CN104003658B - Multiple colored road surface concrete premixing mortar - Google Patents
Multiple colored road surface concrete premixing mortar Download PDFInfo
- Publication number
- CN104003658B CN104003658B CN201410126944.3A CN201410126944A CN104003658B CN 104003658 B CN104003658 B CN 104003658B CN 201410126944 A CN201410126944 A CN 201410126944A CN 104003658 B CN104003658 B CN 104003658B
- Authority
- CN
- China
- Prior art keywords
- road surface
- cement
- mortar
- road
- premixing mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to multiple colored road surface concrete premixing mortar, the pigment of different colours mixing the mortar forming at least two color, raw material and percentage by weight thereof with other raw materials respectively is: cement 20%-25%, sand 70%-75%, powder refining ash 1%-3%, pigment 2%-5%, rubber powder 1%-3%, cellulose ether 0.01%-0.02%, water-repelling agent 0.2%-0.3%, water reducer 0.5%-0.8%, anti-shrinking medium 0.5%-0.8%, fluidizing reagent 0.5%-0.8%, fiber 0.3%-0.5%。Differentiation left and right, road surface road laid by different colours mortar, driver's visual fatigue can be slowed down, road surface toughness and frictional property are better, can shorten braking distance, reduce road accident rate, promote road aesthetics, existing Colophonium or cement pavement are laid mortar and adds reinforcing bar band, extend former pavement life, reduce cost of repairing the roads, avoid bituminous paving abnormal flavour, alleviate air pollution。
Description
Technical field
The present invention relates to a kind of mortar, particularly multiple colored road surface concrete premixing mortar, belongs to building material field。
Background technology
The road surface of the road of current urban road and residential quarters is mostly cement pavement, bituminous paving, and its color is single, it is easy to cause Driver Vision tired。The cracking resistance on road surface is poor, there will be many places slight crack after using a period of time。The friction non-skid property on road surface is also poor, and skidding distance is longer。And bituminous paving can emit bad smell when summer, road pavement pedestrian's health causes certain harm。
Summary of the invention
In order to solve the problems referred to above, the present invention is achieved by the following technical solutions:
Multiple colored road surface concrete premixing mortar, is made up of the pavement concrete premixing mortar of the two kinds of colors laying road surface, left and right respectively respectively following raw material by weight percentage:
Cement 22%, sand 70%, powder refining ash 1%, iron oxide pigment 3%, rubber powder 2%, cellulose ether 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%；
Cement 22%, sand 70%, powder refining ash 1%, chromium oxide pigments 3%, rubber powder 2%, cellulose ether 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%。
Further, cement adopts P0.425 cement。
Further, cellulose ether is hydroxypropylcelluloether ether。
The multiple colored road surface concrete premixing mortar of the present invention, the premixing mortar of useful different colours is laid road surface and is distinguished ridden in left or right direction road, be conducive to slowing down the visual fatigue of driver, it is easy to enable a driver to distinguish the vehicle of different directions, the road surface laid has better toughness and frictional property, shortens skidding distance during driving, can effectively reduce road traffic accident rate, road and sidewalk in residential quarters use, and can beautify the living environment。Promote the aesthetics of urban road, existing bituminous paving and cement surface are laid about 3 centimeters reinforcing bar bands added in construction, easy construction, extend the life-span on original road surface, it is substantially reduced the cost again repaired the roads, and can significantly avoid the situation that bituminous paving emits bad smell, purifying city air in summer, alleviate municipal pollution。Utilize the road surface that colored road surface concrete premixing mortar provided by the present invention is laid to have better anticracking, non-skid property, have extremely strong elasto-plasticity, high-strength cohesive, energy prolonging service life of pavement。
Detailed description of the invention
Following example are used for illustrating the present invention, but are not limited to the scope of the present invention。
Multiple colored road surface concrete premixing mortar, is mixed in proportion with other raw materials respectively by the pigment of different colours, the pavement concrete premixing mortar of composition at least two color,
Multiple colored road surface concrete premixing mortar, it is made up of following raw material by weight percentage: cement 20%-25%, sand 70%-75%, powder refining ash 1%-3%, pigment 2%-5%, rubber powder 1%-3%, cellulose ether 0.01%-0.02%, water-repelling agent 0.2%-0.3%, water reducer 0.5%-0.8%, anti-shrinking medium 0.5%-0.8%, fluidizing reagent 0.5%-0.8%, fiber 0.3%-0.5%。
Pigment is two or more in the pigment such as iron oxide pigment, manganese oxide pigment, chromium oxide pigments, ultramarine pigment, sinopis, mummy pigment。General, iron oxide pigment has red, yellow, brown, black, and manganese oxide pigment has brown, black, and chromium oxide pigments is green, and ultramarine pigment is blue, and sinopis is reddish brown。
In the present embodiment, mortar is made up of following raw material by weight percentage:
Its raw material of the mortar of a kind of color and ratio by weight percentage be: cement adopts P0.425 cement, cement 22%, sand 70%, powder refining ash 1%, pigment is chosen as the iron oxide tan in iron oxide pigment, iron oxide pigment 3%, rubber powder 2%, cellulose ether adopts hydroxypropylcelluloether ether, and its content is 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%。
Each component of aforementioned proportion is added in agitator and stirs, bag encapsulation can be entered and form premixing mortar。
Another kind of its raw material of mortar of color and ratio by weight percentage be: cement adopts P0.425 cement, cement 22%, sand 70%, powder refining ash 1%, pigment is chromium oxide pigments, chromium oxide pigments 3%, rubber powder 2%, cellulose ether adopts hydroxypropylcelluloether ether, and its content is 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%。
Each component of aforementioned proportion is added in agitator and stirs, bag encapsulation can be entered and form premixing mortar。
During use, each component of packed aforementioned proportion adding stirring 10 minutes in agitator, add water after uniformly stirring。The pavement concrete premixing mortar of two kinds of colors is laid respectively the road surface of left and right road, the road surface, left and right of color contrast difference can be formed。
In other embodiments, it is also possible to adopt other ratios to carry out proportioning in the scope of above-mentioned setting and form premixing mortar。
In other embodiments, it is also possible to select the pigment of other colors and other raw materials to carry out proportioning in the proportion of above-mentioned setting, form the pavement concrete premixing mortar of other colors, and then be laid on road surface, left and right and make road surface, left and right color form difference。
In other embodiments, pigment and other raw materials that can also take three kinds of colors carry out proportioning in the proportion of above-mentioned setting and form the pavement concrete premixing mortar of three kinds of colors, with the pavement concrete premixing mortar of two of which color for the main laying carrying out road surface, left and right, road surface, left and right color is made to form difference。The pavement concrete premixing mortar of the third color is laid on crossing or crossing or the road surface, left and right of other positions needing prompting road pedestrian and driver to enhance your vigilance as the pavement concrete premixing mortar of warning color, make to be formed the road surface of the discrepant color of mass-tone with road surface, left and right on road surface, left and right, it is thus possible to intuitively pedestrian and driver are played reminding effect from road surface。
In other embodiments, the pavement concrete premixing mortar as warning color can be two kinds of colors or more。
The multiple colored road surface concrete premixing mortar of the present invention, can lay road surface with the premixing mortar of different colours and distinguish ridden in left or right direction road, be conducive to slowing down the visual fatigue of driver, it is simple to driver can distinguish the vehicle of different directions。The road surface laid has better toughness and frictional property, shortens skidding distance during driving, can effectively reduce road traffic accident rate, and road and sidewalk in residential quarters use, and can beautify the living environment, promote the aesthetics of urban road。And can significantly avoid bituminous paving to emit bad smell in summer situation, and purifying city air, alleviate municipal pollution, protection pedestrian is healthy。Utilize the road surface that colored road surface concrete premixing mortar provided by the present invention is laid to have better anticracking, non-skid property, have extremely strong elasto-plasticity, high-strength cohesive, energy prolonging service life of pavement。
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvement and modification, these improve and modification also should be regarded as protection scope of the present invention。
Claims (3)
1. many kinds of colored road surface concrete premixing mortars, it is characterised in that be made up of the pavement concrete premixing mortar of the two kinds of colors laying road surface, left and right respectively respectively following raw material by weight percentage:
Cement 22%, sand 70%, powder refining ash 1%, iron oxide pigment 3%, rubber powder 2%, cellulose ether 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%；
Cement 22%, sand 70%, powder refining ash 1%, chromium oxide pigments 3%, rubber powder 2%, cellulose ether 0.01%, water-repelling agent 0.2%, water reducer 0.5%, anti-shrinking medium 0.5%, fluidizing reagent 0.5%, fiber 0.29%。
2. multiple colored road surface concrete premixing mortar according to claim 1, it is characterised in that cement adopts P0.425 cement。
3. multiple colored road surface concrete premixing mortar according to claim 1 and 2, it is characterised in that cellulose ether is hydroxypropylcelluloether ether。