CN103936332A - Mineral paint - Google Patents
Mineral paint Download PDFInfo
- Publication number
- CN103936332A CN103936332A CN201410112930.6A CN201410112930A CN103936332A CN 103936332 A CN103936332 A CN 103936332A CN 201410112930 A CN201410112930 A CN 201410112930A CN 103936332 A CN103936332 A CN 103936332A
- Authority
- CN
- China
- Prior art keywords
- parts
- mineral
- paint
- kaolin
- mineral coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mineral paint. The mineral paint comprises the following components in parts by weight: 10 to 12 parts of wollastonite, 8 to 10 parts of kaolin, 5 to 10 parts of magnet, 0.2 to 0.3 part of sodium polyacrylate, 3 to 5 parts of styrene-acrylic emulsion, 1 to 5 parts of active diluent, 0.1 to 0.3 part of nano silver antiseptic, 0.5 to 1 part of epoxy acrylate, and 20 to 30 parts of water. The mineral paint has the advantages that: the paint is made of mineral raw materials, is capable of absorbing indoor formaldehyde and refreshing the indoor air, has a low thermal conductivity, a good flame retardant effect, and stable properties, and can satisfy people's needs.
Description
Technical field
The present invention relates to a kind of coating, relate in particular to a kind of mineral coating.
Background technology
The coating material of the industries such as turning of current domestic construction, old city made, iron skill, boats and ships, petroleum pipeline network more than 95% all adopts organic coating, its starting material are mainly derived from oil, coal, Sweet natural gas and extract, their production has consumed a large amount of energy, and discharging a large amount of VOC gas, severe contamination environment.Since people bring into use organic coating, the development of coatings industry can be described as advances by leaps and bounds, and earth-shaking variation has occurred along with improving constantly of human sciences's technology for its production technology, state of the art.Because the main raw material(s) of organic coating is mainly got natural resourcess such as coming from coal, oil, Sweet natural gas, add and can produce a large amount of by products and volatile gases and residual body man-hour, i.e. serious environment pollution, has wasted again a large amount of energy and resource.Meanwhile, static resistance, the resistance to crocking of organic coating are poor, and film does not have again ventilation property.
Therefore,, for addressing the above problem, spy provides a kind of new technical scheme to satisfy the demands.
Summary of the invention
The invention provides a kind of mineral coating.
The technical solution used in the present invention is:
A kind of mineral coating, comprises the composition of following weight part:
Wollastonite 10-12 part;
Kaolin 8-10 part;
Magnetite 5-10 part;
Sodium polyacrylate 0.2-0.3 part;
Benzene emulsion 3-5 part;
Reactive thinner 1-5 part;
Nano silver antimicrobials 0.1-0.3 part;
Epoxy acrylate 0.5-1 part;
Water 20-30 part.
Described reactive thinner is Viscoat 295 and tripropylene glycol diacrylate.
The weight ratio of described Viscoat 295 and tripropylene glycol diacrylate is 1:1.
The invention has the beneficial effects as follows: adopt mineral raw material, the formaldehyde in can absorption chamber, makes indoor air become fresh and clean, and heat conduction efficiency is low, good flame retardation effect, stable performance, meets people's demand.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only, for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1
A kind of mineral coating, comprises the composition of following weight part:
10 parts of wollastonites;
8 parts of kaolin;
5 parts of magnetites;
0.2 part of sodium polyacrylate;
3 parts of benzene emulsions;
0.5 part of Viscoat 295
0.5 part of tripropylene glycol diacrylate;
0.1 part of nano silver antimicrobials;
0.5 part of epoxy acrylate;
20 parts, water.
Embodiment 2
A kind of mineral coating, comprises the composition of following weight part:
12 parts of wollastonites;
9 parts of kaolin;
7 parts of magnetites;
0.25 part of sodium polyacrylate;
4 parts of benzene emulsions;
1.5 parts of Viscoat 295s
1.5 parts of tripropylene glycol diacrylates;
0.2 part of nano silver antimicrobials;
0.7 part of epoxy acrylate;
25 parts, water.
Embodiment 3
A kind of mineral coating, comprises the composition of following weight part:
12 parts of wollastonites;
10 parts of kaolin;
10 parts of magnetites;
0.3 part of sodium polyacrylate;
5 parts of benzene emulsions;
2.5 parts of Viscoat 295s
2.5 parts of tripropylene glycol diacrylates;
0.3 part of nano silver antimicrobials;
1 part of epoxy acrylate;
30 parts, water.
The invention has the beneficial effects as follows: adopt mineral raw material, the formaldehyde in can absorption chamber, makes indoor air become fresh and clean, and heat conduction efficiency is low, good flame retardation effect, stable performance, meets people's demand.
The above, be only preferred embodiment of the present invention, is not the restriction of the present invention being made to any other form, and according to any amendment or equivalent variations that technical spirit of the present invention is done, still belong to the present invention's scope required for protection.
Claims (3)
1. a mineral coating, is characterized in that: the composition that comprises following weight part:
Wollastonite 10-12 part;
Kaolin 8-10 part;
Magnetite 5-10 part;
Sodium polyacrylate 0.2-0.3 part;
Benzene emulsion 3-5 part;
Reactive thinner 1-5 part;
Nano silver antimicrobials 0.1-0.3 part;
Epoxy acrylate 0.5-1 part;
Water 20-30 part.
2. a kind of mineral coating according to claim 1, is characterized in that: described reactive thinner is Viscoat 295 and tripropylene glycol diacrylate.
3. a kind of mineral coating according to claim 2, is characterized in that: the weight ratio of described Viscoat 295 and tripropylene glycol diacrylate is 1:1.