CN109439025A - A kind of black limed rosin enamel-interior - Google Patents
A kind of black limed rosin enamel-interior Download PDFInfo
- Publication number
- CN109439025A CN109439025A CN201710755279.8A CN201710755279A CN109439025A CN 109439025 A CN109439025 A CN 109439025A CN 201710755279 A CN201710755279 A CN 201710755279A CN 109439025 A CN109439025 A CN 109439025A
- Authority
- CN
- China
- Prior art keywords
- parts
- black
- enamel
- interior
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of black limed rosin enamel-interiors, belong to technical field of coatings, the raw material including following parts by weight: 10~40 parts of carbon black, 25~55 parts of precipitated calcium carbonate, 10~20 parts of blanc fixe, 2~3 parts of titanium dioxide and 1~3 part of vinyl unsaturated carboxylic acid.A kind of black limed rosin enamel-interior of the invention, using carbon black as film forming matter, and using vitreum earth silicon material, special ceramic materials, vinyl unsaturated carboxylic acid, fibrous material as filler, insulation antiseptic anticorrosive paint is made, a kind of waterproof heat insulation coating is made using raw materials such as elastic emulsion, hollow glass micropearl, diatomite, infrared reflection agent, asbestos wools, the coating, which only coats 2mm thickness, can reach good waterproof thermal-insulated effect, it can also be used to make the top finishing of interior metal and wooden object.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of black limed rosin enamel-interior.
Background technique
The performance of acrylic rubber is influenced by atomic number of alkyl carbon purpose in its principal monomer alkyl acrylate.With third
Rubber based on olefin(e) acid ester, oil resistant, heat resistance are preferable；And the rubber based on butyl acrylate, because of atomic number of alkyl carbon
Purpose increases, and increases the screen effect of ester group polar group, therefore water resistance is made to make moderate progress, simultaneously because screen effect, subtracts
Power between weak rubber molecule, increases internal plasticity, so that brittleness temperature be made to reduce, cold resistance is preferable.If by above two
Monomer is used in combination, then the rubber between the two performance can be obtained.
Anticorrosive paint is generally divided into conventional anticorrosive paint and anticorrosive paint, is essential one kind in paint
Coating.Conventional anticorrosive paint is under general condition, to play the role of the longevity etch-proof, protection non-ferrous metal uses to metal etc.
Life；It for anticorrosive paint refers to relatively conventional anticorrosive paint, can be applied in relatively harsh corrosive environment, and have and can reach
A kind of anticorrosive paint of protection period longer than conventional anticorrosive paint.
Nowadays anticorrosive paint has become the important fresh combatants of paint field, and anticorrosive paint plays increasing work
With development prospect is considerable.But traditional product gradually improves perfect, new product and constantly researches and develops appearance, Yao Shiying anticorrosion market and
New standard and requirement in environmental regulation development, it is still necessary to proactive, Continuous Innovation.
No matter the acrylic rubber of which seed type, there are two the common features of molecular structure: first is that highly polar；Two
It is fully saturated property.To make it have superior resistance to mineral oil and pyro-oxidation resistance.Its oil resistivity is only second to fluorine glue, and
To it is general in the nitrile rubber of high acrylonitrile content it is similar.And heat resistance compares butyronitrile between general purpose rubber and silicon, fluorubber
Rubber is higher by 30~60 DEG C using temperature, 180 DEG C of maximum operation (service) temperature, discontinuously uses with the short time up to 200 DEG C, at 150 DEG C
The hot air aging several years, performance was without significant change.Furthermore, it is most important that it is to the extreme pressure type containing extreme pressure agents such as sulphur, chlorine, phosphorus
Lubricating oil is sufficiently stable, and using temperature up to 150 DEG C, interruption can be higher using temperature.And the nitrile rubber with double bond exists
In oil containing extreme pressure agent, when temperature is more than 110 DEG C, that is, significant hardening occurs and becomes fragile.Acrylic rubber also has excellent
Good ozone resistants, air-tightness, resistance to flexion and resistance to breach growth property and uvioresistant discolouration etc..
Summary of the invention
Goal of the invention: the purpose of the present invention is to provide a kind of black limed rosin enamel-interiors.
Technical solution: for achieving the above object, the present invention adopts the following technical scheme:
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 10~40 parts of carbon black, precipitated calcium carbonate 25
~55 parts, 10~20 parts of blanc fixe, 2~3 parts of titanium dioxide and 1~3 part of vinyl unsaturated carboxylic acid.
The raw material further includes the improved silica that parts by weight are 5~10 parts.
The raw material further includes the kaolin that parts by weight are 2~3 parts.
The raw material further includes the silica for the vitreum that parts by weight are 5~10 parts.
The raw material further includes the calcium carbonate that parts by weight are 5~10 parts.
The utility model has the advantages that compared with prior art, a kind of black limed rosin enamel-interior of the invention, using carbon black as film forming matter
Matter, and using vitreum earth silicon material, special ceramic materials, vinyl unsaturated carboxylic acid, fibrous material as filler, guarantor is made
Warm anti-corrosion anticorrosive paint is made using raw materials such as elastic emulsion, hollow glass micropearl, diatomite, infrared reflection agent, asbestos wools
A kind of waterproof heat insulation coating, which, which only coats 2mm thickness, can reach good waterproof thermal-insulated effect.
Specific embodiment
The present invention is described further With reference to embodiment.
Embodiment 1
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 10 parts of carbon black, 25 parts of precipitated calcium carbonate,
10 parts of blanc fixe, 2 parts of titanium dioxide and 1 part of vinyl unsaturated carboxylic acid.
Raw material further includes the titanium dioxide that parts by weight are 5 parts of improved silica, 2 parts of kaolin, 5 parts of vitreum
Silicon.
Embodiment 2
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 40 parts of carbon black, 55 parts of precipitated calcium carbonate,
20 parts of blanc fixe, 3 parts of titanium dioxide and 3 parts of vinyl unsaturated carboxylic acid.
Raw material further includes the dioxy that parts by weight are 10 parts of improved silica, 3 parts of kaolin, 10 parts of vitreum
SiClx.
Embodiment 3
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 15 parts of carbon black, 30 parts of precipitated calcium carbonate,
12 parts of blanc fixe, 2.2 parts of titanium dioxide and 1.5 parts of vinyl unsaturated carboxylic acid.
Raw material further includes the dioxy that parts by weight are 6 parts of improved silica, 2.5 parts of kaolin, 7 parts of vitreum
SiClx.
Embodiment 4
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 30 parts of carbon black, 25 parts of precipitated calcium carbonate,
20 parts of blanc fixe, 3 parts of titanium dioxide and 1 part of vinyl unsaturated carboxylic acid.
Raw material further includes the dioxy that parts by weight are 10 parts of improved silica, 3 parts of kaolin, 8 parts of vitreum
SiClx.
Embodiment 5
A kind of black limed rosin enamel-interior, the raw material including following parts by weight: 40 parts of carbon black, 55 parts of precipitated calcium carbonate,
20 parts of blanc fixe, 3 parts of titanium dioxide and 1 part of vinyl unsaturated carboxylic acid.
Raw material further includes the dioxy that parts by weight are 10 parts of improved silica, 3 parts of kaolin, 8 parts of vitreum
SiClx.
To sum up:
Disadvantage
Poor processability, the easy roll banding of sizing material, flow velocity is slow, and cold resistance is poor, not resistant to water, vapor, soda acid, salting liquid and has
Machine polar solvent, poor flexibility at room temperature wear no resistance, poor electrical performance.
It is 180 DEG C of manufacture since acrylic rubber is only second to fluorubber in terms of heat-resisting and oil resistant comprehensive performance
Rubber oil sea, O-ring, gasket and the sebific duct used under high temperature uses material.Again because of its stabilization to high temperature extreme pressure lublicating oil
Property, therefore had comparative advantage in the world with making all kinds of automobile sealed accessories.Additionally using the excellent spy of acrylic rubber
Property manufacture adhesive tape, container lining, deep prospecting rubber product, sponge oil resistant gasket and oil resistant asbestos-rubber product
Deng.Acrylic rubber is also applied in the hard-core technologies such as aviation, rocket, guided missile department.As being used to prepare solid fuel
Adhesive etc..
Effect
Since the solubility parameter of polyacrylate and the solubility parameter of uncured epoxy resin are not much different, the two has
Good intersolubility.Again because polyacrylate backbone is free of double bond, it has good thermal oxidation resistance effect.
The determinant of acrylic liquid rubber flexibilizing epoxy has: whether rubber phase forms, the composition and bullet of rubber phase
Property, the size distribution of rubber phase particles, the chemical bonding and epoxy resin-base molecule knot of rubber phase and epoxy resin-base
The epoxy-functional concentration etc. of l in structure and its molecule.Wherein principal element is the Phase stracture of solidified resin system, rubber phase
With the chemical bonding of epoxy matrix and the ductility of epoxy-resin systems itself, acrylic liquid rubber flexibilizing epoxy system |
Phase structure to be mainly rubber phase be dispersed in epoxy matrix with the spherical particle of rule, dispersed phase by differ in size two
Kind spheroidal particle composition.
The two poles of the earth distribution of particle size is beneficial to toughening.Small particle mainly works to shear-deformable, big
Grain can prevent the growth of crackle.In this way, it is to Toughening Epoxy Resin, the good results are evident.
Claims (5)
1. a kind of black limed rosin enamel-interior, it is characterised in that: the raw material including following parts by weight: 10~40 parts of carbon black, light
25~55 parts of matter calcium carbonate, 10~20 parts of blanc fixe, 2~3 parts of titanium dioxide and 1~3 part of vinyl unsaturated carboxylic acid.
2. a kind of black limed rosin enamel-interior according to claim 1, it is characterised in that: the raw material further includes weight
The improved silica that number is 5~10 parts.
3. a kind of black limed rosin enamel-interior according to claim 1, it is characterised in that: the raw material further includes weight
The kaolin that number is 2~3 parts.
4. a kind of black limed rosin enamel-interior according to claim 1, it is characterised in that: the raw material further includes weight
The silica for the vitreum that number is 5~10 parts.
5. a kind of black limed rosin enamel-interior according to claim 1, it is characterised in that: the raw material further includes weight
The calcium carbonate that number is 5~10 parts.