CN103965412A - 一种防霉菌阻燃耐高温片状模塑料及其制备方法 - Google Patents
一种防霉菌阻燃耐高温片状模塑料及其制备方法 Download PDFInfo
- Publication number
- CN103965412A CN103965412A CN201410220770.7A CN201410220770A CN103965412A CN 103965412 A CN103965412 A CN 103965412A CN 201410220770 A CN201410220770 A CN 201410220770A CN 103965412 A CN103965412 A CN 103965412A
- Authority
- CN
- China
- Prior art keywords
- temperature
- molding compound
- preparation
- resistant
- tert
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种防霉菌阻燃耐高温片状模塑料及其制备方法,属于装饰材料领域,配方包括不饱和聚酯树脂,低收缩添加剂,叔丁酯TBPB,二氧化钛,硬脂酸锌,对苯醌,苯乙烯,碳酸钙,氢氧化铝,氧化镁,PE膜,玻璃纤维,2,6-二叔丁基对甲酚,本发明的有益效果为用新型玻璃钢材料代替现有的金属吊顶材料,轻质强韧坚固耐磨,且不易发潮更不容易发霉不滋生细菌,还具有阻燃耐高温防电的效果,最主要的是无毒害耐腐蚀,还可以通过人们不同的喜好来调配任意颜色。
Description
技术领域
本发明涉及到装饰材料领域,具体涉及到一种防霉菌阻燃耐高温片状模塑料及其制备方法。
背景技术
PVC吊顶塑料材质的普遍缺点就是物理性能不够稳定,所以关键的问题就在于,即便PVC不遇水,时间长了也会变形;目前大多数都是塑钢板,但现代的家装塑钢板有些地方已经表现出来落伍的现象了:有的虽可阻燃,但其耐高温性能不佳,不防火;隔音效果差,实用性不强,颜色单调样式呆板,塑钢板一般都是一种颜色不能实现多颜色;还有一种就是最新潮的金属材质的吊顶,但是此材料时间长会滋生细菌和发霉,并且有辐射不防电,再就是需要经常保持金属面的干净。
发明内容
本发明的目的提供一种防霉菌阻燃耐高温片状模塑料及其制备方法,该材料具有电绝缘性能,热稳定性,耐化学防腐性,解决上述吊顶材料的不足。
本发明是通过以下方式实现的一种防霉菌阻燃耐高温片状模塑料及其制备方法,该材料的配方由以下重量百分比的各组分制备:
不饱和聚酯树脂 14%~18%
低收缩添加剂 8%~12%
叔丁酯TBPB 0.1%~0.4%
二氧化钛 0.5%~0.9%
硬脂酸锌 1%~2%
对苯醌 0.2%~0.5%
苯乙烯 1.2%~1.6%
碳酸钙 4%~5%
氢氧化铝 30%~35%
氧化镁 0.8%~1.2%
PE膜 1.8%~2.3%
玻璃纤维 26%~29%
2,6-二叔丁基对甲酚 0.1%~0.5%
所述材料配方各组分质量比为:不饱和聚酯树脂16%,低收缩添加剂10.7%,叔丁酯TBPB0.2%,二氧化钛0.7%,硬脂酸锌1.5%,对苯醌0.3%,苯乙烯1.4%,碳酸钙4.7%,氢氧化铝33.3%,氧化镁0.95%,PE膜2.1%,玻璃纤维27.9%,2,6-二叔丁基对甲酚0.3%。
制备方法为:最先将对苯醌和苯乙烯进行混合调制放置,然后将不饱和聚酯树脂倒入容器,添加低收缩添加剂进行搅拌,再同时加入叔丁酯TBPB和2,6-二叔丁基对甲酚,当叔丁酯TBPB和2,6-二叔丁基对甲酚倒入之后再加入事先调制好的对苯醌和苯乙烯的混合溶液,再依次加入二氧化钛和硬脂酸锌进行充分搅拌,充分搅拌之后在放入碳酸钙和氢氧化铝所得的溶液放到片台机上,通过片台机依次混入氧化镁,PE膜和玻璃纤维。
所述的片台机中的温度控制在40摄氏度以下。
用于A级的传统SMC的密度为1.8~1.9g/cm3,这比铝低30%,比钢低75%,但是在材料中还是较高,此配方产出的产品密度抵达1.3g/cm3,比钢的重量减少了35%~40%,而且隔热能力强于金属100~200倍,能长时间接收200℃的高温。
本发明的有益效果为用新型玻璃钢材料代替现有的金属吊顶材料,轻质强韧坚固耐磨,且不易发潮更不容易发霉不滋生细菌,还具有阻燃耐高温防电的效果,最主要的是无毒害耐腐蚀,还可以通过人们不同的喜好来调配任意颜色。
具体实施方式
实施例1
按照配方采取各组分的质量比为:不饱和聚酯树脂14%,低收缩添加剂8%,叔丁酯TBPB0.1%,二氧化钛0.5%,硬脂酸锌1%,对苯醌0.2%,苯乙烯1.2%,碳酸钙4%,氢氧化铝30%,氧化镁0.8%,PE膜1.8%,玻璃纤维26%,2,6-二叔丁基对甲酚0.1%。
制备方法为:最先将对苯醌和苯乙烯进行混合调制放置,然后将不饱和聚酯树脂倒入容器,添加低收缩添加剂进行搅拌,再同时加入叔丁酯TBPB和2,6-二叔丁基对甲酚,当叔丁酯TBPB和2,6-二叔丁基对甲酚倒入之后再加入事先调制好的对苯醌和苯乙烯的混合溶液,再依次加入二氧化钛和硬脂酸锌进行充分搅拌,充分搅拌之后在放入碳酸钙和氢氧化铝所得的溶液放到片台机上,通过片台机依次混入氧化镁,PE膜和玻璃纤维。所述的片台机中的温度控制在40摄氏度以下。
实施例2
按照配方采取各组分的质量比为:不饱和聚酯树脂16%,低收缩添加剂10.7%,叔丁酯TBPB0.2%,二氧化钛0.7%,硬脂酸锌1.5%,对苯醌0.3%,苯乙烯1.4%,碳酸钙4.7%,氢氧化铝33.3%,氧化镁0.95%,PE膜2.1%,玻璃纤维27.9%,2,6-二叔丁基对甲酚0.3%。
制作方法同实施例1。
实施例3
按照配方采取各组分的质量比为:不饱和聚酯树脂18%,低收缩添加剂12%,叔丁酯TBPB0.4%,二氧化钛0.9%,硬脂酸锌2%,对苯醌0.5%,苯乙烯1.6%,碳酸钙5%,氢氧化铝35%,氧化镁1.2%,PE膜2.3%,玻璃纤维29%,2,6-二叔丁基对甲酚0.5%。
制作方法同实施例1。
通过以上实施例的实验证实最好的一组质量分数比例为实施例2。
Claims (3)
1.一种防霉菌阻燃耐高温片状模塑料及其制备方法,其特征在于,该材料的配方由以下重量百分比的各组分制备:
不饱和聚酯树脂 14%~18%
低收缩添加剂 8%~12%
叔丁酯TBPB 0.1%~0.4%
二氧化钛 0.5%~0.9%
硬脂酸锌 1%~2%
对苯醌 0.2%~0.5%
苯乙烯 1.2%~1.6%
碳酸钙 4%~5%
氢氧化铝 30%~35%
氧化镁 0.8%~1.2%
PE膜 1.8%~2.3%
玻璃纤维 26%~29%
2,6-二叔丁基对甲酚 0.1%~0.5%。
2.根据权利要求1所述的一种防霉菌阻燃耐高温片状模塑料及其制备方法,其特征在于,制备方法为:最先将对苯醌和苯乙烯进行混合调制放置,然后将不饱和聚酯树脂倒入容器,添加低收缩添加剂进行搅拌,再同时加入叔丁酯TBPB和2,6-二叔丁基对甲酚,当叔丁酯TBPB和2,6-二叔丁基对甲酚倒入之后再加入事先调制好的对苯醌和苯乙烯的混合溶液,再依次加入二氧化钛和硬脂酸锌进行充分搅拌,充分搅拌之后在放入碳酸钙和氢氧化铝所得的溶液放到片台机上,通过片台机依次混入氧化镁,PE膜和玻璃纤维。
3.根据权利要求2所述的一种防霉菌阻燃耐高温片状模塑料及其制备方法,其特征在于,所述的片台机中的温度控制在40摄氏度以下。