CN103951340A - 一种低密度蒸压加气混凝土板专用修补砂浆 - Google Patents

一种低密度蒸压加气混凝土板专用修补砂浆 Download PDF

Info

Publication number
CN103951340A
CN103951340A CN201410145220.3A CN201410145220A CN103951340A CN 103951340 A CN103951340 A CN 103951340A CN 201410145220 A CN201410145220 A CN 201410145220A CN 103951340 A CN103951340 A CN 103951340A
Authority
CN
China
Prior art keywords
aerated concrete
autoclaved aerated
low density
special
concrete slab
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410145220.3A
Other languages
English (en)
Other versions
CN103951340B (zh
Inventor
刘佳锐
徐春利
刘锶锜
姚清华
张友菊
刘利娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN TIANZHU BUILDING MATERIALS Co Ltd
Original Assignee
TIANJIN TIANZHU BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN TIANZHU BUILDING MATERIALS Co Ltd filed Critical TIANJIN TIANZHU BUILDING MATERIALS Co Ltd
Priority to CN201410145220.3A priority Critical patent/CN103951340B/zh
Publication of CN103951340A publication Critical patent/CN103951340A/zh
Application granted granted Critical
Publication of CN103951340B publication Critical patent/CN103951340B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种低密度蒸压加气混凝土板专用修补砂浆，以白色硅酸盐水泥和砂为基料，配以填料和功能性掺合料，各组分的重量百分比为：白色硅酸盐水泥20～30wt%、砂40～60wt%、蒸压加气混凝土碎粉0～15wt%、重钙粉0～15wt%、可再分散胶粉0.1～2wt%、保水剂0.01～0.5wt%、纤维0.01～0.5wt%。本发明制备的修补砂浆易于施工及打磨、硬化后具有和蒸压加气混凝土相似的质感，强度等指标符合现有标准要求。

Description

一种低密度蒸压加气混凝土板专用修补砂浆
技术领域
本发明主要涉及一种蒸压加气混凝土专用修补砂浆，主要用于修补低密度蒸压加气混凝土板，属于建筑材料及施工技术领域。
背景技术
蒸压加气混凝土板是以水泥、石灰、硅砂等为主要原料，再根据结构要求配置添加不同数量经防腐处理的钢筋网片的一种轻质、多孔、新型的绿色环保建筑材料。目前，随着国内外对建筑节能要求的不断提高，蒸压加气混凝土板因其质轻，且具有良好的防火、隔音、隔热、保温等无与伦比的性能，已广泛应用于建筑外墙、内隔墙及屋面等。
然而，低密度蒸压加气混凝土板因其强度较低，在运输和施工过程中极易出现缺棱掉角、划痕、表面缺失等，严重影响产品的合格率和利用率。另外，施工过程中还需对产生的连接件、预埋件孔洞等材料破损处作填补处理等。现有的普通硅酸盐修补砂浆具有强度高和相容性好等优点，但存在施工性差、与蒸压加气混凝土板粘接强度低以及美观性差等问题。
发明内容
本发明的目的是提供一种低密度蒸压加气混凝土板专用修补砂浆，以解决普通硅酸盐水泥修补砂浆施工性差、与蒸压加气混凝土粘接强度低以及美观性差等问题。
为了实现上述目的，本发明采取的技术方案是：一种低密度蒸压加气混凝土板专用修补砂浆，以白色硅酸盐水泥和砂为基料，配以填料和功能性掺合料，各组分的重量百分比为：白色硅酸盐水泥20～30wt%、砂40～60wt%、蒸压加气混凝土碎粉0～15wt%、重钙粉0～15wt%、可再分散胶粉0.1～2wt%、保水剂0.01～0.5wt%、纤维0.01～0.5wt%。
所述砂为天然石英砂、白云石砂、天然河砂中的一种或几种，细度为20～140目。
所述的白色硅酸盐水泥需符合GB/T2015-2005标准。
所述的碎粉为蒸压加气混凝土产生的废弃物经粉碎后所得。
所述的重钙粉细度为200～400目。
所述的可再分散胶粉为乙烯/醋酸乙烯酯的共聚物、醋酸乙烯/叔碳酸乙烯共聚物、丙烯酸共聚物、聚乙烯醇共聚物中的一种或几种。
所述的保水剂为甲基纤维素醚、羟丙基甲基纤维素或羟乙基甲基纤维素醚中的一种，粘度在40000～200000mpa·s。
所述的纤维为聚丙烯纤维、聚酯纤维或木质纤维中的一种或两种。
本发明的优点是：
1.采用无机胶凝材料白色硅酸盐水泥和砂为主料，使得硬化后的修补砂浆具有与蒸压加气混凝土相似的外观，提高了美观性。
2.通过加入蒸压加气混凝土产生的废弃物-碎粉，有效节约了成本，同时达到了废物综合利用的目的。
3.通过加入一定量的高粘度保水剂和纤维，可降低修补砂浆的水分被蒸压加气混凝土吸附从而导致的开裂，增加两者间的粘结强度。
4.本发明适用范围广，主要用于修补低密度蒸压加气混凝土板，还可用于修补蒸压加气混凝土砌块和薄层修补等。
具体实施方式
以下结合具体实施方式对本发明作进一步说明，但本发明的保护范围不仅限于下述实施例的内容。
实施例1
按照下列重量份数称取原材料：
白色硅酸盐水泥（32.5）30份、石英砂（30-60目25份、40-70目15份、70-140目10份）50份、重钙粉（200目）15份、蒸压加气混凝土碎粉5份、可再分散胶粉1份、羟丙基甲基纤维素醚0.2份（粘度为40000mpa·s）、木质纤维0.2份。
上述修补砂浆主要用于蒸压加气混凝土板表面缺失、划痕等深度小于5mm的缺陷修补。
实施例2
按照下列重量份数称取原材料：
白色硅酸盐水泥（52.5）20份、石英砂（30-60目）30份、白云石砂（40-70目）15份、天然河砂（70-140目）15份、重钙粉（400目）10份、蒸压加气混凝土碎粉10份、可再分散胶粉1.5份、羟丙基甲基纤维素醚0.2份（粘度为100000mpa·s）、木质纤维0.1份、聚丙烯纤维0.1份。
上述修补砂浆主要用于蒸压加气混凝土缺棱掉角、连接件、预埋件孔洞等材料破损处的填补处理等深度大于5mm的缺陷修补。

Claims (8)

1.一种低密度蒸压加气混凝土板专用修补砂浆，以白色硅酸盐水泥和砂为基料，配以填料和功能性掺合料，其特征在于，各组分的重量百分比为：白色硅酸盐水泥20～30wt%、砂40～60wt%、蒸压加气混凝土碎粉0～15wt%、重钙粉0～15wt%、可再分散胶粉0.1～2wt%、保水剂0.01～0.5wt%、纤维0.01～0.5wt%。
2.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述砂为天然石英砂、天然河砂、白云石砂中的一种或几种，细度为20～140目。
3.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的白色硅酸盐水泥需符合GB/T2015-2005标准。
4.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的碎粉为蒸压加气混凝土产生的废弃物经粉碎后所得。
5.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的重钙粉细度为200～400目。
6.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的可再分散胶粉为乙烯/醋酸乙烯酯的共聚物、醋酸乙烯/叔碳酸乙烯共聚物、丙烯酸共聚物、聚乙烯醇共聚物中的一种或几种。
7.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的保水剂为甲基纤维素醚、羟丙基甲基纤维素或羟乙基甲基纤维素醚中的一种，粘度在40000～200000mpa·s。
8.根据权利要求1所述低密度蒸压加气混凝土板专用修补砂浆，其特征在于，所述的纤维为聚丙烯纤维、聚酯纤维或木质纤维中的一种或两种。
CN201410145220.3A 2014-04-11 2014-04-11 一种低密度蒸压加气混凝土板专用修补砂浆 Active CN103951340B (zh)