CN103937397B - A kind of dermatoglyph powder coating - Google Patents
A kind of dermatoglyph powder coating Download PDFInfo
- Publication number
- CN103937397B CN103937397B CN201410184435.6A CN201410184435A CN103937397B CN 103937397 B CN103937397 B CN 103937397B CN 201410184435 A CN201410184435 A CN 201410184435A CN 103937397 B CN103937397 B CN 103937397B
- Authority
- CN
- China
- Prior art keywords
- weight part
- dermatoglyph
- powder coating
- powder
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of dermatoglyph powder coating, be made up of end powder and sludge ice agent, the mass ratio of end powder and sludge ice agent is 100:0.1 ~ 1; Described its raw material of end powder consists of: urethane resin 40-50 weight part, 1174 solidifying agent 4-5 weight parts, pure polyester resin 8-10 weight part, TGIC solidifying agent 0.7-1.4 weight part, catalyzer 0.5-0.8 weight part, pigment 1-5 weight part, filler 25-45 weight part, dermatoglyph agent 0.8-1.5 weight part.The dermatoglyph powder coating good weatherability that the present invention obtains, has special texture appearance effect, and very excellent decorate properties.And the preparation method of this powder coating is simple, easy to use.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of dermatoglyph powder coating.
Background technology
Crimping powder coating title in the field of business is various, and other more popular title also has Wrinkle Texture Powder Coatings, water wave powdery paint, and such powder coating surface has special texture appearance effect, has very excellent decorate properties.Therefore crimping powder coating is widely used in the covering with paint of the indoor outer product applications such as five metals, furniture, electrical equipment, antitheft door.Crimping powder coating is divided into epoxy/Dyhard RU 100 type and hydroxy-terminated polyester/tetra-methoxy methyl glycoluril resin type two kinds of film forming matter types, is applied to the durable decorative articles of indoor decorative goods and open air respectively.Have a large amount of manufacture and development because the raw material developing epoxy/Dyhard RU 100 type crimping powder coating is domestic, the purchasing of raw materials is convenient and cheap, and therefore this type of powder coating is widely used and popularization once just releasing market at home.But, for hydroxy-terminated polyester/tetra-methoxy methyl glycoluril resin (TMMGU) type crimping powder coating, because necessary critical materials needs import before, and supplier cans be counted on one's fingers at home, Development Techniques monopolized by offshore company completely, selling price is jointly handled by foreign-made business and internal trade business and is controlled, cause cost of material very high, and selling price is in High High Level running for many years, has surmounted the acceptable compass of domestic powder coating and relevant consuming market completely always.Therefore, application market is almost without place at home for outdoor crimping powder coating, and the ground atrophy of city's field amplitude, can develop up till now and can be counted on one's fingers with the company of selling this series products.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, provide a kind of dermatoglyph powder coating, this dermatoglyph powder coating good weatherability, has special texture appearance effect, and very excellent decorate properties.And the preparation method of this powder coating is simple, easy to use.
For achieving the above object, the present invention adopts following technical scheme:
A kind of dermatoglyph powder coating, be made up of end powder and sludge ice agent, the mass ratio of end powder and sludge ice agent is 100:0.1 ~ 1; Described its raw material of end powder consists of: urethane resin 40-50 weight part, 1174 solidifying agent 4-5 weight parts, pure polyester resin 8-10 weight part, TGIC solidifying agent 0.7-1.4 weight part, catalyzer 0.5-0.8 weight part, pigment 1-5 weight part, filler 25-45 weight part, dermatoglyph agent 0.8-1.5 weight part.
Described catalyzer is that amine closes sulfonic acid catalyst.
Described catalyzer is 32-18A, purchased from French Bao Shi chemical company.
Described filler is barite.
The method preparing dermatoglyph powder coating as above is specially: weigh each raw material by formula, drops in stirrer and carries out sufficient pre-mixing, through forcing machine extruding in flakes, sieves finally by the classification of pulverizing mill 100 ~ 200 order, powder of the obtained end; Then in end powder, add sludge ice agent, stir, obtained dermatoglyph powder coating.
Beneficial effect of the present invention is:
The dermatoglyph powder coating good weatherability that the present invention obtains, has special texture appearance effect, and very excellent decorate properties.And the preparation method of this powder coating is simple, easy to use.
Embodiment
The present invention's the following example further illustrates the present invention, but protection scope of the present invention is not limited to the following example.
embodiment 1
By urethane resin 40 weight part, 1174 solidifying agent 4 weight parts, pure polyester resin 10 weight part, TGIC solidifying agent 1.0 weight part, catalyzer 0.6 weight part, pigment 3 weight part, filler 25 weight part, dermatoglyph agent 0.8 weight part, drop in stirrer and carry out sufficient pre-mixing, through forcing machine extruding in flakes, sieve finally by the classification of pulverizing mill 100 order, powder of the obtained end; Then be that 100:0.1 adds sludge ice agent by end powder and sludge ice agent mass ratio, stir, obtained dermatoglyph powder coating.
By this dermatoglyph powder paint on door, after baking-curing, good weatherability, texture appearance is effective.
embodiment 2
By urethane resin 45 weight part, 1174 solidifying agent 5 weight parts, pure polyester resin 8 weight part, TGIC solidifying agent 0.7 weight part, catalyzer 0.5 weight part, pigment 5 weight part, filler 35 weight part, dermatoglyph agent 1.2 weight part, drop in stirrer and carry out sufficient pre-mixing, through forcing machine extruding in flakes, sieve finally by the classification of pulverizing mill 200 order, powder of the obtained end; Then be that 100:0.5 adds sludge ice agent by end powder and sludge ice agent mass ratio, stir, obtained dermatoglyph powder coating;
By this dermatoglyph powder paint on door, after baking-curing, good weatherability, texture appearance is effective.
embodiment 3
By urethane resin 50 weight part, 1174 solidifying agent 4 weight parts, pure polyester resin 9 weight part, TGIC solidifying agent 1.4 weight part, catalyzer 0.8 weight part, pigment 1 weight part, filler 45 weight part, dermatoglyph agent 1.5 weight part, drop in stirrer and carry out sufficient pre-mixing, through forcing machine extruding in flakes, sieve finally by the classification of pulverizing mill 200 order, powder of the obtained end; Then be that 100:1 adds sludge ice agent by end powder and sludge ice agent mass ratio, stir, obtained dermatoglyph powder coating;
By this dermatoglyph powder paint on door, after baking-curing, good weatherability, texture appearance is effective.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (4)
1. a dermatoglyph powder coating, is characterized in that: be made up of end powder and sludge ice agent, and the mass ratio of end powder and sludge ice agent is 100:0.1 ~ 1; Described its raw material of end powder consists of: urethane resin 40-50 weight part, 1174 solidifying agent 4-5 weight parts, pure polyester resin 8-10 weight part, TGIC solidifying agent 0.7-1.4 weight part, catalyzer 0.5-0.8 weight part, pigment 1-5 weight part, filler 25-45 weight part, dermatoglyph agent 0.8-1.5 weight part.
2. a kind of dermatoglyph powder coating according to claim 1, is characterized in that: described catalyzer is that amine closes sulfonic acid catalyst.
3. a kind of dermatoglyph powder coating according to claim 2, is characterized in that: described catalyzer is 32-18A.
4. a kind of dermatoglyph powder coating according to claim 1, is characterized in that: described filler is barite.