CN103911860A - Artificial fiber fireproof fire retardant - Google Patents
Artificial fiber fireproof fire retardant Download PDFInfo
- Publication number
- CN103911860A CN103911860A CN201310737588.4A CN201310737588A CN103911860A CN 103911860 A CN103911860 A CN 103911860A CN 201310737588 A CN201310737588 A CN 201310737588A CN 103911860 A CN103911860 A CN 103911860A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire retardant
- fire
- artificial fiber
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an artificial fiber fireproof fire retardant. The artificial fiber fireproof fire retardant comprises, by weight, 10-20 parts of a fire retardant CP, 6-10 parts of methyl acrylate, 3-5 parts of acetic ester, 3-8 parts of trimethylol melamine, 4-8 parts of glycidyl methacrylate, 3-8 parts of acrylic acid-2-ethylpropyl ester, 4-8 parts of methacrylic acid, 1-3 parts of diethyl phthalate, 10-20 parts of polyvinyl alcohol and 200-400 parts of water. Compared with the prior art, the artificial fiber fireproof fire retardant can produce good fireproof flame-retardation effects on a textile prepared from artificial fibers. The artificial fiber fireproof fire retardant has good mildew-resistant and corrosion-resistant functions.
Description
Technical field
The invention belongs to textile auxiliary technical field, more specifically relate to a kind of artificial fibre fire-proof flame-retarded agent.
Background technology
Artificial fibre belongs to combustible material, and slightly not careful just easy initiation fire, therefore, carries out fire protection flame retarding processing to artificial fibre, is to prevent that fire from the important measures of fire damage occurring or reducing.China also expressly provides at present, must use fire-proof flame-retardant fibre textiles in seagoing vessel, aircraft and luxurious hotel etc.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, a kind of artificial fibre fire-proof flame-retarded agent is provided.
For achieving the above object, the present invention has taked following technical scheme:
A kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:10～20, methyl acrylate: 6～10, ethyl acetate: 3～5,
Trimethylol melamine: 3～8, glycidyl methacrylate: 4～8,
Acrylic acid-2-ethyl propyl ester: 3～8, methacrylic acid: 4～8,
Diethyl phthalate: 1～3, polyvinyl alcohol: 10～20, water: 200～400.
As preferably, described a kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:10, methyl acrylate: 6, ethyl acetate: 3,
Trimethylol melamine: 3, glycidyl methacrylate: 4,
Acrylic acid-2-ethyl propyl ester: 3, methacrylic acid: 4,
Diethyl phthalate: 1, polyvinyl alcohol: 10, water: 200.
As preferably, described a kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:20, methyl acrylate: 10, ethyl acetate: 5,
Trimethylol melamine: 8, glycidyl methacrylate: 8,
Acrylic acid-2-ethyl propyl ester: 8, methacrylic acid: 8,
Diethyl phthalate: 3, polyvinyl alcohol: 20, water: 400.
As preferably, described a kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:16, methyl acrylate: 8, ethyl acetate: 4,
Trimethylol melamine: 6, glycidyl methacrylate: 6,
Acrylic acid-2-ethyl propyl ester: 5, methacrylic acid: 6,
Diethyl phthalate: 2, polyvinyl alcohol: 15, water: 300.
The preparation method of described a kind of artificial fibre fire-proof flame-retarded agent is: by proportioning, each component is mixed, after dispersed with stirring is even, get final product to obtain finished product.
Compared with prior art, the textiles that the present invention makes artificial fibre has good fire protection flame retarding effect, and in addition, the present invention also has good mildew-resistant, anti-corrosion function.
The specific embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:10, methyl acrylate: 6, ethyl acetate: 3,
Trimethylol melamine: 3, glycidyl methacrylate: 4,
Acrylic acid-2-ethyl propyl ester: 3, methacrylic acid: 4,
Diethyl phthalate: 1, polyvinyl alcohol: 10, water: 200.
Embodiment 2
A kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:20, methyl acrylate: 10, ethyl acetate: 5,
Trimethylol melamine: 8, glycidyl methacrylate: 8,
Acrylic acid-2-ethyl propyl ester: 8, methacrylic acid: 8,
Diethyl phthalate: 3, polyvinyl alcohol: 20, water: 400.
Embodiment 3
A kind of artificial fibre fire-proof flame-retarded agent, in weight portion, composed of the following components:
Fire retardant CP:16, methyl acrylate: 8, ethyl acetate: 4,
Trimethylol melamine: 6, glycidyl methacrylate: 6,
Acrylic acid-2-ethyl propyl ester: 5, methacrylic acid: 6,
Diethyl phthalate: 2, polyvinyl alcohol: 15, water: 300.
The preparation method of described a kind of artificial fibre fire-proof flame-retarded agent is: by proportioning, each component is mixed, after dispersed with stirring is even, get final product to obtain finished product.
Claims (4)
1. an artificial fibre fire-proof flame-retarded agent, is characterized in that, in weight portion, composed of the following components:
Fire retardant CP:10～20, methyl acrylate: 6～10, ethyl acetate: 3～5,
Trimethylol melamine: 3～8, glycidyl methacrylate: 4～8,
Acrylic acid-2-ethyl propyl ester: 3～8, methacrylic acid: 4～8,
Diethyl phthalate: 1～3, polyvinyl alcohol: 10～20, water: 200～400.
2. a kind of artificial fibre fire-proof flame-retarded agent according to claim 1, is characterized in that, in weight portion, composed of the following components:
Fire retardant CP:10, methyl acrylate: 6, ethyl acetate: 3,
Trimethylol melamine: 3, glycidyl methacrylate: 4,
Acrylic acid-2-ethyl propyl ester: 3, methacrylic acid: 4,
Diethyl phthalate: 1, polyvinyl alcohol: 10, water: 200.
3. a kind of artificial fibre fire-proof flame-retarded agent according to claim 1, is characterized in that, in weight portion, composed of the following components:
Fire retardant CP:20, methyl acrylate: 10, ethyl acetate: 5,
Trimethylol melamine: 8, glycidyl methacrylate: 8,
Acrylic acid-2-ethyl propyl ester: 8, methacrylic acid: 8,
Diethyl phthalate: 3, polyvinyl alcohol: 20, water: 400.
4. a kind of artificial fibre fire-proof flame-retarded agent according to claim 1, is characterized in that, in weight portion, composed of the following components:
Fire retardant CP:16, methyl acrylate: 8, ethyl acetate: 4,
Trimethylol melamine: 6, glycidyl methacrylate: 6,
Acrylic acid-2-ethyl propyl ester: 5, methacrylic acid: 6,
Diethyl phthalate: 2, polyvinyl alcohol: 15, water: 300.