CN103922593A - Dark red color crystal pearl blank and preparation method thereof - Google Patents
Dark red color crystal pearl blank and preparation method thereof Download PDFInfo
- Publication number
- CN103922593A CN103922593A CN201410103969.1A CN201410103969A CN103922593A CN 103922593 A CN103922593 A CN 103922593A CN 201410103969 A CN201410103969 A CN 201410103969A CN 103922593 A CN103922593 A CN 103922593A
- Authority
- CN
- China
- Prior art keywords
- parts
- dark red
- red color
- color crystal
- bead blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a dark red color crystal pearl blank and a preparation method thereof. The dark red color crystal pearl blank comprises, by weight, 80-190 parts of quartz sand, 10-30 parts of zinc oxide, 20-75 parts of soda ash, 10-35 parts of potassium carbonate, 7-23 parts of boric acid, 2-8 parts of calcium carbonate, 0.5-3 parts of aluminum hydroxide, 1-4 parts of gravy salt, 0.3-3 parts of cadmium yellow, 0.5-2.5 parts of selenium powder, and 0.5-6 parts of cadmium red. According to the present invention, during dark red color crystal pearl blank preparing, oxidation reduction balance of copper ions during a melting process maintains a stable state so as to obtain good colorability; and the lead-containing raw material is not used, and advantages of good gloss, bright and uniform color, no color difference, no pattern, high yield, no lead, no pollution and good production benefit are provided.
Description
Technical field
The present invention relates to a kind of dark red color crystal bead blank and preparation method thereof.
Background technology
Dark red color crystal bead blank is the work in-process for preparing dark red color crystal product, existing dark red color crystal bead blank process using crucible is manufactured, exist aberration, color is uneven, there is decorative pattern, unstable product quality, production efficiency is low, be not suitable for continuous production in enormous quantities, and burn and cause environmental pollution with coal.
Summary of the invention
It is good that technical problem to be solved by this invention is to provide a kind of color reproduction, solid colour no color differnece, without decorative pattern, and constant product quality, production efficiency is high, can be applicable to the dark red color crystal bead blank of the production operation of continuous tank furnace.
For addressing the above problem, the present invention is achieved through the following technical solutions: a kind of dark red color crystal bead blank, this dark red color crystal bead blank is made up of following weight part proportioning composition: quartz sand 80-190 part, zinc oxide 10-30 part, soda ash 20-75 part, salt of wormwood 10-35 part, boric acid 7-23 part, calcium carbonate 2-8 part, aluminium hydroxide 0.5-3 part, salt 1-4 part, cadmium yellow 0.3-3 part, selenium powder 0.5-2.5 part and cadmium red 0.5-6 part.
Another technical problem to be solved by this invention is to provide a kind of preparation method of dark red color crystal bead blank,
The present invention is achieved through the following technical solutions: the preparation process of described dark red color crystal bead blank is as follows:
1) extracting by weight ratio quartz sand 80-190 part, zinc oxide 10-30 part, soda ash 20-75 part, salt of wormwood 10-35 part, boric acid 7-23 part, calcium carbonate 2-8 part, aluminium hydroxide 0.5-3 part, salt 1-4 part, cadmium yellow 0.3-3 part, selenium powder 0.5-2.5 part and cadmium red 0.5-6 part mixes;
2) the dark red color crystal bead blank raw material mixing is carried out to granulation by tablets press;
3) the dark red color crystal bead blank raw material of granulation shape is put into glass quartz tank furnace and found, while founding, keep neutral atmosphere and liquid level of solution stable;
4) after cooling crystal solution Jing Liao road homogenizing, be molded into dark red color crystal bead blank;
5) moulding pearl embryo is put into fire and thrown stove polishing, integer, uniform coloring, allow moulding pearl embryo at the uniform velocity enter stainless steel pipes, pipe temperature is controlled at 850 DEG C, 200 revolutions per seconds of rotating speeds, in pipeline 5 minutes, pipeline was exactly out through integer, solid colour, no color differnece, without the dark red color crystal bead blank of decorative pattern.
Further, described in the preparation process 3 of dark red color crystal bead blank, while founding, temperature is controlled at 1310 DEG C-1350 DEG C.
Further, described in the preparation process 4 of dark red color crystal bead blank, cooling temperature is controlled at 800 DEG C-1000 DEG C.
The beneficial effect of the dark red color crystal bead blank of the present invention is: described dark red color crystal bead blank makes the redox equilibrium of cupric ion in the process of founding keep stable while preparation, thereby obtains good tint permanence; Do not adopt leaded raw material, there is glossiness good, bright-colored, neat, no color differnece, without decorative pattern, output is high, unleaded pollution-free, the advantage that productivity effect is good.
Embodiment
Following examples are used for illustrating the present invention, but are not used for limiting the scope of the invention.
Embodiment 1
The dark red color crystal bead blank of one of the present invention, this dark red color crystal bead blank is made up of following weight part proportioning composition: 0.5 part of 80 parts of quartz sands, 10 parts, zinc oxide, 20 parts of soda ash, 10 parts, salt of wormwood, 7 parts of boric acid, 2 parts, calcium carbonate, 0.5 part, aluminium hydroxide, 1 part of salt, 0.3 part of cadmium yellow, 0.5 part of selenium powder and cadmium red.
The preparation process of described dark red color crystal bead blank is as follows:
1) extracting by weight ratio 0.5 part of 80 parts of quartz sands, 10 parts, zinc oxide, 20 parts of soda ash, 10 parts, salt of wormwood, 7 parts of boric acid, 2 parts, calcium carbonate, 0.5 part, aluminium hydroxide, 1 part of salt, 0.3 part of cadmium yellow, 0.5 part of selenium powder and cadmium red mixes;
2) the dark red color crystal bead blank raw material mixing is carried out to granulation by tablets press;
3) the dark red color crystal bead blank raw material of granulation shape is put into glass quartz tank furnace and found, keep neutral atmosphere and liquid level of solution stable while founding, temperature is controlled at 1310 DEG C-1350 DEG C;
4) after cooling crystal solution Jing Liao road homogenizing, be molded into dark red color crystal bead blank, temperature is controlled at 800 DEG C-1000 DEG C;
5) moulding pearl embryo is put into fire and thrown stove polishing, integer, uniform coloring, allow moulding pearl embryo at the uniform velocity enter stainless steel pipes, pipe temperature is controlled at 850 DEG C, 200 revolutions per seconds of rotating speeds, in pipeline 5 minutes, pipeline was exactly out through integer, solid colour, no color differnece, without the dark red color crystal bead blank of decorative pattern.
Embodiment 2
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 6 parts of 190 parts of quartz sands, 30 parts, zinc oxide, 75 parts of soda ash, 35 parts, salt of wormwood, 23 parts of boric acid, 8 parts, calcium carbonate, 3 parts, aluminium hydroxide, 4 parts of salt, 3 parts of cadmium yellows, 2.5 parts of selenium powders and cadmium reds.
Embodiment 3
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 1 part of 135 parts of quartz sands, 18 parts, zinc oxide, 25 parts of soda ash, 15 parts, salt of wormwood, 11 parts of boric acid, 3 parts, calcium carbonate, 1 part, aluminium hydroxide, 1.5 parts of salt, 0.5 part of cadmium yellow, 1 part of selenium powder and cadmium red.
Embodiment 4
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 5.5 parts of 180 parts of quartz sands, 27 parts, zinc oxide, 70 parts of soda ash, 33 parts, salt of wormwood, 21 parts of boric acid, 7 parts, calcium carbonate, 2.8 parts, aluminium hydroxide, 3.5 parts of salt, 2.7 parts of cadmium yellows, 2.3 parts of selenium powders and cadmium reds.
Embodiment 5
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 3 parts of 156 parts of quartz sands, 22 parts, zinc oxide, 54 parts of soda ash, 26 parts, salt of wormwood, 17 parts of boric acid, 5 parts, calcium carbonate, 2 parts, aluminium hydroxide, 3 parts of salt, 2 parts of cadmium yellows, 2 parts of selenium powders and cadmium reds.
Embodiment 6
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 3 parts of 160 parts of quartz sands, 15 parts, zinc oxide, 37 parts of soda ash, 27 parts, salt of wormwood, 15 parts of boric acid, 6 parts, calcium carbonate, 3 parts, aluminium hydroxide, 3 parts of salt, 1 part of cadmium yellow, 2 parts of selenium powders and cadmium reds.
Embodiment 7
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 1.2 parts of 120 parts of quartz sands, 14 parts, zinc oxide, 32 parts of soda ash, 16 parts, salt of wormwood, 11 parts of boric acid, 3 parts, calcium carbonate, 1.5 parts, aluminium hydroxide, 1.5 parts of salt, 0.6 part of cadmium yellow, 0.9 part of selenium powder and cadmium reds.
Embodiment 8
Its difference from Example 1 is, this dark red color crystal bead blank is made up of following weight part proportioning composition: 4.8 parts of 155 parts of quartz sands, 27 parts, zinc oxide, 66 parts of soda ash, 29 parts, salt of wormwood, 18 parts of boric acid, 7.5 parts, calcium carbonate, 2.5 parts, aluminium hydroxide, 3.8 parts of salt, 2.5 parts of cadmium yellows, 1.7 parts of selenium powders and cadmium reds.
The present invention is not limited to above-mentioned preferred forms, and other any or akin products identical with the present invention that anyone draws under enlightenment of the present invention, within all dropping on protection scope of the present invention.
Claims (4)
1. a dark red color crystal bead blank, is characterized in that: this dark red color crystal bead blank is made up of following weight part proportioning composition: quartz sand 80-190 part, zinc oxide 10-30 part, soda ash 20-75 part, salt of wormwood 10-35 part, boric acid 7-23 part, calcium carbonate 2-8 part, aluminium hydroxide 0.5-3 part, salt 1-4 part, cadmium yellow 0.3-3 part, selenium powder 0.5-2.5 part and cadmium red 0.5-6 part.
2. a preparation method who prepares dark red color crystal bead blank claimed in claim 1, is characterized in that: the method comprises the following steps:
1) extracting by weight ratio quartz sand 80-190 part, zinc oxide 10-30 part, soda ash 20-75 part, salt of wormwood 10-35 part, boric acid 7-23 part, calcium carbonate 2-8 part, aluminium hydroxide 0.5-3 part, salt 1-4 part, cadmium yellow 0.3-3 part, selenium powder 0.5-2.5 part and cadmium red 0.5-6 part mixes;
2) the dark red color crystal bead blank raw material mixing is carried out to granulation by tablets press;
3) the dark red color crystal bead blank raw material of granulation shape is put into glass quartz tank furnace and found, while founding, keep neutral atmosphere and liquid level of solution stable;
4) after cooling crystal solution Jing Liao road homogenizing, be molded into dark red color crystal bead blank;
5) moulding pearl embryo is put into fire and thrown stove polishing, integer, uniform coloring, allow moulding pearl embryo at the uniform velocity enter stainless steel pipes, pipe temperature is controlled at 850 DEG C, 200 revolutions per seconds of rotating speeds, in pipeline 5 minutes, pipeline was exactly out through integer, solid colour, no color differnece, without the dark red color crystal bead blank of decorative pattern.
3. dark red color crystal bead blank preparation method according to claim 2, is characterized in that: described in the preparation process 3 of dark red color crystal bead blank, while founding, temperature is controlled at 1310 DEG C-1350 DEG C.
4. dark red color crystal bead blank preparation method according to claim 2, is characterized in that: described in the preparation process 4 of dark red color crystal bead blank, cooling temperature is controlled at 800 DEG C-1000 DEG C.