CN103979869A - 一种用铁矿尾渣制成的轻质隔墙板及其制作方法 - Google Patents

一种用铁矿尾渣制成的轻质隔墙板及其制作方法 Download PDF

Info

Publication number
CN103979869A
CN103979869A CN201410152188.1A CN201410152188A CN103979869A CN 103979869 A CN103979869 A CN 103979869A CN 201410152188 A CN201410152188 A CN 201410152188A CN 103979869 A CN103979869 A CN 103979869A
Authority
CN
China
Prior art keywords
parts
iron ore
ore tailings
partition board
lightweight partition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410152188.1A
Other languages
English (en)
Other versions
CN103979869B (zh
Inventor
叶赵伍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yi Xin Energy-Saving Material Co Ltd
Original Assignee
Anhui Yi Xin Energy-Saving Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yi Xin Energy-Saving Material Co Ltd filed Critical Anhui Yi Xin Energy-Saving Material Co Ltd
Priority to CN201410152188.1A priority Critical patent/CN103979869B/zh
Publication of CN103979869A publication Critical patent/CN103979869A/zh
Application granted granted Critical
Publication of CN103979869B publication Critical patent/CN103979869B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用铁矿尾渣制成的轻质隔墙板，其特征在于，由下列重量份的原料制成：水泥20-25、涤纶纤维12-16、工业氟石膏19-21、钢纤维8-12、粉煤灰18-22、磷酸三酊酯2-5、木质素磺酸盐3-6、邻苯二甲酸丁苄酯1-4、氧化锌0.4-0.9、铁矿尾渣18-24、花生壳16-20、亚麻仁油1-3、助剂2-5、适量水；本发明将铁矿尾渣、粉煤灰等废弃物“无害化”和“资源化”，变废为宝，具有重大的经济效益和社会效益，本发明生产的轻质隔墙板具有吸收甲醛、高强度、轻质量、保温、隔热、防水、抗冲击、不返卤等突出特点，可替代传统隔墙红砖、加气砖、菱镁板及石膏板，应用前景广阔。

Description

一种用铁矿尾渣制成的轻质隔墙板及其制作方法
技术领域
本发明涉及建筑材料领域，具体涉及一种用铁矿尾渣制成的轻质隔墙板及其制作方法。
背景技术
轻质隔墙板是由无害化磷石膏、轻质钢渣、粉煤灰等多种工业废渣组成，经变频蒸汽加压养护而成的一种新型节能墙材料，它是一种外型象空心楼板一样的墙材，但是它两边有公母隼槽，安装时只需将板材立起，公、母隼涂上少量嵌缝砂浆后对拼装起来即可。它具有质量轻、强度高、多重环保、保温隔热、隔音、呼吸调湿、防火、快速施工、降低墙体成本等优点，故而在建筑室内装修领域备受青睐，然而目前市场上使用的轻质隔墙板抗压强度低、抗拉强度弱、抗开裂性能和吊挂能力不佳、生产成本高、隔音保温效果差等缺点。
发明内容
本发明的目的就是提供一种用铁矿尾渣制成的轻质隔墙板及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种用铁矿尾渣制成的轻质隔墙板，其特征在于，由下列重量份的原料制成：水泥20-25、涤纶纤维12-16、工业氟石膏19-21、钢纤维8-12、粉煤灰18-22、磷酸三酊酯2-5、木质素磺酸盐3-6、邻苯二甲酸丁苄酯1-4、氧化锌0.4-0.9、铁矿尾渣18-24、花生壳16-20、亚麻仁油1-3、助剂2-5、适量水。
所述的助剂由下列重量份原料制成：火山灰6-9、元明粉2-5、氯化镁3-5、氧化镁2-4、聚乙烯醇0.2-0.5、偏硅酸钠0.03-0.07、铝酸钠0.05-0.6、酒石酸0.8-2.1、硅丙乳液2.1-4.3、2-咪唑烷酮0.04-0.09、碳化硅1-3、促进剂CZ  0.03-0.05、丁香油1.2-3.2，其制备方法是将50%氯化镁溶液中加入氧化镁粉末搅拌均匀得无机胶凝剂，然后将其他剩余物料粉碎混匀，加适量水搅拌30-40分钟成浆，造粒，成球粒径在2-5mm，烘干即得。
所述的一种用铁矿尾渣制成的轻质隔墙板的制备方法，其特征在于包括以下步骤：
（1）将花生壳送入炭化炉中，在503-638℃下炭化处理3-4小时，取出，粉碎成粉末，向所得的粉末在鼓风使其翻腾条件下喷雾状亚麻仁油，再加入钢纤维搅拌使之混匀；
（2）将铁矿尾渣、工业氟石膏、粉煤灰于601-848℃下煅烧3-6小时后取出，粉碎；
（3）取涤纶纤维加热到250-300℃，搅拌10-18分钟，趁热加入步骤（2）的反应物料和邻苯二甲酸丁苄酯搅拌5-10分钟，冷却，研磨成粉；
（4）将步骤（1）、（3）反应物料及其他剩余物料粉碎加适量水搅拌混匀得料浆，将制得的浆料加入墙板挤压成型机成型、切割、自然养护，即得。
本发明有以下有益效果：本发明将铁矿尾渣、粉煤灰等废弃物“无害化”和“资源化”，变废为宝，具有重大的经济效益和社会效益，本发明生产的轻质隔墙板具有吸收甲醛、高强度、轻质量、保温、隔热、防水、抗冲击、不返卤等突出特点，可替代传统隔墙红砖、加气砖、菱镁板及石膏板，应用前景广阔。
具体实施方式
所述的一种用铁矿尾渣制成的轻质隔墙板，其特征在于，由下列重量份的原料制成：水泥20、涤纶纤维12、工业氟石膏19、钢纤维9、粉煤灰18、磷酸三酊酯4、木质素磺酸盐3、邻苯二甲酸丁苄酯1、氧化锌0.4、铁矿尾渣18、花生壳16、亚麻仁油1、助剂2、适量水。
所述的助剂由下列重量份原料制成：火山灰6、元明粉2、氯化镁5、氧化镁4、聚乙烯醇0.25、偏硅酸钠0.05、铝酸钠0.4、酒石酸0.8、硅丙乳液2.3、2-咪唑烷酮0.04、碳化硅1、促进剂CZ  0.03、丁香油1.2，其制备方法是将50%氯化镁溶液中加入氧化镁粉末搅拌均匀得无机胶凝剂，然后将其他剩余物料粉碎混匀，加适量水搅拌30-40分钟成浆，造粒，成球粒径在2-5mm，烘干即得。
制作方法包括以下步骤：
（1）将花生壳送入炭化炉中，在503-638℃下炭化处理3-4小时，取出，粉碎成粉末，向所得的粉末在鼓风使其翻腾条件下喷雾状亚麻仁油，再加入钢纤维搅拌使之混匀；
（2）将铁矿尾渣、工业氟石膏、粉煤灰于601-848℃下煅烧3-6小时后取出，粉碎；
（3）取涤纶纤维加热到250-300℃，搅拌10-18分钟，趁热加入步骤（2）的反应物料和邻苯二甲酸丁苄酯搅拌5-10分钟，冷却，研磨成粉；
（4）将步骤（1）、（3）反应物料及其他剩余物料粉碎加适量水搅拌混匀得料浆，将制得的浆料加入墙板挤压成型机成型、切割、自然养护，即得。
通过上述实施例加工得到的轻质隔墙板的技术指标如下：
（1）容重：520kg/m3；
（2）导热系数（平均温度25±2℃）：0.079W/(m·k)；
（3）抗压强度：5.1MPa；
（4）耐高温，外观平整光滑。

Claims (2)

1.一种用铁矿尾渣制成的轻质隔墙板，其特征在于，由下列重量份的原料制成：水泥20-25、涤纶纤维12-16、工业氟石膏19-21、钢纤维8-12、粉煤灰18-22、磷酸三酊酯2-5、木质素磺酸盐3-6、邻苯二甲酸丁苄酯1-4、氧化锌0.4-0.9、铁矿尾渣18-24、花生壳16-20、亚麻仁油1-3、助剂2-5、适量水；所述的助剂由下列重量份原料制成：火山灰6-9、元明粉2-5、氯化镁3-5、氧化镁2-4、聚乙烯醇0.2-0.5、偏硅酸钠0.03-0.07、铝酸钠0.05-0.6、酒石酸0.8-2.1、硅丙乳液2.1-4.3、2-咪唑烷酮0.04-0.09、碳化硅1-3、促进剂CZ  0.03-0.05、丁香油1.2-3.2，其制备方法是将50%氯化镁溶液中加入氧化镁粉末搅拌均匀得无机胶凝剂，然后将其他剩余物料粉碎混匀，加适量水搅拌30-40分钟成浆，造粒，成球粒径在2-5mm，烘干即得。
2.根据权利要求1所述的一种用铁矿尾渣制成的轻质隔墙板的制作方法，其特征在于包括以下步骤：
（1）将花生壳送入炭化炉中，在503-638℃下炭化处理3-4小时，取出，粉碎成粉末，向所得的粉末在鼓风使其翻腾条件下喷雾状亚麻仁油，再加入钢纤维搅拌使之混匀；
（2）将铁矿尾渣、工业氟石膏、粉煤灰于601-848℃下煅烧3-6小时后取出，粉碎；
（3）取涤纶纤维加热到250-300℃，搅拌10-18分钟，趁热加入步骤（2）的反应物料和邻苯二甲酸丁苄酯搅拌5-10分钟，冷却，研磨成粉；
（4）将步骤（1）、（3）反应物料及其他剩余物料粉碎加适量水搅拌混匀得料浆，将制得的浆料加入墙板挤压成型机成型、切割、自然养护，即得。
CN201410152188.1A 2014-04-16 2014-04-16 一种用铁矿尾渣制成的轻质隔墙板及其制作方法 Active CN103979869B (zh)