CN103992081A - 一种采用建筑垃圾制作加气混凝土砌块的配方及加工方法 - Google Patents
一种采用建筑垃圾制作加气混凝土砌块的配方及加工方法 Download PDFInfo
- Publication number
- CN103992081A CN103992081A CN201410122099.2A CN201410122099A CN103992081A CN 103992081 A CN103992081 A CN 103992081A CN 201410122099 A CN201410122099 A CN 201410122099A CN 103992081 A CN103992081 A CN 103992081A
- Authority
- CN
- China
- Prior art keywords
- building waste
- building block
- waste
- building
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种混凝土的制备方法,具体是一种采用建筑垃圾制作加气混凝土砌块的配方及加工方法。其特征在于配料的配比为:其特征在于配料的配比为:建筑垃圾:35-40%,煤灰粉15-25%,生石灰6-11%,水泥10-15%,硅沙3-7%,铝粉(添加剂)0.5-1%,脱流膏3-5%,红泥5-10%。本发明可对建筑垃圾进行充分利用,变废为宝,同时所得的混凝土砌块抗压强度高,耐久性好,同时,本发明的加工工艺简单,使用的配料价格低廉且原料丰富,从而可以更广泛的进行推广使用。
Description
技术领域
本发明涉及一种混凝土的制备方法,具体是一种采用建筑垃圾制作加气混凝土砌块的配方及加工方法。
背景技术
混凝土是当代最主要的土木工程材料之一,通常讲的混凝土是指用水泥作胶凝材料,砂、石作集料;与水(可含外加剂和掺合料)按一定比例配合,经搅拌而得的水泥混凝土,也称普通混凝土,它广泛应用于土木工程,建筑垃圾是指建设、施工单位或个人对各类建筑物、构筑物、管网等进行建设、铺设或拆除、修缮过程中所产生的渣土、弃土、弃料、余泥及其他废弃物。随着工业化、城镇化进程的加快,建筑业也同时快速发展,相伴而产生的建筑垃圾日益增多,中国建筑垃圾的数量已占到城市垃圾总量的1/3以上。
发明内容
本发明的目的在于,解决上述存在的问题,提供一种采用建筑垃圾制作加气混凝土砌块的配方及加工方法。
本发明是通过以下技术方案来实现的:
一种采用建筑垃圾制作加气混凝土砌块的配方,其特征在于配料的配比为:建筑垃圾:35-40%,煤灰粉15-25%,生石灰6-11%,水泥10-15%,硅沙3-7%,铝粉(添加剂)0.5-1%,脱流膏3-5%,红泥5-10%。
其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入30-40℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到210-250℃后,静置6-8小时,等待压力泄完后出釜,形成成品。
有益效果:由于采用了上述的技术方案, 本发明可对建筑垃圾进行充分利用,变废为宝,同时所得的混凝土砌块抗压强度高,耐久性好,同时,本发明的加工工艺简单,使用的配料价格低廉且原料丰富,从而可以更广泛的进行推广使用。
具体实施方式
一种采用建筑垃圾制作加气混凝土砌块的配方,其特征在于配料的配比为:建筑垃圾:35-40%,煤灰粉15-25%,生石灰6-11%,水泥10-15%,硅沙3-7%,铝粉(添加剂)0.5-1%,脱流膏3-5%,红泥5-10%。
其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入30-40℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到210-250℃后,静置6-8小时,等待压力泄完后出釜,形成成品。
下面结合实施例对本发明进行进一步描述:
实施例1:
本发明配料的配比为:建筑垃圾:35%,煤灰粉25%,生石灰11%,水泥15%,硅沙5.5%,铝粉(添加剂)0.5%,脱流膏3%,红泥5%。
其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入30℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到210℃后,静置8小时,等待压力泄完后出釜,形成成品。
实施例2:
本发明配料的配比为:建筑垃圾:38%,煤灰粉20%,生石灰8%,水泥12%,硅沙6%,铝粉(添加剂)1%,脱流膏5%,红泥10%。
其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入35℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到230℃后,静置7小时,等待压力泄完后出釜,形成成品。
实施例3:
本发明配料的配比为:建筑垃圾: 40%,煤灰粉15%,生石灰11%,水泥11%,硅沙7%,铝粉(添加剂)1%,脱流膏5%,红泥10%。
其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入40℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到250℃后,静置6小时,等待压力泄完后出釜,形成成品。
以上显示和描述了本发明的主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明的要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种采用建筑垃圾制作加气混凝土砌块,其特征在于配料的配比为:建筑垃圾:35-40%,煤灰粉15-25%,生石灰6-11%,水泥10-15%,硅沙3-7%,铝粉(添加剂)0.5-1%,脱流膏3-5%,红泥5-10%。
2.根据权利要求1所述的一种采用建筑垃圾制作加气混凝土砌块,其特征在于其其加工方法是:按照上述配比的配料,将建筑垃圾进行碾磨粉碎;加入煤灰粉和红泥,混合均匀后,加入30-40℃的水40%,加水后进行充分搅拌成浆状,然后通过细度为200目的过滤筛进行过滤;在过滤后的原料中加入水泥、生石灰和铝粉,加热且充分搅拌1分钟左右,观察待温度在45℃时将最后所得的混合搅拌物进行泄料,倒入模框,待硬度达到切割要求时将模框去掉,按照长高宽为600X200X200mm或600X100X200mm进行切割、编组,将编好组的砌块放入加热釜中加热,待温度达到210-250℃后,静置6-8小时,等待压力泄完后出釜,形成成品。