CN103964817A - Blue and white porcelain material - Google Patents
Blue and white porcelain material Download PDFInfo
- Publication number
- CN103964817A CN103964817A CN201410140899.7A CN201410140899A CN103964817A CN 103964817 A CN103964817 A CN 103964817A CN 201410140899 A CN201410140899 A CN 201410140899A CN 103964817 A CN103964817 A CN 103964817A
- Authority
- CN
- China
- Prior art keywords
- white porcelain
- powder
- bule
- percent
- blue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of porcelain and discloses a blue and white porcelain material. The blue and white porcelain material is prepared by the following raw materials by weight percentage: 75.5-83.2 percent of natural clay, 10 to 15 percent of quartz, 2.6 to 5 percent of aluminium oxide powder, 2 to 4 percent of zirconium dioxide powder, and 0.4 to 0.8 percent of yttrium oxide powder. The blue and white porcelain prepared through the materials provided by the formula of the invention has the characteristics of low friction and high abrasion resistance, the defective percentage due to breakage is greatly lowered, and the production cost is lowered.
Description
Technical field
The invention belongs to ceramic production technology field, be specifically related to a kind of bule and white porcelain material.
Background technology
Pottery be take clay as main raw material and various natural mineral are mixing through pulverizing, moulding and the calcining material and the various goods that make.People a kind of potter's clay is made in special kiln high-temperature firing article pottery, pottery is the general name of pottery and porcelain.The traditional concept of pottery refers to all artificial Industrial products that the inorganic non-metallic mineral such as clay are raw material of take.It comprises by clay or the mixture that contains clay through mixing, is shaped, and calcining and the various goods made.By the most coarse earthenware, to the meticulousst fine pottery and porcelain, all belong to its scope.Therefore main raw material for it is to take from natural silicate minerals (as clay, quartz etc.), with the industry such as glass, cement, enamel, refractory materials, belongs to the category of " silicate industry ".Bule and white porcelain is a kind of of pottery, and the common problem of existing bule and white porcelain material is: fracture, and fracture mode shows as transgranular fracture, and fracture fraction defective reaches 4%, thereby has greatly increased bule and white porcelain production cost.
summary of the invention
For above-mentioned situation, the object of this invention is to provide a kind of bule and white porcelain material.
The present invention takes following scheme of the invention to realize: a kind of bule and white porcelain material, and the formula of described bule and white porcelain material is made by the raw material of following weight percent content: natural clay 75.5-83.2%; Quartzy 10-15%; Alumina powder 2.6-5%; Zirconium dioxide powder 2-4%; Yttrium oxide powder 0.4-0.8%.
The formula of described bule and white porcelain material comprises the raw material of following weight percent content: natural clay 78.6%; Quartzy 13%; Alumina powder 4.6%; Zirconium dioxide powder 3.2%; Yttrium oxide powder 0.6%.
Alumina powder: high temperature thermal insulation material and reinforced composite, aluminum oxide aluminium powder has outstanding resistance to elevated temperatures.
Zirconium dioxide powder: there is high rigidity, high strength, high tenacity, the physical and chemical performance that high wear resistance and chemical resistance etc. are good.
Yttrium oxide powder: high temperature resistant and radiation hardness additive.
Production method of the present invention is that the natural clay of aforementioned proportion, quartz, alumina powder, Zirconium dioxide powder and yttrium oxide powder are first passed through to stirrer batch mixing, then through shredder, grind and granulator granulation, makes the bule and white porcelain powder mixing; Then the moulding of described bule and white porcelain powder is made to material base; Finally, by described material base sintering, obtain bule and white porcelain material.
The present invention has following beneficial effect in sum: the bule and white porcelain of making by formula materials provided by the present invention, there is the characteristic of low friction, high abrasion, and fracture fraction defective reduces greatly, has reduced production cost.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail:
Embodiment 1
A bule and white porcelain material, the formula of described bule and white porcelain material is made by the raw material of following weight percent content: natural clay 75.5-83.2%; Quartzy 10-15%; Alumina powder 2.6-5%; Zirconium dioxide powder 2-4%; Yttrium oxide powder 0.4-0.8%.
Alumina powder: high temperature thermal insulation material and reinforced composite, aluminum oxide aluminium powder has outstanding resistance to elevated temperatures.
Zirconium dioxide powder: there is high rigidity, high strength, high tenacity, the physical and chemical performance that high wear resistance and chemical resistance etc. are good.
Yttrium oxide powder: high temperature resistant and radiation hardness additive.
Production method of the present invention is that the natural clay of aforementioned proportion, quartz, alumina powder, Zirconium dioxide powder and yttrium oxide powder are first passed through to stirrer batch mixing, then through shredder, grind and granulator granulation, makes the bule and white porcelain powder mixing; Then the moulding of described bule and white porcelain powder is made to material base; Finally, by described material base sintering, obtain bule and white porcelain material.
Embodiment 2
The formula of described bule and white porcelain material comprises the raw material of following weight percent content: natural clay 78.6%; Quartzy 13%; Alumina powder 4.6%; Zirconium dioxide powder 3.2%; Yttrium oxide powder 0.6%.
Production method is with embodiment 1.
Through embodiment 1 and 2 is carried out to scientific statistics discovery, the effect of embodiment 2 is best, and fracture fraction defective is only 0.45%, greatly reduces fraction defective.
Claims (2)
1. a bule and white porcelain material, is characterized in that, the formula of described bule and white porcelain material is made by the raw material of following weight percent content: natural clay 75.5-83.2%; Quartzy 10-15%; Alumina powder 2.6-5%; Zirconium dioxide powder 2-4%; Yttrium oxide powder 0.4-0.8%.
2. according to the bule and white porcelain material described in claim 1, it is characterized in that, the formula of described bule and white porcelain material comprises the raw material of following weight percent content: natural clay 78.6%; Quartzy 13%; Alumina powder 4.6%; Zirconium dioxide powder 3.2%; Yttrium oxide powder 0.6%.