CN103880110A - Method for manufacturing multi-effect water purification filter material - Google Patents
Method for manufacturing multi-effect water purification filter material Download PDFInfo
- Publication number
- CN103880110A CN103880110A CN201410104747.1A CN201410104747A CN103880110A CN 103880110 A CN103880110 A CN 103880110A CN 201410104747 A CN201410104747 A CN 201410104747A CN 103880110 A CN103880110 A CN 103880110A
- Authority
- CN
- China
- Prior art keywords
- accounts
- filtrate
- content
- filter material
- hard solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a multi-effect water purification filter material. The method comprises the following steps: putting wooden activated carbon, far infrared sintered balls, zeolite, medical stone and activated aluminum oxide into a high-temperature melting furnace, melting at high temperature till the materials are mixed into a viscous liquid, meanwhile putting coal ash, water and furfural slag into a stirring machine, uniformly stirring to obtain a soft solid, putting the viscous liquid in air so as to be naturally cooled to obtain a hard solid, uniformly adhering the hard solid to the surface of the hard solid to form a filter material blank, putting the filter material blank into an oven, baking so as to enable the soft solid to be completely dried and firmly adhered to the surface of the hard solid, thereby finally forming the filter material. In such a mode, the filter material maintains multiple effects that the granular impurities are absorbed, smell is removed, the filtrate is purified, the oxygen content of the filter material is increased, the biologic activity of the filtrate is improved, and the like, and meanwhile the filtering performance of the filter material is improved, machining procedures are reduced, and production of the filter material of large scale is facilitated.
Description
Technical field
The present invention relates to a kind of manufacture method, particularly a kind of manufacture method of many effects water purification filtrate.
Background technology
Along with improving constantly of present science and technology, water purifying plant is more and more welcome, simultaneously China's water of advocating thriftiness energetically, solve the phenomenon of the water scarcity causing because water is seriously polluted, present stage, water purifying plant is widely used various life areas by feat of the water purification function of self uniqueness, although but common water purifier has effect of water purification, but effect of its filtrate is poor, impurity in water all can not be filtered totally, even also retain some objectionable impuritiess, this healthy harm to people is huge.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of manufacture method of many effects water purification filtrate, can make filtrate keep adsorption particle impurity, remove peculiar smell, clear filtrate, interpolation filtrate oxygen level, when the multiple efficacies such as the biological activity of increase filtrate, increase the strainability of filtrate, and reduced manufacturing procedure, be applicable to the production of filtrate in enormous quantities.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the manufacture method that a kind of many effects water purification filtrate is provided, comprise: matrix and additive, carry out proportioning according to quality: the content of described matrix accounts for 70-80%, the content of described additive accounts for 20-30%, described matrix comprises: wood activated charcoal, far infrared agglomeration ball, zeolite, medical stone and activated alumina, according to quality proportioning: the content of described wood activated charcoal accounts for 15%, the content of described far infrared agglomeration ball accounts for 20%, the content of described zeolite accounts for 25%, the content of described medical stone accounts for 18%, the content of described activated alumina accounts for 22%, described additive comprises: coal ash, water and alditol slag, according to quality proportioning: the content of described coal ash accounts for 55%, described whose content accounts for 15%, the quality of described alditol slag accounts for 30%, its manufacture method is as follows:
(1), each composition of above-mentioned matrix is put into high-temperature smelting pot together according to aforementioned proportion carry out high temperature fusion, until each composition is mixed into viscous fluid;
(2), coal ash, water put into stirrer together with alditol slag carry out uniform stirring, obtain soft solid;
(3), by above-mentioned viscous fluid as for carrying out naturally cooling 2-3 hour in air, obtain hard solid;
(4), above-mentioned hard solid is adhered to described hard solid surface uniformly, formation filtrate blank;
(5), above-mentioned filtrate blank put into baking oven toast 1-2 hour, make soft solid complete drying, and firmly adhere to hard solid surface, finally form filtrate.
In a preferred embodiment of the present invention, in described step (1), the fusion temperature of smelting furnace is 400 ℃.
In a preferred embodiment of the present invention, in described step (5), the storing temperature of baking oven is 150 ℃.
Beneficial effect of the present invention: the present invention can make filtrate keep adsorption particle impurity, remove peculiar smell, clear filtrate, interpolation filtrate oxygen level, when the multiple efficacies such as the biological activity of increase filtrate, increase the strainability of filtrate, and reduced manufacturing procedure, be applicable to the production of filtrate in enormous quantities.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
In an embodiment of the present invention, a kind of manufacture method of many effects water purification filtrate, comprise: matrix and additive, carry out proportioning according to quality: the content of described matrix accounts for 70-80%, the content of described additive accounts for 20-30%, described matrix comprises: wood activated charcoal, far infrared agglomeration ball, zeolite, medical stone and activated alumina, according to quality proportioning: the content of described wood activated charcoal accounts for 15%, the content of described far infrared agglomeration ball accounts for 20%, the content of described zeolite accounts for 25%, the content of described medical stone accounts for 18%, the content of described activated alumina accounts for 22%, described additive comprises: coal ash, water and alditol slag, according to quality proportioning: the content of described coal ash accounts for 55%, described whose content accounts for 15%, the quality of described alditol slag accounts for 30%, its manufacture method is as follows:
(1), each composition of above-mentioned matrix is put into high-temperature smelting pot together according to aforementioned proportion carry out high temperature fusion, until each composition is mixed into viscous fluid;
(2), coal ash, water put into stirrer together with alditol slag carry out uniform stirring, obtain soft solid;
(3), by above-mentioned viscous fluid as for carrying out naturally cooling 2-3 hour in air, obtain hard solid;
(4), above-mentioned hard solid is adhered to described hard solid surface uniformly, formation filtrate blank;
(5), above-mentioned filtrate blank put into baking oven toast 1-2 hour, make soft solid complete drying, and firmly adhere to hard solid surface, finally form filtrate.
Further illustrate, the granule foreign of wood activated charcoal in can absorption filtrate, far infrared agglomeration ball can increase the oxygen level in filtrate, and improve the biological activity of filtrate, zeolite can be removed peculiar smell, make filtrate more as clear as crystal, medical stone can discharge trace element zinc and strontium, to arsenic, mercury, plumbous, cadmium element has stronger adsorptive power, activated alumina can promote the purification efficiency of each composition in filtrate matrix, thereby further improve water purification performance, these material at high temperature are fused into after viscous fluid, can fully play separately its effect, again by its naturally cooling, formation hard is fixed, use coal ash simultaneously, the soft solid that water and alditol slag mix, possess and have stronger viscosity, set it as the kernel of filtrate, can promote the strainability of external hard plastic solid, and viscous fluid in smelting furnace is for producing in enormous quantities, therefore this technology can be applicable to the production in enormous quantities of filtrate.
In another preferred embodiment of the present invention, in described step (1), the fusion temperature of smelting furnace is 400 ℃.
Further illustrate, fusion temperature is 400 ℃ and can makes the each composition in described matrix all can melt, thereby can be mixed into uniformly one.
In another preferred embodiment of the present invention, in described step (5), the storing temperature of baking oven is 150 ℃.
Further illustrate, because the moisture in filtrate blank needs evaporation, with the high temperature of 150 ℃, it is carried out to high temperature drying, can increase the speed of evaporation, raise the efficiency.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. the manufacture method of the filtrate of effect water purification more than a kind, it is characterized in that: comprising: matrix and additive, carry out proportioning according to quality: the content of described matrix accounts for 70-80%, the content of described additive accounts for 20-30%, described matrix comprises: wood activated charcoal, far infrared agglomeration ball, zeolite, medical stone and activated alumina, according to quality proportioning: the content of described wood activated charcoal accounts for 15%, the content of described far infrared agglomeration ball accounts for 20%, the content of described zeolite accounts for 25%, the content of described medical stone accounts for 18%, the content of described activated alumina accounts for 22%, described additive comprises: coal ash, water and alditol slag, according to quality proportioning: the content of described coal ash accounts for 55%, described whose content accounts for 15%, the quality of described alditol slag accounts for 30%, its manufacture method is as follows:
(1), each composition of above-mentioned matrix is put into high-temperature smelting pot together according to aforementioned proportion carry out high temperature fusion, until each composition is mixed into viscous fluid;
(2), coal ash, water put into stirrer together with alditol slag carry out uniform stirring, obtain soft solid;
(3), by above-mentioned viscous fluid as for carrying out naturally cooling 2-3 hour in air, obtain hard solid;
(4), above-mentioned hard solid is adhered to described hard solid surface uniformly, formation filtrate blank;
(5), above-mentioned filtrate blank put into baking oven toast 1-2 hour, make soft solid complete drying, and firmly adhere to hard solid surface, finally form filtrate.
2. the manufacture method of many effects water purification filtrate according to claim 1, is characterized in that: in described step (1), the fusion temperature of smelting furnace is 400 ℃.
3. the manufacture method of many effects water purification filtrate according to claim 1, is characterized in that: in described step (5), the storing temperature of baking oven is 150 ℃.