CN103897375B - A kind of Acid-proof plastic - Google Patents
A kind of Acid-proof plastic Download PDFInfo
- Publication number
- CN103897375B CN103897375B CN201310554021.3A CN201310554021A CN103897375B CN 103897375 B CN103897375 B CN 103897375B CN 201310554021 A CN201310554021 A CN 201310554021A CN 103897375 B CN103897375 B CN 103897375B
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- micro mist
- proof
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of Acid-proof plastic, the parts by weight of its each component are: acid-proof base-material 20 ~ 26 parts, rubber resin 4 ~ 8 parts, polyvinyl resin 10 ~ 20 parts, polyamide resin 15 ~ 25 parts, polycarbonate resin 30 ~ 50 parts, rhodia micro mist 2 ~ 4 parts, polycaprolactone micro mist 30 ~ 50 parts, sour front three phenolic ester 15 ~ 25 parts, sanitas 4 ~ 8 parts, additive 4 ~ 8 parts, compatilizer 3 ~ 6 parts.Acid-proof plastic of the present invention, has the effect of potent anti-bacteria, kill bacteria and acid-proof, can be used for production anti-attrition wear part, driving parts, and chemical industry, instrument etc.
Description
Technical field
The present invention relates to a kind of plastics, particularly a kind of Acid-proof plastic.
Background technology
Along with the develop rapidly of society, the standard of living of people constantly improves, and plastics are indispensable status in people's daily life, and polypropylene is a kind of non-toxic plastic, has superior heat resistance and good physicals, is widely used.But it is matt, easily brittle or break at low temperatures, equally with other plastics easily to be polluted by various unwanted bacteria and syphilis, under suitable temperature and humidity condition, very easily bacterial growth, for this reason, people add anti-acid starting material in acrylic plastering, this method, easily make its colour changed into yellow of polypropylene product, meanwhile, because the acid-proof stock dispersion added is uneven, acid-proof effect is undesirable can not be lasting.
Summary of the invention
The object of the invention is, a kind of nontoxic Acid-proof plastic is provided.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of Acid-proof plastic, and the parts by weight of its each component are: acid-proof base-material 20 ~ 26 parts, rubber resin 4 ~ 8 parts, polyvinyl resin 10 ~ 20 parts, polyamide resin 15 ~ 25 parts, polycarbonate resin 30 ~ 50 parts, rhodia micro mist 2 ~ 4 parts, polycaprolactone micro mist 30 ~ 50 parts, tritolyl phosphate 15 ~ 25 parts, sanitas 4 ~ 8 parts, additive 4 ~ 8 parts, compatilizer 3 ~ 6 parts.
Further, described acid-proof base-material is ethylene-propylene rubber(EPR), chlorinated rubber, fluorine glue mix, and blending ratio is 2:1:4.
Further, described sanitas is 1,3-dihydroxymethyl-5, and 5-T10 forms.
Further, described additive is the mixture of a kind of or any several arbitrary proportion in cellulose butyrate micro mist, thermoplastic polyester micro mist, polycaprolactone micro mist.
Further, described compatilizer is one in polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, Chlorinated Polypropylene III or its mixture.
The invention has the beneficial effects as follows: the invention provides a kind of Acid-proof plastic, there is the effect of potent anti-bacteria, kill bacteria and acid-proof, can be used for production anti-attrition wear part, driving parts, and chemical industry, instrument etc.
Embodiment
For understanding the present invention better; below by three embodiments, elaboration concrete is further done to the present invention; but unintelligible is limitation of the invention; for some nonessential improvement and adjustment that those skilled in the art does according to foregoing invention content, be also considered as dropping in protection scope of the present invention.
Embodiment 1
A kind of Acid-proof plastic of the present embodiment, the parts by weight of its each component are: acid-proof base-material 26 parts, rubber resin 8 parts, polyvinyl resin 20 parts, polyamide resin 25 parts, polycarbonate resin 50 parts, rhodia micro mist 4 parts, polycaprolactone micro mist 50 parts, tritolyl phosphate 25 parts, sanitas 8 parts, additive 8 parts, compatilizer 6 parts.
Described acid-proof base-material is ethylene-propylene rubber(EPR), chlorinated rubber, fluorine glue mix, and blending ratio is 2:1:4.
Described sanitas is 1,3-dihydroxymethyl-5, and 5-T10 forms.
Described additive is the mixture of a kind of or any several arbitrary proportion in cellulose butyrate micro mist, thermoplastic polyester micro mist, polycaprolactone micro mist.
Described compatilizer is one in polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, Chlorinated Polypropylene III or its mixture.
Embodiment 2
A kind of Acid-proof plastic of the present embodiment, the parts by weight of its each component are: acid-proof base-material 20 parts, rubber resin 4 parts, polyvinyl resin 10 parts, polyamide resin 15 parts, polycarbonate resin 30 parts, rhodia micro mist 2 parts, polycaprolactone micro mist 30 parts, tritolyl phosphate 15 parts, sanitas 4 parts, additive 4 parts, compatilizer 3 parts.
Described acid-proof base-material is ethylene-propylene rubber(EPR), chlorinated rubber, fluorine glue mix, and blending ratio is 2:1:4.
Described sanitas is 1,3-dihydroxymethyl-5, and 5-T10 forms.
Described additive is the mixture of a kind of or any several arbitrary proportion in cellulose butyrate micro mist, thermoplastic polyester micro mist, polycaprolactone micro mist.
Described compatilizer is one in polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, Chlorinated Polypropylene III or its mixture.
Embodiment 3
A kind of Acid-proof plastic of the present embodiment, the parts by weight of its each component are: acid-proof base-material 25 parts, rubber resin 7 parts, polyvinyl resin 17 parts, polyamide resin 24 parts, polycarbonate resin 45 parts, rhodia micro mist 3 parts, polycaprolactone micro mist 42 parts, tritolyl phosphate 18 parts, sanitas 7 parts, additive 5 parts, compatilizer 4 parts.
Described acid-proof base-material is ethylene-propylene rubber(EPR), chlorinated rubber, fluorine glue mix, and blending ratio is 2:1:4.
Described sanitas is 1,3-dihydroxymethyl-5, and 5-T10 forms.
Described additive is the mixture of a kind of or any several arbitrary proportion in cellulose butyrate micro mist, thermoplastic polyester micro mist, polycaprolactone micro mist.
Described compatilizer is one in polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, Chlorinated Polypropylene III or its mixture.
Claims (3)
1. an Acid-proof plastic, it is characterized in that, the parts by weight of its each component are: acid-proof base-material 20 ~ 26 parts, rubber resin 4 ~ 8 parts, polyvinyl resin 10 ~ 20 parts, polyamide resin 15 ~ 25 parts, polycarbonate resin 30 ~ 50 parts, rhodia micro mist 2 ~ 4 parts, polycaprolactone micro mist 30 ~ 50 parts, tritolyl phosphate 15 ~ 25 parts, sanitas 4 ~ 8 parts, additive 4 ~ 8 parts, compatilizer 3 ~ 6 parts; Described acid-proof base-material is ethylene-propylene rubber(EPR), chlorinated rubber, fluorine glue mix, and blending ratio is 2:1:4; Described additive is mixture that is a kind of in cellulose butyrate micro mist and thermoplastic polyester micro mist or any several arbitrary proportion.
2. a kind of Acid-proof plastic according to claim 1, is characterized in that, described sanitas is 1,3-dihydroxymethyl-5,5-T10 composition.
3. a kind of Acid-proof plastic according to claim 1, is characterized in that, described compatilizer is one in polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, Chlorinated Polypropylene III or its mixture.