CN103923365B - 一种橡胶填充剂及包含它的橡胶 - Google Patents
一种橡胶填充剂及包含它的橡胶 Download PDFInfo
- Publication number
- CN103923365B CN103923365B CN201410102888.XA CN201410102888A CN103923365B CN 103923365 B CN103923365 B CN 103923365B CN 201410102888 A CN201410102888 A CN 201410102888A CN 103923365 B CN103923365 B CN 103923365B
- Authority
- CN
- China
- Prior art keywords
- rubber
- plant ash
- agent
- filler
- promotor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种橡胶填充剂及包含它的橡胶。橡胶填充剂,包括草木灰。包含上述橡胶填充剂的橡胶,其原料组分包括:天然橡胶100份,胎面再生胶850-950份,硫化剂14-18份,活性剂15-25份,促进剂2-6份,防老剂1-3份,炭黑70-90份,机油30-50份,草木灰100-700份,所述份数为质量份数。本发明以草木灰或改性草木灰作为橡胶填充剂,不仅降低了橡胶的密度,提高了橡胶的力学性能,且变废为宝,大幅度减少了环境污染。
Description
技术领域
本发明涉及一种橡胶填充剂及包含它的橡胶。
背景技术
草木灰包括常见的麦秆灰、稻草灰、高粱杆灰及其他杂草灰等,其主要成分为碳酸钾、二氧化硅等。以往每年收获季节后麦秆和稻草可以作为燃料应用于烧火做饭,随着生产力水平的发展、生活水平的提高和不断改善,麦秆、稻草、高粱杆收割后随意在农田焚烧,所产生的烟雾严重影响了空气质量,剩余草木灰也因质地轻而随风四处飞舞,严重污染了空气,对雾霾的产生有严重的主因。随着我国相继出台禁烧法令并配套建立专门的生物、植物焚烧站,草木灰就成为了一种广泛易得的原材料。众所周知橡胶中最廉价的填充材料为重质碳酸钙,此材料只能填充并无补强效果,由于自身密度较大,补充橡胶后对橡胶的密度影响很大,造成橡胶的密度较大,比重较大,性能较差的缺陷。
发明内容
本发明的目的是提供一种橡胶填充剂及包含它的橡胶。
为解决上述技术问题,本发明的技术方案是:
一种橡胶填充剂,包括草木灰。
申请人经研究意外发现,将草木灰作为填充剂填充在橡胶中,橡胶的密度明显减少,产品力学性能明显提高,而且产品的性能质量稳定。
为了降低生产成本、同时保证所得产品的性能,草木灰的质量用量为天然橡胶质量的1-7倍。
上述橡胶填充剂还包括机油,机油的质量用量为天然橡胶质量的0.3-0.5倍。这样可进一步保证产品的均匀性和力学性能。
为了进一步提高橡胶的力学性能,所述草木灰为改性草木灰,改性草木灰的制备为:将草木灰80-90份、液体丁苯橡胶10-20份和硅烷偶联剂1-3份在常温常压下混合均匀并造3-5目的粒子即得,所述份数为质量份数。
包含上述橡胶填充剂的橡胶,其原料组分包括:天然橡胶100份,胎面再生胶850-950份,硫化剂14-18份,活性剂15-25份,促进剂2-6份,防老剂1-3份,炭黑70-90份,机油30-50份,草木灰100-700份,所述份数为质量份数。
为了进一步提高所得橡胶的力学性能,橡胶的原料组分还包括:轻质碳酸钙150-450份。
优选,硫化剂为硫磺;活性剂包括质量比为(4-5):1的氧化锌和硬脂酸;促进剂为2、2'-二硫代二苯并噻唑和2-硫醇基苯并噻唑中一种两种以上任意配比的混合物;防老剂为2,2,4-三甲基-1,2-二氢化喹啉。
更优选,促进剂为质量比为1:1的2、2'-二硫代二苯并噻唑和2-硫醇基苯并噻唑的混合物。
申请人经研究发现:上述各助剂之间产生了意想不到的协同效应,用上述配方所制备的橡胶不仅质轻,而且力学性能有了较大的提升。
橡胶的制备工艺参照现有技术。
本发明未特别说明的技术均为现有技术。
本发明以草木灰或改性草木灰作为橡胶填充剂,不仅降低了橡胶的密度,提高了橡胶的力学性能,且变废为宝,大幅度减少了环境污染。
具体实施方式
为了更好地理解本发明,下面结合实施例进一步阐明本发明的内容,但本发明的内容不仅仅局限于下面的实施例。
表1中列出了实施例的原料配比表,橡胶的制备参照现有成熟工艺(公告号为CN101537668B的授权专利)。表2列出了各实施例所得产品的性能。
实施例中所用草木灰为:由玉米杆焚烧而得。
所用的改性草木灰为:取上述草木灰用100目的振动筛过筛,按草木灰85份、液体丁苯橡胶(型号1712,厂家,齐鲁石化)15份和硅烷偶联剂(KH550)2份在常温常压的高速搅拌机内搅拌均匀,再通过造粒机造成目数为3-5目的粒子,这样在橡胶混炼时不易飞扬,同时便于在橡胶中均匀分散。
表1各实施例所用原料配比表
表2各实施例所得橡胶的性能表
性能指标 | 硬度 | 扯断伸长率 | 扯断强度 | 密度 |
单位 | 邵氏A度 | % | Mpa | g/cm3 |
参照标准 | GB/T531-1999 | GB/T528-1998 | GB/T528-1998 | GB4472-84 |
对比例1 | 70 | 270 | 5.4 | 1.52 |
实施例1 | 73 | 310 | 6.1 | 1.37 |
实施例2 | 75 | 312 | 6.5 | 1.35 |
实施例3 | 78 | 315 | 6.8 | 1.30 |
实施例4 | 72 | 320 | 7.5 | 1.35 |
实施例5 | 75 | 340 | 8.5 | 1.30 |
实施例6 | 77 | 380 | 10 | 1.25 |
Claims (7)
1.一种橡胶填充剂,其特征在于:包括草木灰,所述草木灰为改性草木灰,改性草木灰的制备为:将草木灰80-90份、液体丁苯橡胶10-20份和硅烷偶联剂1-3份在常温常压下混合均匀、并造3-5目的粒子即得,所述份数为质量份数。
2.包含权利要求1所述的橡胶填充剂的橡胶,其特征在于:其原料组分包括:天然橡胶100份,胎面再生胶850-950份,硫化剂14-18份,活性剂15-25份,促进剂2-6份,防老剂1-3份,炭黑70-90份,机油30-50份,改性草木灰100-700份,所述份数为质量份数。
3.如权利要求2所述的橡胶,其特征在于:其原料组分还包括:轻质碳酸钙150-450份。
4.如权利要求2或3所述的橡胶,其特征在于:硫化剂为硫磺;活性剂包括质量比为(4-5):1的氧化锌和硬脂酸。
5.如权利要求2或3所述的橡胶,其特征在于:促进剂为2、2'-二硫代二苯并噻唑和2-硫醇基苯并噻唑中一种两种以上任意配比的混合物。
6.如权利要求5所述的橡胶,其特征在于:促进剂为质量比为1:1的2、2'-二硫代二苯并噻唑和2-硫醇基苯并噻唑的混合物。
7.如权利要求2或3所述的橡胶,其特征在于:防老剂为2,2,4-三甲基-1,2-二氢化喹啉。