishing apparatus of tire pyrolysis gained carbon black and treatment process thereof.
Background technology
Tire is the topmost rubber item of China.2009, China produced tire consumption of rubber and has accounted for about 70% of national rubber sources total amount consumed, and year produces damaged tire 2.33 hundred million, weight is roughly equal to 8,600,000 tons, amount to rubber sources about more than 300 ten thousand tons, if energy all recyclings, be equivalent to China's natural rubber output of 5 years.General tire can produce 40-45% oil fuel, 30-40% carbon black, about 10% combustible gas and about 10% steel wire, for the carbon black that cracking produces, its granularity is generally 70-80 order, its utility value is low, the processing mode that current producer is general is directly contracted out by carbon black dress to sell, this way, first seriously polluted, secondly the output value is low.
Summary of the invention
Summary of the invention of the present invention is for deficiency of the prior art, provides a kind of finishing apparatus and treatment process of tire pyrolysis gained carbon black.
The present invention is achieved by the following technical solutions:
A kind of tire pyrolysis carbon black post-treatment equipment, comprise storage bin, storage bin is connected with feed bin with gas blower by air delivery pipe, described feed bin is connected with transfer hopper with blower fan by air delivery pipe, dedusting feed bin and induced draft fan II is provided with after described transfer hopper, described transfer hopper is connected pulverizing mill respectively by screw machine I with screw machine II with below dedusting feed bin, pulverizing mill is connected with powder hopper, powder hopper is connected with powder packets vanning and tablets press respectively by screw machine III and screw machine IV, described tablets press is connected with dryer, described dryer connects granule packaging case.
The effect one of air delivery pipe adopts the mode of closing to carry carbon black, and protection of the environment, another effect is that carbon black is transferred to carbon black post-treatment workshop by cracking workshop, and the cost that wind send is significantly less than other modes.
Fly-ash separator and induced draft fan I is provided with after above-mentioned feed bin.
Above-mentioned powder hopper is also connected with dust cleaning case and induced draft fan III.
Above-mentioned dryer is connected with water cooler, is connected with dusting machine and induced draft fan IV after described water cooler.
The effect of fly-ash separator, dust cleaning case, dusting machine is all the dedustings to pipeline, and the effect of induced draft fan I, III and IV is all play wind to send effect.
Above-mentioned baker is also connected with roasting kiln.
As another goal of the invention of the present invention, a kind of tire pyrolysis carbon black post-treatment technique utilizing above-mentioned finishing apparatus to propose, comprises the steps:
(1) cracker gained carbon black is transported in storage bin after being transported to tramp iron separator by carrier bar;
(2) carbon black in storage bin is transported in the feed bin for concentrating and store by gas blower and air delivery pipe;
(3) by induced draft fan II, the carbon black in feed bin is transported in transfer hopper, carbon black in transfer hopper is transported in pulverizing mill through screw machine I and carries out abrasive dust, the carbon black that dedusting feed bin is omitted owing to collecting transfer hopper, and through screw machine II, carbon black is transported to abrasive dust in pulverizing mill;
(4) grinding hopper is entered after pulverizing mill abrasive dust; two kinds of processing modes are divided into after powder hopper; powder is directly cased by powder packets by screw machine III by the first; another kind is connected in tablets press by screw machine IV; and in tablets press, add water and activator carries out granulation; by dryer, carbon black pellet is dried after granulation, packaging after drying.
Carbon black powder granularity after above-mentioned pulverizing mill abrasive dust is 350 orders.
Above-mentioned activator is stearic acid.
The bake out temperature of above-mentioned dryer is 110 DEG C, the cooling temperature of water cooler 35 DEG C.
The invention has the beneficial effects as follows: carbon black post-treatment equipment of the present invention adopts pipeline and wind model by the aftertreatment opposing seal of carbon black, lower than carrier bar conveying and other mode of movements in the cost of equipment, and the environment of sealing makes the environmental pollution of this equipment and process little, it is only be in communication with the outside at carbon black entrance and two product outlet places, next provides a kind of finishing apparatus and technique thereof of carbon black, carbon black post-treatment is come true by theory, improve the recycle value of carbon black, add the benefit of company.
Accompanying drawing explanation
Fig. 1 is tire pyrolysis carbon black post-treatment equipment schematic diagram of the present invention.
Specific embodiment
Below in conjunction with the drawings and specific embodiments, the present invention will be further described, so that those skilled in the art better can understand the present invention, but therefore do not limit the present invention.
Embodiment 1
A kind of tire pyrolysis carbon black post-treatment equipment, comprise storage bin, storage bin is connected with feed bin with gas blower by air delivery pipe, described feed bin is connected with transfer hopper with blower fan by air delivery pipe, dedusting feed bin and induced draft fan II (12.5kw) is provided with after described transfer hopper, described transfer hopper is connected pulverizing mill (75kw) respectively by screw machine I (7.5kw) with screw machine II (1.5kw) with below dedusting feed bin, pulverizing mill is connected with powder hopper, powder hopper is connected with powder packets vanning and tablets press (22.5kw) respectively by screw machine III (4.5kw) and screw machine IV (4.5kw), described tablets press is connected with dryer (12.5kw), described dryer connects granule packaging case.
Fly-ash separator and induced draft fan I (2.5kw) is provided with after above-mentioned feed bin.
Above-mentioned powder hopper is also connected with dust cleaning case and induced draft fan III (12kw).
Above-mentioned dryer is connected with water cooler, is connected with dusting machine and induced draft fan IV (12.5kw) after described water cooler.
Above-mentioned baker is also connected with roasting kiln (1.5kw).
A kind of tire pyrolysis carbon black post-treatment technique according to claim 1, comprises the steps:
(1) cracker gained carbon black is transported in storage bin after being transported to tramp iron separator by carrier bar;
(2) carbon black in storage bin is transported in the feed bin for concentrating and store by the gas blower of power 21KW and diameter 159cm air delivery pipe;
(3) by induced draft fan II (12.5kw), the carbon black in feed bin is transported in transfer hopper, carbon black in transfer hopper is transported in pulverizing mill through screw machine I (7.5kw) and carries out abrasive dust (24kw), the carbon black that dedusting feed bin is omitted owing to collecting transfer hopper, and through screw machine II (1.5kw), carbon black is transported to abrasive dust in pulverizing mill;
(4) grinding hopper is entered after pulverizing mill abrasive dust; two kinds of processing modes are divided into after powder hopper; powder is directly cased by powder packets by screw machine III (4.5kw) by the first; another kind is connected in tablets press by screw machine IV (4.5kw); and interpolation water and activator carry out granulation in tablets press (22.5kw); by dryer (12.5kw), carbon black pellet is dried after granulation, packaging after drying.
Carbon black powder granularity after above-mentioned pulverizing mill abrasive dust is 350 orders.
Above-mentioned activator is stearic acid.
Before the oven dry of above-mentioned dryer, temperature is 260 DEG C, and after drying, temperature is 110 DEG C, and before the cooling of water cooler, temperature is 90 DEG C, temperature 35 DEG C after cooling.
Pulverizing mill in above-mentioned technique: model: YB2-280s-4, producer is the three-dimensional dynamo-electric factory in Zhejiang;
Dryer: model: R2S703485001, power: 7.5kw, producer: Leah road, Zibo;
Tablets press: model: 280m-6, producer: Liaocheng City Rong Xiang motor;
Gas blower: model: Y123B-4, producer: Zichuan Hua Bo.
Above-mentioned induced draft fan I, II, III, IV: producer: Zichuan Hua Bo.
Claims (9)
1. a tire pyrolysis carbon black post-treatment equipment, it is characterized in that: this equipment comprises storage bin, storage bin is connected with feed bin by air delivery pipe and gas blower, described feed bin is connected with transfer hopper by air delivery pipe and blower fan, dedusting feed bin is provided with after described transfer hopper, described dedusting feed bin is connected with induced draft fan II, described transfer hopper is connected pulverizing mill respectively by screw machine I with screw machine II with below dedusting feed bin, pulverizing mill is connected with powder hopper, powder hopper is connected with powder packets vanning and tablets press respectively by screw machine III and screw machine IV, described tablets press is connected with dryer, described dryer connects granule packaging case.
2. a kind of tire pyrolysis carbon black post-treatment equipment according to claim 1, it is characterized in that: be provided with fly-ash separator after described feed bin, described fly-ash separator is connected with induced draft fan I.
3. a kind of tire pyrolysis carbon black post-treatment equipment according to claim 1, is characterized in that: described powder hopper is also connected with dust cleaning case, and described dust cleaning case is connected with induced draft fan III.
4. a kind of tire pyrolysis carbon black post-treatment equipment according to claim 1, is characterized in that: described dryer is connected with water cooler, is connected with dusting machine after described water cooler, be connected with induced draft fan IV after described dusting machine.
5. a kind of tire pyrolysis carbon black post-treatment equipment according to claim 4, is characterized in that: described dryer is also connected with roasting kiln.
6., according to a kind of tire pyrolysis carbon black post-treatment technique described in claim 1, comprise the steps: that (1) cracker gained carbon black is transported in storage bin after being transported to tramp iron separator by carrier bar; (2) carbon black in storage bin is transported in the feed bin for concentrating and store by gas blower and air delivery pipe; (3) by induced draft fan II, the carbon black in feed bin is transported in transfer hopper, carbon black in transfer hopper is transported in pulverizing mill through screw machine I and carries out abrasive dust, the carbon black that dedusting feed bin is omitted owing to collecting transfer hopper, and through screw machine II, carbon black is transported to abrasive dust in pulverizing mill; (4) powder materials case is entered after pulverizing mill abrasive dust; two kinds of processing modes are divided into after powder hopper; powder is directly cased by powder packets by screw machine III by the first; another kind is connected in tablets press by screw machine IV; and in tablets press, add water and activator carries out granulation; by dryer, carbon black pellet is dried after granulation, packaging after drying.
7. a kind of tire pyrolysis carbon black post-treatment technique according to claim 6, is characterized in that: the carbon black powder granularity after described pulverizing mill abrasive dust is 350 orders.
8. a kind of tire pyrolysis carbon black post-treatment technique according to claim 6, is characterized in that: described activator is stearic acid.
9. a kind of tire pyrolysis carbon black post-treatment technique according to claim 6, is characterized in that: the bake out temperature of described dryer is 110 DEG C, the cooling temperature of water cooler 35 DEG C.