CN103965830A - Preparation method for bamboo wood chip foam having negative oxygen ions - Google Patents
Preparation method for bamboo wood chip foam having negative oxygen ions Download PDFInfo
- Publication number
- CN103965830A CN103965830A CN201310038447.3A CN201310038447A CN103965830A CN 103965830 A CN103965830 A CN 103965830A CN 201310038447 A CN201310038447 A CN 201310038447A CN 103965830 A CN103965830 A CN 103965830A
- Authority
- CN
- China
- Prior art keywords
- bamboo wood
- wood chip
- negative oxygen
- oxygen ion
- chip foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a preparation method for bamboo wood chip foam having negative oxygen ions. The method comprises: 1, selecting a bamboo wood chip foam base material, 2, preparing a nanometer tourmaline negative oxygen ion slurry, 3, jetting or fusing the nanometer tourmaline negative oxygen ion slurry prepared in the step 2 into the bamboo wood chip foam base material, and 4, drying the jetted or fused bamboo wood chip foam base material to obtain the bamboo wood chip foam finished product having negative oxygen ions, wherein the nanometer tourmaline negative oxygen ion slurry preparing step comprises dissolving tourmaline into water, a weight ratio of the tourmaline to water is 4:6, and the fusing step comprises soaking the bamboo wood chip foam base material in the nanometer tourmaline negative oxygen ion slurry for 24 h. The method has beneficial effects of practicality, easily available base material, low production cost and easy use, wherein the prepared negative oxygen ion active carbon can be provided for effectively improving surrounding air environment.
Description
Technical field
The present invention relates to a kind of manufacture method of negative oxygen ion product, particularly a kind of manufacture method with negative oxygen ion bamboo wood chip foam.
Background technology
Negative oxygen ion colorless and odorless, its function is but very surprising, consequently by medical circle, is become " air VITAMIN ".First, it can enter in human body by blood and refreshing level system, and people's organism physiology activity is exerted an influence.When negative oxygen ion enters brain, can, by adjusting corticocerebral function, play and improve sleep quality, the effect of reducing blood pressure.When negative oxygen ion enters after human respiratory tract, can make bronchial smooth muscle lax, improve cardiorespiratory system function, increase work efficiency.Negative oxygen ion can reduce human-body fatigue in blood, improves human body reaction, improves body immunity.Secondly, negative oxygen ion can also play cleaning action to airborne oil smoke, second hand smoking, thus the respiratory disease such as prevention pneumonia, trachitis, and alleviate the negative effect that smoking causes.
Negative oxygen ion is the indispensable material of human body, 13,000,000,000 negative oxygen ions of human body needs every day, but the negative oxygen ion that urbanite can only obtain 2,000,000,000 left and right every day particularly general indoor obtainable just still less, main because present atmospheric pollution is more and more serious, airborne negative oxygen ion reason less and less causes.
At present, also there is no well to manufacture the method for anion material, and negative ion product, in addition, bamboo wood chip foam has good adsorptive power, the cost of its acquisition is also low, at present, bamboo wood chip foam is substantially all that utilization ratio is low like this with the fuel of make a return journey moisture or conduct burning, caused the very large wasting of resources, bamboo wood chip foam resource is not reasonably utilized.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, and a kind of manufacture method with negative oxygen ion bamboo wood chip foam is provided.
To achieve these goals, the measure that the present invention takes:
With a manufacture method for negative oxygen ion bamboo wood chip foam, the first step: choose bamboo wood chip foam sill; Second step: preparation of nano tourmalinite negative oxygen ion slurries; The 3rd step: the nano-tourmaline negative oxygen ion slurries spray that above-mentioned second step is prepared or fuse in bamboo wood chip foam sill; The 4th step: spray or the bamboo wood chip foam sill that fused are dried, can obtain with negative oxygen ion bamboo wood chip foam finished product;
The bamboo wood chip foam sill that the described the first step is chosen is bamboo wood chip foam or bamboo wood saw foam;
The nano-tourmaline negative oxygen ion slurries of described second step preparation are for to be dissolved in tourmalinite in water, and the weight ratio of tourmalinite and water is 4: 6;
The 3rd described step is by the uniform spray of nano-tourmaline negative oxygen ion slurries or fuses bamboo wood chip foam sill inside or surperficial;
Fusing for bamboo wood chip foam sill being immersed in nano-tourmaline negative oxygen ion slurries to 24 hours of the 3rd described step;
The 4th described step is dried as air-dry at 15～50 ℃ of temperature.
Beneficial effect of the present invention: practicality, sill easily obtains, and production cost is low, easy to use, and produced negative oxygen ion gac can effectively improve people's ambient air environment, as: the Air quality in compartment, the Air quality in parlor.
Embodiment
With a manufacture method for negative oxygen ion bamboo wood chip foam, the first step: choose bamboo wood chip foam sill; Second step: preparation of nano tourmalinite negative oxygen ion slurries; The 3rd step: the nano-tourmaline negative oxygen ion slurries spray that above-mentioned second step is prepared or fuse in bamboo wood chip foam sill; The 4th step: spray or the bamboo wood chip foam sill that fused are dried, can obtain with negative oxygen ion bamboo wood chip foam finished product, negative oxygen ion bamboo wood chip foam finished product when in use, can improve the quality of ambient air; The bamboo wood chip foam sill that the described the first step is chosen is bamboo wood chip foam or bamboo wood saw foam, effectively reduce production cost, bamboo wood chip foam or bamboo wood saw foam are reasonably used, and bamboo wood chip foam or bamboo wood saw foam are softer, be convenient to being dispersed in air of negative oxygen ion, easy to use; The nano-tourmaline negative oxygen ion slurries of described second step preparation are for to be dissolved in tourmalinite in water, and the weight ratio of tourmalinite and water is 4: 6, makes the nano-tourmaline content in solution high, and the product of producing is long duration of service; The 3rd described step is for by the uniform spray of nano-tourmaline negative oxygen ion slurries or to fuse bamboo wood chip foam sill inner or surperficial, and production cost is low, is convenient to nanometer acetylene to improve air, evaporate in air; Fusing for bamboo wood chip foam sill being immersed in nano-tourmaline negative oxygen ion slurries to 24 hours of the 3rd described step, the negative oxygen ion in bamboo wood chip foam is more abundant, and duration of service is long; The 4th described step is dried as air-dry at 15～50 ℃ of temperature, can guarantee sill, and the negative oxygen ion content in bamboo wood chip foam is high, thereby realizes object of the present invention.
Those ordinary skill in the art's simple change and replacement are all within protection scope of the present invention.
Claims (6)
1. with a manufacture method for negative oxygen ion bamboo wood chip foam, it is characterized in that:
The first step: choose bamboo wood chip foam sill;
Second step: preparation of nano tourmalinite negative oxygen ion slurries;
The 3rd step: the nano-tourmaline negative oxygen ion slurries spray that above-mentioned second step is prepared or fuse in bamboo wood chip foam sill;
The 4th step: spray or the bamboo wood chip foam sill that fused are dried, can obtain with negative oxygen ion bamboo wood chip foam finished product.
2. a kind of manufacture method with negative oxygen ion bamboo wood chip foam according to claim 1, is characterized in that: the bamboo wood chip foam sill that the described the first step is chosen is bamboo wood chip foam or bamboo wood saw foam.
3. a kind of manufacture method with negative oxygen ion bamboo wood chip foam according to claim 1, is characterized in that: the nano-tourmaline negative oxygen ion slurries of described second step preparation are for to be dissolved in tourmalinite in water, and the weight ratio of tourmalinite and water is 4: 6.
4. a kind of manufacture method with negative oxygen ion bamboo wood chip foam according to claim 1, is characterized in that: the 3rd described step is by the uniform spray of nano-tourmaline negative oxygen ion slurries or fuses bamboo wood chip foam sill inside or surperficial.
5. a kind of manufacture method with negative oxygen ion bamboo wood chip foam according to claim 1, is characterized in that: the fusing for bamboo wood chip foam sill being immersed in nano-tourmaline negative oxygen ion slurries to 24 hours of the 3rd described step.
6. a kind of manufacture method with negative oxygen ion bamboo wood chip foam according to claim 1, is characterized in that: the 4th described step is dried as air-dry at 15～50 ℃ of temperature.