CN103887055A - 一种小型软磁铁氧体磁芯高电感抛光方法 - Google Patents
一种小型软磁铁氧体磁芯高电感抛光方法 Download PDFInfo
- Publication number
- CN103887055A CN103887055A CN201310494678.5A CN201310494678A CN103887055A CN 103887055 A CN103887055 A CN 103887055A CN 201310494678 A CN201310494678 A CN 201310494678A CN 103887055 A CN103887055 A CN 103887055A
- Authority
- CN
- China
- Prior art keywords
- product
- sucker
- inductance
- small
- polishing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种小型软磁铁氧体磁芯高电感抛光方法,其特征在于:所述小型软磁铁氧体磁芯高电感抛光方法包括以下步骤:步骤一:将产品进行外观全检后整体摆放在小吸盘上,使用钢板尺整齐,然后吸盘上磁,使用专用压板轻微用力压平整;步骤二:用毛刷均匀将粘合剂涂抹于产品表面,粘合剂粘合后为固态,不溶于水,软硬度适中和保证磨削后能够轻易去除等条件;步骤三:将吸盘放入450℃-550℃高温里烘烤,大概1-2分钟取出;步骤四:冷却60分钟后,将吸盘卸磁,使用治具贴住产品和吸盘接触面,使产品分离开;步骤五:将产品进行抛光,抛光后,将产品使用稀释剂清洗干净。该方法操作简单、成本降低、合格率高、质量稳定。
Description
技术领域
本发明属于软磁铁氧体磁芯制造领域,特别涉及一种小型软磁铁氧体磁芯高电感抛光方法。
背景技术
软磁铁氧体磨削类高导磁芯,为了可以得到更高的电感,需将产品配合面进行抛光处理。现有技术中,而一些小型磁芯,在加工过程面临两个问题,一是作业时容易打乱,作业后磨斜(两翅或者单翅倾斜)报废比例大,完全靠作业人员的技术水平来控制,合格率极低。二是电感一致性极差,无法达到电感参数“CPK”的要求,人工挑选增加占用很大成本和质量困惑。面对这两大难题,目前行内没有有效的解决办法。
发明内容
针对上述现有技术得不足,本发明提供一种操作简单、成本降低、合格率高、质量稳定的小型软磁铁氧体磁芯高电感抛光方法。
本发明的技术方案是:一种小型软磁铁氧体磁芯高电感抛光方法,其特征在于:所述小型软磁铁氧体磁芯高电感抛光方法包括以下步骤:
步骤一:将产品进行外观全检后整体摆放在小吸盘上,使用钢板尺整齐,然后吸盘上磁,使用专用压板轻微用力压平整;
步骤二:用毛刷均匀将粘合剂涂抹于产品表面,粘合剂需要满足粘合后为固态,不溶于水,软硬度适中和保证磨削后能够轻易去除等条件;
步骤三:将吸盘放入450℃-550℃高温里烘烤,大概1-2分钟取出;
步骤四:冷却60分钟后,将吸盘卸磁,使用治具贴住产品和吸盘接触面,使产品分离开;
步骤五:将产品进行抛光,抛光后,将产品使用稀释剂清洗干净。
本发明的有益效果是:该小型软磁铁氧体磁芯高电感抛光方法,不需要经验丰富的操作人员进行小心翼翼的操作,一般懂得使用磨床的操作人员即可,减少了研磨倾斜和研磨时打乱造成的损失。且本技术抛光后的产品电感较之原抛光作业后的产品电感高出20%左右,生产成本降低了30%,成品合格率提高了15%,提高了产品的档次和竞争力。
Claims (1)
1.一种小型软磁铁氧体磁芯高电感抛光方法,其特征在于:所述小型软磁铁氧体磁芯高电感抛光方法包括以下步骤:
步骤一:将产品进行外观全检后整体摆放在小吸盘上,使用钢板尺整齐,然后吸盘上磁,使用专用压板轻微用力压平整;
步骤二:用毛刷均匀将粘合剂涂抹于产品表面,粘合剂粘合后为固态,不溶于水,软硬度适中和保证磨削后能够轻易去除等条件;
步骤三:将吸盘放入450℃-550℃高温里烘烤,大概1-2分钟取出;
步骤四:冷却60分钟后,将吸盘卸磁,使用治具贴住产品和吸盘接触面,使产品分离开;
步骤五:将产品进行抛光,抛光后,将产品使用稀释剂清洗干净。