CN103951902B - A kind of polyvinyl chloride cable material for automobile and preparation method thereof - Google Patents
A kind of polyvinyl chloride cable material for automobile and preparation method thereof Download PDFInfo
- Publication number
- CN103951902B CN103951902B CN201410116452.6A CN201410116452A CN103951902B CN 103951902 B CN103951902 B CN 103951902B CN 201410116452 A CN201410116452 A CN 201410116452A CN 103951902 B CN103951902 B CN 103951902B
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- automobile
- agent
- hour
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of polyvinyl chloride cable material for automobile, it is characterized in that, be made up of the raw material of following weight part: SG-4 polyvinyl chloride 30-34, trioctyl trimellitate 12-15, Flos Rosae Rugosae quintessence oil 0.2-0.3, Paris white 20-24, propionate 5-6, octyl epoxy stearate 5-7, anti-scorching agent CTP 1-2, vinyl three ('beta '-methoxy oxyethyl group) silane 3-4, polyisobutene 4-6, isocyanic ester 1-2, anti-aging agent OD? 1-2, auxiliary agent 6-8; CABLE MATERIALS for automobile of the present invention effectively can reduce smell, has excellent tensile strength, wear resistance, thermotolerance simultaneously, has again good surface and mechanical property.
Description
Technical field
The present invention relates to polymeric material field, particularly a kind of polyvinyl chloride cable material for automobile and preparation method thereof.
Background technology
Usual automobile electric wire polyvinyl chloride cable material production method take polyvinyl chloride (PVC) RESINS as base-material, add softening agent, stablizer and processing aid, process through special kneading device, although automotive line production primary demand can be met, there is the problem that smell is large, scraped finish performance is not good and processing characteristics is undesirable.Automotive line due to its use location special, automobile cannot avoid mutual friction between the lines in operational process, once the worn out meeting of plastics jacket directly causes short circuit to cause hidden peril of accident, in addition, automobile bodies is a space comparatively closed, the necessary environment-friendly tasteless of the kit item used in compartment, to the healthy not damaged of people.In sum, automotive line PVC Insulation Material, also must tasteless, resistance to scraped finish except necessary electric property.
Summary of the invention
The object of this invention is to provide a kind of polyvinyl chloride cable material for automobile and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
For a polyvinyl chloride cable material for automobile, be made up of the raw material of following weight part: SG-4 polyvinyl chloride 30-34, trioctyl trimellitate 12-15, Flos Rosae Rugosae quintessence oil 0.2-0.3, Paris white 20-24, propionate 5-6, octyl epoxy stearate 5-7, anti-scorching agent CTP 1-2, vinyl three ('beta '-methoxy oxyethyl group) silane 3-4, polyisobutene 4-6, isocyanic ester 1-2, anti-aging agent OD1-2, auxiliary agent 6-8;
Described auxiliary agent is made up of the raw material of following weight part: diatomite 10-12, tri (propylene glycol) diacrylate 2-3, zinc oxide 5-6, jade powder 4-5,3-aminopropyl trimethoxysilane 2-3, linking agent TAC1-2, Zinc Gluconate 1-2, Zinic stearas 1-2, magnesium nitrate 7-9, Syzygium aromaticum stem oil 1-2, Flos Rosae Rugosae quintessence oil 0.1-0.2; Diatomite in powder is sent in calcining furnace to calcine 3-4 hour at 700-730 DEG C by preparation method, take out, send in 10-15% hydrochloric acid and soak 1-2 hour, filter to obtain filter residue, wash with clear water, dry, be ground into 200-250 order powder, then the powder of drying is mixed with tri (propylene glycol) diacrylate, zinc oxide, linking agent TAC, grinding 1-2 hour, add other remaining component again, mixed grinding 1-2 hour, to obtain final product.
Polyvinyl chloride cable material for automobile of the present invention, be made up of following concrete steps:
(1) SG-4 polyvinyl chloride is heated to molten state, add trioctyl trimellitate, Flos Rosae Rugosae quintessence oil, Paris white, propionate, octyl epoxy stearate, anti-scorching agent CTP, auxiliary agent, stir and mediate 15-25 minute, send into twin screw extruder granulation, obtain A material;
(2) by all the other remaining components heating mixed melting, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3), after A, B material being mixed, melt extrude granulation on the twin screw extruder, to obtain final product.
Excellent effect of the present invention is: the CABLE MATERIALS for automobile of the present invention effectively can reduce smell, has excellent tensile strength, wear resistance, thermotolerance simultaneously, has again good surface and mechanical property.
Embodiment
Below by specific examples, the present invention is described in detail.
For a polyvinyl chloride cable material for automobile, be made up of the raw material of following weight part (kilogram): SG-4 polyvinyl chloride 30, trioctyl trimellitate 12, Flos Rosae Rugosae quintessence oil 0.2, Paris white 20, propionate 5, octyl epoxy stearate 5, anti-scorching agent CTP 1, vinyl three ('beta '-methoxy oxyethyl group) silane 3, polyisobutene 4, isocyanic ester 1, anti-aging agent OD1, auxiliary agent 6;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): diatomite 10, tri (propylene glycol) diacrylate 3, zinc oxide 5, jade powder 4,3-aminopropyl trimethoxysilane 2, linking agent TAC2, Zinc Gluconate 1, Zinic stearas 2, magnesium nitrate 9, Syzygium aromaticum stem oil 2, Flos Rosae Rugosae quintessence oil 0.1; Diatomite is sent in calcining furnace to calcine 3-4 hour at 700-730 DEG C by preparation method, take out, send in 10-15% hydrochloric acid and soak 1-2 hour, filter to obtain filter residue, wash with clear water, dry, be ground into 200-250 order powder, then the powder of drying is mixed with tri (propylene glycol) diacrylate, zinc oxide, linking agent TAC, grinding 1-2 hour, add other remaining component again, mixed grinding 1-2 hour, to obtain final product.
Polyvinyl chloride cable material for automobile of the present invention, be made up of following concrete steps:
(1) SG-4 polyvinyl chloride is heated to molten state, add trioctyl trimellitate, Flos Rosae Rugosae quintessence oil, Paris white, propionate, octyl epoxy stearate, anti-scorching agent CTP, auxiliary agent, stir and mediate 15-25 minute, send into twin screw extruder granulation, obtain A material;
(2) by all the other remaining components heating mixed melting, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3), after A, B material being mixed, melt extrude granulation on the twin screw extruder, to obtain final product.
Carried out performance test to material of the present invention, main condition are as follows:
Claims (1)
1. the polyvinyl chloride cable material for automobile, it is characterized in that, be made up of the raw material of following weight part: SG-4 polyvinyl chloride 30-34, trioctyl trimellitate 12-15, Flos Rosae Rugosae quintessence oil 0.2-0.3, Paris white 20-24, propionate 5-6, octyl epoxy stearate 5-7, anti-scorching agent CTP 1-2, vinyl three ('beta '-methoxy oxyethyl group) silane 3-4, polyisobutene 4-6, isocyanic ester 1-2, anti-aging agent OD1-2, auxiliary agent 6-8;
Described auxiliary agent is made up of the raw material of following weight part: diatomite 10-12, tri (propylene glycol) diacrylate 2-3, zinc oxide 5-6, jade powder 4-5,3-aminopropyl trimethoxysilane 2-3, linking agent TAC1-2, Zinc Gluconate 1-2, Zinic stearas 1-2, magnesium nitrate 7-9, Syzygium aromaticum stem oil 1-2, Flos Rosae Rugosae quintessence oil 0.1-0.2; Diatomite is sent in calcining furnace to calcine 3-4 hour at 700-730 DEG C by preparation method, take out, send in 10-15% hydrochloric acid and soak 1-2 hour, filter to obtain filter residue, wash with clear water, dry, be ground into 200-250 order powder, then the powder of drying is mixed with tri (propylene glycol) diacrylate, zinc oxide, linking agent TAC, grinding 1-2 hour, add other remaining component again, mixed grinding 1-2 hour, to obtain final product;
The described polyvinyl chloride cable material for automobile, be made up of following concrete steps:
(1) SG-4 polyvinyl chloride is heated to molten state, add trioctyl trimellitate, Flos Rosae Rugosae quintessence oil, Paris white, propionate, octyl epoxy stearate, anti-scorching agent CTP, auxiliary agent, stir and mediate 15-25 minute, send into twin screw extruder granulation, obtain A material;
(2) by all the other remaining components heating mixed melting, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3), after A, B material being mixed, melt extrude granulation on the twin screw extruder, to obtain final product.