CN103911887A - Reactive printing paste for all-cotton fabrics - Google Patents

Reactive printing paste for all-cotton fabrics Download PDF

Info

Publication number
CN103911887A
CN103911887A CN201410154281.6A CN201410154281A CN103911887A CN 103911887 A CN103911887 A CN 103911887A CN 201410154281 A CN201410154281 A CN 201410154281A CN 103911887 A CN103911887 A CN 103911887A
Authority
CN
China
Prior art keywords
parts
carboxymethyl starch
reactive printing
applicable
cotton fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410154281.6A
Other languages
Chinese (zh)
Inventor
毕晓芳
劳吉清
姚金荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Runhong Trade Co Ltd
Original Assignee
Suzhou Runhong Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Runhong Trade Co Ltd filed Critical Suzhou Runhong Trade Co Ltd
Priority to CN201410154281.6A priority Critical patent/CN103911887A/en
Publication of CN103911887A publication Critical patent/CN103911887A/en
Pending legal-status Critical Current

Abstract

The invention relates to a reactive printing paste for all-cotton fabrics, which comprises 80 parts of carboxymethyl starch, 12 parts of sodium alginate, 8 parts of nano silicon dioxide and 5 parts of protein size. The paste uses the carboxymethyl starch as the main material, sodium alginate as the auxiliary material and nano silicon dioxide as the assistant, the properties of the materials can satisfy the demands for reactive printing and dyeing, and the sodium alginate consumption is lower, thereby lowering the production cost of the printing and dyeing enterprises. The paste is especially suitable for reactive printing and dyeing of all-cotton fabrics.

Description

A kind of reactive printing thickener that is applicable to all-cotton fabric
Technical field
The present invention relates to a kind of reactive printing thickener that is applicable to all-cotton fabric.
Background technology
In printing with reactive dye, thickener is generally used as thickener and regulates the rheological property of mill base.Sodium alginate because it does not react with REACTIVE DYES, tinctorial yield is high, chromatogram is complete, easily from fabric wash away, the advantage such as fabrics feel soft, be the first-selection of printing paste with active dye always.But its price is more expensive, stamp cost is relatively high, and therefore finding the thickener that a kind of # with low cost can print meticulous colored type has become the task of top priority.
Starch is a kind of renewable resource, and its deposit is abundant, easily obtains, but has active hydroxyl on its molecule, easily reacts with dyestuff, therefore in the application of printing paste with active dye, is restricted.
Summary of the invention
The object of the invention is to: overcome the defect of above-mentioned prior art, propose a kind of reactive printing thickener that is applicable to all-cotton fabric.
In order to achieve the above object, the present invention propose a kind of reactive printing thickener that is applicable to all-cotton fabric, its component by mass ratio as follows:
80 parts of carboxymethyl starch, 12 parts of sodium alginates, 6 parts of nano silicons, 5 parts, albumen slurry;
Described carboxymethyl starch is after cornstarch and farina are fully mixed with NaOH, monoxone, the extruding of use screw extruder, the second half at extruder is sprayed formaldehyde to material, final drying makes, and described cornstarch, farina, NaOH, chloroacetic mass ratio are 50:50:5:8;
Described carboxymethyl starch adds in deionized water after mixing with silica flour, and add NaOH and methyl alcohol, after being hydrolyzed, dry purification obtains the mixture of carboxymethyl starch and nano silicon, wherein, batching is by quality proportioning, 80 parts of carboxymethyl starch, 2.6 parts of silica flours, 0.1 part, NaOH, 0.2 part of methyl alcohol;
It is in 0.2% sodium hydroxide solution that described albumen slurry adds concentration by soybean protein, at the uniform velocity stirs after 15 minutes at 45 DEG C and obtains after elimination sediment.
The reactive printing thickener that the present invention is applicable to all-cotton fabric also has following improvement:
1, the present invention is applicable to the reactive printing thickener of all-cotton fabric, also comprises the Sodium Benzoate of 3 parts by mass.
2, the present invention is applicable to the reactive printing thickener of all-cotton fabric, also comprises the sodium thiosulfate of 4 parts by mass.
3, the present invention is applicable to the reactive printing thickener of all-cotton fabric, also comprises the polyvinyl alcohol of 2 parts by mass.
Thickener of the present invention is mainly taking carboxymethyl starch as main, and sodium alginate is auxiliary, and nano silicon is as auxiliary agent, and thickener various aspects of performance can meet active printing and dyeing demand, and its sodium alginate consumption is lower, has reduced the production cost of printing and dyeing enterprise.Thickener of the present invention is particularly useful for the activity printing and dyeing of all-cotton fabric.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be further described.
The present embodiment is applicable to the reactive printing thickener of all-cotton fabric, its component by mass ratio as follows:
80 parts of carboxymethyl starch, 12 parts of sodium alginates, 8 parts of nano silicons, 5 parts, albumen slurry, 3 parts of Sodium Benzoates, 4 parts, sodium thiosulfate, 2 parts of polyvinyl alcohol;
Carboxymethyl starch is after cornstarch and farina are fully mixed with NaOH, monoxone, the extruding of use screw extruder, the second half at extruder is sprayed formaldehyde to material, final drying makes, and described cornstarch, farina, NaOH, chloroacetic mass ratio are 50:50:5:8;
Carboxymethyl starch adds in deionized water after mixing with silica flour, and add NaOH and methyl alcohol, after being hydrolyzed, dry purification obtains the mixture of carboxymethyl starch and nano silicon, wherein, batching is by quality proportioning, 80 parts of carboxymethyl starch, 2.6 parts of silica flours, 0.1 part, NaOH, 0.2 part of methyl alcohol;
It is in 0.2% sodium hydroxide solution that albumen slurry adds concentration by soybean protein, at the uniform velocity stirs after 15 minutes at 45 DEG C and obtains after elimination sediment.
In addition to the implementation, the present invention can also have other embodiments.All employings are equal to the technical scheme of replacement or equivalent transformation formation, all drop on the protection domain of requirement of the present invention.

Claims (4)

1. be applicable to a reactive printing thickener for all-cotton fabric, its component by mass ratio as follows:
80 parts of carboxymethyl starch, 12 parts of sodium alginates, 6 parts of nano silicons, 5 parts, albumen slurry;
Described carboxymethyl starch is after cornstarch and farina are fully mixed with NaOH, monoxone, the extruding of use screw extruder, the second half at extruder is sprayed formaldehyde to material, final drying makes, and described cornstarch, farina, NaOH, chloroacetic mass ratio are 50:50:5:8;
Described carboxymethyl starch adds in deionized water after mixing with silica flour, and add NaOH and methyl alcohol, after being hydrolyzed, dry purification obtains the mixture of carboxymethyl starch and nano silicon, wherein, batching is by quality proportioning, 80 parts of carboxymethyl starch, 2.6 parts of silica flours, 0.1 part, NaOH, 0.2 part of methyl alcohol;
It is in 0.2% sodium hydroxide solution that described albumen slurry adds concentration by soybean protein, at the uniform velocity stirs after 15 minutes at 45 DEG C and obtains after elimination sediment.
2. the reactive printing thickener that is applicable to all-cotton fabric according to claim 1, is characterized in that: the Sodium Benzoate that also comprises 3 parts by mass.
3. the reactive printing thickener that is applicable to all-cotton fabric according to claim 2, is characterized in that: the sodium thiosulfate that also comprises 4 parts by mass.
4. the reactive printing thickener that is applicable to all-cotton fabric according to claim 3, is characterized in that: the polyvinyl alcohol that also comprises 2 parts by mass.
CN201410154281.6A 2014-04-17 2014-04-17 Reactive printing paste for all-cotton fabrics Pending CN103911887A (en)