CN103992596A - Novel low temperature and oil resistant flexible pipe and production method thereof - Google Patents
Novel low temperature and oil resistant flexible pipe and production method thereof Download PDFInfo
- Publication number
- CN103992596A CN103992596A CN201410182535.5A CN201410182535A CN103992596A CN 103992596 A CN103992596 A CN 103992596A CN 201410182535 A CN201410182535 A CN 201410182535A CN 103992596 A CN103992596 A CN 103992596A
- Authority
- CN
- China
- Prior art keywords
- parts
- low temperature
- flexible pipe
- oil resistant
- resistant flexible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel low temperature and oil resistant flexible pipe. The flexible pipe comprises, by weight, 80-120 parts of PVC resin, 1.5-2.5 parts of barium stearate, 8.0-12.0 parts of dioctyl adipate, 35-45 parts of tritolyl phosphate and 0.5-1.5 parts of carbon black. Compared with flexible pipes in the invention, the novel low temperature and oil resistant flexible pipe produced in the invention has the advantages of low price, few used raw materials, simple production process, and stable oil resistance at a low temperature.
Description
Technical field
The present invention relates to material science, refer more particularly to a kind of novel anti-low temperature oil resistant flexible pipe and production method thereof.
Background technology
Oil resisting rubber hose, its feature is to have good acid resistance gasoline, the performance of ethanol-tolerant gasoline, and also also good to the stopping property of Water Oil Or Gas.The general oil-proofness of oil resisting rubber hose is in the market better, but cold resistance is not all right, under the environment of low temperature, cause the ability that dissolving, swelling, cracking, distortion or physicals reduce, and oil resistance also can be affected in various degree the in the situation that of low temperature, Given this situation, now study a kind of anti-low temperature oil resistant flexible pipe, can resist severe cold, and in severe cold, there is equally the novel anti-low temperature oil resistant flexible pipe of good oil resistance.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of anti-low temperature, oil resistant, the stable flexible pipe of physical and chemical performance, i.e. novel anti-low temperature oil resistant flexible pipe.
For solving the problems of the technologies described above, the present invention by the following technical solutions:
A novel anti-low temperature oil resistant flexible pipe, is characterized in that, comprise following weight part raw material: polyvinyl chloride resin 80-120 part, barium stearate 1.5-2.5 part, Octyl adipate 8.0-12.0 part, tritolyl phosphate 35-45 part, carbon black 0.5-1.5 part.
Preferably, the raw material of described each weight part is: polyvinyl chloride resin 90-110 part, barium stearate 1.75-2.25 part, Octyl adipate 9.0-11.0 part, tritolyl phosphate 37.5-42.5 part, carbon black 0.75-1.25 part.
Preferably, the raw material of described each weight part is: 100 parts of polyvinyl chloride resins, 2.0 parts of barium stearates, 10.0 parts of Octyl adipates, 40.0 parts of tritolyl phosphates, 1.0 parts of carbon blacks.
A production method for novel anti-low temperature oil resistant flexible pipe, is characterized in that, comprises the following steps:
(1) take by weight each raw material: polyvinyl chloride resin 80-120 part, barium stearate 1.5-2.5 part, Octyl adipate 8.0-12.0 part, tritolyl phosphate 35-45 part, carbon black 0.5-1.5 part;
(2) after will step (1) raw material mediating, in temperature, be 150 ℃-170 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
Embodiment
Below in conjunction with embodiment, technical scheme of the present invention is further described in detail.
Embodiment mono-:
(1) take by weight each raw material: 80 parts of polyvinyl chloride resins, 1.5 parts of barium stearates, 8.0 parts of Octyl adipates, 35 parts of tritolyl phosphates, 0.5 part of carbon black;
(2) after will step (1) raw material mediating, in temperature, be 150 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
Embodiment bis-:
(1) take by weight each raw material: 120 parts of polyvinyl chloride resins, 2.5 parts of barium stearates, 12.0 parts of Octyl adipates, 45 parts of tritolyl phosphates, 1.5 parts of carbon blacks;
(2) after will step (1) raw material mediating, in temperature, be 170 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
Embodiment tri-:
(1) take by weight each raw material: 100 parts of polyvinyl chloride resins, 2.0 parts of barium stearates, 10.0 parts of Octyl adipates, 40.0 parts of tritolyl phosphates, 1.0 parts of carbon blacks;
(2) after will step (1) raw material mediating, in temperature, be 160 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
Embodiment tetra-:
(1) take by weight each raw material: 90 parts of polyvinyl chloride resins, 1.75 parts of barium stearates, 9.0 parts of Octyl adipates, 37.5 parts of tritolyl phosphates, 0.75 part of carbon black;
(2) after will step (1) raw material mediating, in temperature, be 150 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
Embodiment five:
(1) take by weight each raw material: 110 parts of polyvinyl chloride resins, 2.25 parts of barium stearates, 11.0 parts of Octyl adipates, 42.5 parts of tritolyl phosphates, 1.25 parts of carbon blacks;
(2) after will step (1) raw material mediating, in temperature, be 170 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.
The present invention compared with prior art, has the following advantages: product price that (1) the present invention produces is cheap, use raw material less, and production technique is simple; (2) the present invention's oil resistance in the situation that of lower temperature is still stable.
It should be noted last that, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement technical scheme of the present invention, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (4)
1. a novel anti-low temperature oil resistant flexible pipe, is characterized in that, comprise following weight part raw material: polyvinyl chloride resin 80-120 part, barium stearate 1.5-2.5 part, Octyl adipate 8.0-12.0 part, tritolyl phosphate 35-45 part, carbon black 0.5-1.5 part.
2. novel anti-low temperature oil resistant flexible pipe according to claim 1, is characterized in that, the raw material of described each weight part is: polyvinyl chloride resin 90-110 part, barium stearate 1.75-2.25 part, Octyl adipate 9.0-11.0 part, tritolyl phosphate 37.5-42.5 part, carbon black 0.75-1.25 part.
3. novel anti-low temperature oil resistant flexible pipe according to claim 1, is characterized in that, the raw material of described each weight part is: 100 parts of polyvinyl chloride resins, 2.0 parts of barium stearates, 10.0 parts of Octyl adipates, 40.0 parts of tritolyl phosphates, 1.0 parts of carbon blacks.
4. a production method for novel anti-low temperature oil resistant flexible pipe according to claim 1, is characterized in that, comprises the following steps:
(1) take by weight each raw material: polyvinyl chloride resin 80-120 part, barium stearate 1.5-2.5 part, Octyl adipate 8.0-12.0 part, tritolyl phosphate 35-45 part, carbon black 0.5-1.5 part;
(2) after will step (1) raw material mediating, in temperature, be 150 ℃-170 ℃, compression ratio is 2-4, under the condition that length-to-diameter ratio is 20-25 through twin-roll mixing, pulverize extrusion moulding, cooling and shaping;
(3) the more cooling product cutting after step (2) processing can be obtained to novel anti-low temperature oil resistant flexible pipe.