CN104263166A - Novel sealing plate coating - Google Patents
Novel sealing plate coating Download PDFInfo
- Publication number
- CN104263166A CN104263166A CN201410327523.7A CN201410327523A CN104263166A CN 104263166 A CN104263166 A CN 104263166A CN 201410327523 A CN201410327523 A CN 201410327523A CN 104263166 A CN104263166 A CN 104263166A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- sealing plate
- hardening
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel sealing plate coating. The coating material is composed of the following components by weight: 150-200 parts of silicone-acrylic emulsion, 6-8 parts of mica powder, 90-100 parts of elastic emulsion, 80-90 parts of silicone-acrylic emulsion, 4-8 parts of a hardening agent, 2-5 parts of a moistening agent, 4-6 parts of a dispersing agent, 2-6 parts of a defoaming agent, 1.5-3.5 parts of a corrosion-resistant agent, 10-20 parts of limestone, 25-30 parts of methanol, 40-45 parts of graphite powder and 100-200 parts of water. The above moistening agent is PE100; an activating agent is Hydropalat3204; the dispersing agent is Hydropalat100; the defoaming agent is BYK-093; the hardening agent is nano silica; and the corrosion-resistant agent is sodium nitrite. The coating comprises the corrosion-resistant agent, the hardening agent and the elastic emulsion, so that the sealing plate has excellent corrosion resistance, warm stability, high temperature resistance and wear resistance.
Description
Technical field
The present invention relates to a kind of novel seal plate coating.
Background technology
Sealing plate is again combine between the higher and lower levels version and rubber wear-resisting plate, is widely used in the tightness system of anti-pollution etch-proof junction in the industrial equipmentss such as chemical fibre, pharmacy, papermaking, machinofacture.But sealing plate exposes in atmosphere for a long time, be easy to the erosion being subject to external environment, thus affect sealing plate stopping property.
Summary of the invention
A kind of stability is the invention provides high, high temperature resistant, anticorrosion, wear-resisting sealing plate in order to solve the problem.
Technical scheme of the present invention is:
The invention discloses a kind of sealing plate coating, described coated material, be made up of the composition of following parts by weight:
Organosilicon crylic acid latex 150-200 part,
Mica powder 6-8 part,
Elastic emulsion 90-100 part,
Organosilicon crylic acid latex 80-90 part,
Hardening agent 4-8 part,
Wetting agent 2-5 part,
Dispersion agent 4-6 part,
Defoamer 2-6 part,
Sanitas 1.5-3.5 part,
Wingdale 10-20 part,
Methyl alcohol 25-30 part,
Graphite Powder 99 40-45 part,
Water 100-200 part.
Above-mentioned wetting agent is PE100, and promoting agent is Hydropalat3204, and dispersion agent is Hydropalat100, and defoamer is BYK-093, and Hardening agent is nano silicon, and sanitas is Sodium Nitrite.
Beneficial effect:
There is sanitas in described coated component, Hardening agent, elastic emulsion, make sealing plate have superior preservative property, warm stability, high temperature resistant, wear resistance.
Embodiment
The invention will be further described below.
Embodiment 1
A kind of sealing plate coating, described coated material, is made up of the composition of following parts by weight:
Organosilicon crylic acid latex 170 parts, mica powder 7 parts, elastic emulsion 95 parts, organosilicon crylic acid latex 85 parts of Hardening agent 6 parts, wetting agent 4 parts, dispersion agent 5 parts, defoamer 4 parts, sanitas 2.5 parts, 15 parts, Wingdale, methyl alcohol 27 parts, Graphite Powder 99 43 parts, 165 parts, water.
Above-mentioned wetting agent is PE100, and promoting agent is Hydropalat3204, and dispersion agent is Hydropalat100, and defoamer is BYK-093, and Hardening agent is nano silicon, and sanitas is Sodium Nitrite.
Above-mentioned solvent and solute are mixed with water, stir 10 minutes, reheat 40 minutes, cool 1 hour, finally by coating uniform application at sealing plate outside surface, dry, test sealing plate preservative property, stability, high temperature resistant, wear resistance, test result is as table 1.
A kind of sealing plate of the present invention, comprise sealing plate body, described sealing plate surface is provided with coating, has sanitas in described coated component, Hardening agent, elastic emulsion, makes sealing plate have superior preservative property, stability, high temperature resistant, wear resistance.
Embodiment 2
A kind of sealing plate coating, described coated material, is made up of the composition of following parts by weight:
Organosilicon crylic acid latex 175 parts, mica powder 6 parts, elastic emulsion 98 parts, organosilicon crylic acid latex 86 parts, Hardening agent, 7 parts, wetting agent 3 parts, dispersion agent 5 parts, defoamer 5 parts, sanitas 1.5 parts, 16 parts, Wingdale, methyl alcohol 28 parts, Graphite Powder 99 43 parts, 170 parts, water.
Above-mentioned wetting agent is PE100, and promoting agent is Hydropalat3204, and dispersion agent is Hydropalat100, and defoamer is BYK-093, and Hardening agent is nano silicon, and sanitas is Sodium Nitrite.
Above-mentioned solvent and solute are mixed with water, stir 10 minutes, reheat 40 minutes, cool 1 hour, finally by coating uniform application at sealing plate outside surface, dry, test sealing plate preservative property, stability, high temperature resistant, wear resistance, test result is as table 1.
A kind of sealing plate of the present invention, comprise sealing plate body, described sealing plate surface is provided with coating, has sanitas in described coated component, Hardening agent, elastic emulsion, makes sealing plate have superior preservative property, stability, high temperature resistant, wear resistance.
Table 1 test result of the present invention.
| ? | High thermal resistance | Wear resistance | Preservative property | Stability |
| Conventional seals plate | Difference | Generally | Generally | Generally |
| Embodiment 1 | Good | Good | Good | Better |
| Embodiment 2 | Better | Better | Better | Good |
Here description of the invention and application is illustrative, not wants by scope restriction of the present invention in the above-described embodiments, and therefore, the present invention is not by the restriction of the present embodiment, and the technical scheme that any employing equivalence replacement obtains is all in the scope of protection of the invention.
Claims (2)
1. the invention discloses a kind of sealing plate coating, described coated material, be made up of the composition of following parts by weight:
Organosilicon crylic acid latex 150-200 part,
Mica powder 6-8 part,
Elastic emulsion 90-100 part,
Organosilicon crylic acid latex 80-90 part,
Hardening agent 4-8 part,
Wetting agent 2-5 part,
Dispersion agent 4-6 part,
Defoamer 2-6 part,
Sanitas 1.5-3.5 part,
Wingdale 10-20 part,
Methyl alcohol 25-30 part,
Graphite Powder 99 40-45 part,
Water 100-200 part.
2. a kind of sealing plate as claimed in claim 1, it is characterized in that above-mentioned wetting agent is PE100, promoting agent is Hydropalat3204, and dispersion agent is Hydropalat100, and defoamer is BYK-093, and Hardening agent is nano silicon, and sanitas is Sodium Nitrite.