CN103990456B - 一种氧化银/钒酸银复合光催化剂的制备方法 - Google Patents

一种氧化银/钒酸银复合光催化剂的制备方法 Download PDF

Info

Publication number
CN103990456B
CN103990456B CN201410259164.6A CN201410259164A CN103990456B CN 103990456 B CN103990456 B CN 103990456B CN 201410259164 A CN201410259164 A CN 201410259164A CN 103990456 B CN103990456 B CN 103990456B
Authority
CN
China
Prior art keywords
silver
silver oxide
vanadate
concentration
catalyst
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410259164.6A
Other languages
English (en)
Other versions
CN103990456A (zh
Inventor
马建锋
王凯
李良银
姚超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Hongsheng gloves Co., Ltd
Original Assignee
Changzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou University filed Critical Changzhou University
Priority to CN201410259164.6A priority Critical patent/CN103990456B/zh
Publication of CN103990456A publication Critical patent/CN103990456A/zh
Application granted granted Critical
Publication of CN103990456B publication Critical patent/CN103990456B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种氧化银/钒酸银复合光催化剂的制备方法，具体步骤如下：在搅拌下将25～50mL浓度为0.2～0.4mol/L的硝酸银滴加到25～50mL浓度为0.1～0.2mol/L的氢氧化钠溶液中，得到氧化银颗粒；将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。利用氧化银颗粒作为载体和复合催化剂的成分，利用其和含有过量氨水的钒酸铵反应，氧化银颗粒表面部分转化为钒酸银覆盖于氧化银颗粒表面。钒酸银负载于氧化银银表面，和氧化银银紧密接触，有利于光生电子的跃迁，避免复合，有利于提高催化效率。

Description

一种氧化银/钒酸银复合光催化剂的制备方法
技术领域
本发明属于水处理领域，涉及一种氧化银/钒酸银复合光催化剂的制备方法，尤其涉及一种用于处理有机废水的光催化材料及其制备方法。
背景技术
当前，伴随工业技术的飞速发展，人类赖以生存的水资源均受到不同程度的污染，水资源污染已经成为世界各国面临的亟待解决的问题。水中的污染物，特别是有毒有机污染物的存在，不仅造成环境污染、生态破坏，而且严重危害人类健康。这些有机污染物包括多环芳烃、多氯联苯、农药、环境干扰素、染料等。
钒酸银是一类具有可见光响应的新型光催化剂，其单斜相禁带宽度低于2.7eV，具有较高的可见光响应，且性质稳定，近年来成为研究热点。钒酸银有多种制备方法，如固相合成法、共沉淀法、化学沉积法、有机金属分解法、水热法、超声化学法等。
复合催化剂有利于电子跃迁，在催化剂表面形成自由基而提高催化效率，然而，通常得到的半导体材料为纳米粉体，当其在液相体系中使用时，较小的纳米颗粒悬浮在溶液中不易沉降，难以分离回收，不利于再循环重复使用，另外，复合催化剂的稳定性差，晶体生长困难，粒径和负载量不易控制，难以达到长时间的催化要求，影响和限制了其在工业生产上的实际应用。
发明内容
本发明的目的是为克服现有技术的不足，提供一种氧化银/钒酸银复合光催化剂的制备方法。
本发明的目的可以通过以下技术方案实现：
一种氧化银/钒酸银复合光催化剂的制备方法采用以下方法制得：
1)在搅拌下将25～50mL浓度为0.2～0.4mol/L的硝酸银滴加到25～50mL浓度为0.1～0.2mol/L的氢氧化钠溶液中，得到氧化银颗粒；
2)将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；
3)将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。
本发明的有益效果是：
1、利用氧化银颗粒作为载体和复合催化剂的成分，利用其和含有过量氨水的钒酸铵反应，氧化银颗粒表面部分转化为钒酸银覆盖于氧化银颗粒表面。
2、钒酸银负载于氧化银银表面，和氧化银银紧密接触，有利于光生电子的跃迁，避免复合，有利于提高催化效率。
具体实施方式
实施例1
在搅拌下将25mL浓度为0.4mol/L的硝酸银滴加到50mL浓度为0.1mol/L的氢氧化钠溶液中，得到氧化银颗粒；将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。
将得到的氧化银/钒酸银复合光催化剂加入到装有100mL浓度为30mg/L的OrangeII废水中，在300w碘钨灯照射下，反应60分钟，脱色率为95.2％。相同质量的钒酸银在相同的条件下的脱色率仅为75.2％。
实施例2
在搅拌下将50mL浓度为0.2mol/L的硝酸银滴加到50mL浓度为0.1mol/L的氢氧化钠溶液中，得到氧化银颗粒；将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。
将得到的氧化银/钒酸银复合光催化剂加入到装有100mL浓度为30mg/L的OrangeII废水中，在300w碘钨灯照射下，反应60分钟，脱色率为92.1％。
实施例3
在搅拌下将50mL浓度为0.2mol/L的硝酸银滴加到25mL浓度为0.2mol/L的氢氧化钠溶液中，得到氧化银颗粒；将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。
将得到的氧化银/钒酸银复合光催化剂加入到装有100mL浓度为30mg/L的亚甲基蓝废水中，在300w碘钨灯照射下，反应60分钟，脱色率为92.4％。

Claims (1)

1.一种氧化银/钒酸银复合光催化剂的制备方法，其特征是依次包括如下步骤：
1)在搅拌下将25～50mL浓度为0.2～0.4mol/L的硝酸银滴加到25～50mL浓度为0.1～0.2mol/L的氢氧化钠溶液中，得到氧化银颗粒；
2)将3～5g V2O5粉末溶解于25～30mL浓度为20％～25％(质量百分浓度)的氨水溶液中，保持氨水过量，制得钒酸铵溶液；
3)将氧化银颗粒加入到钒酸铵溶液中，搅拌3～4分钟，迅速分离，用蒸馏水洗涤3～4次，105℃烘干，即制得一种氧化银/钒酸银复合光催化剂。
CN201410259164.6A 2014-06-11 2014-06-11 一种氧化银/钒酸银复合光催化剂的制备方法 Active CN103990456B (zh)