CN105923692A - Nano aluminum oxide water-purifying agent and preparation method thereof - Google Patents
Nano aluminum oxide water-purifying agent and preparation method thereof Download PDFInfo
- Publication number
- CN105923692A CN105923692A CN201610448948.2A CN201610448948A CN105923692A CN 105923692 A CN105923692 A CN 105923692A CN 201610448948 A CN201610448948 A CN 201610448948A CN 105923692 A CN105923692 A CN 105923692A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- water
- purifying agent
- aluminum oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nano aluminum oxide water-purifying agent and a preparation method thereof. The nano aluminum oxide water-purifying agent is made from the following materials according to parts by weight: 2-6 parts of nano aluminum oxide, 20-40 parts of medical stone, 5-15 parts of celestite, 25-40 parts of zeolite, 10-25 parts of perlite, and 20-40 parts of wood charcoal. The nano aluminum oxide water-purifying agent has high adsorbing capacity, can adsorb toxic harmful substances in water, such as heavy metal, remove peculiar odor in water and reduce the content of harmful substances in water, and can release various minerals and trace elements good for the growth of fry while purifying water since the materials are rich in minerals, thus helping the fry to grow healthily and quickly.
Description
Technical field
The invention belongs to water treatment field, be specifically related to a kind of nano oxidized aluminium water purifying agent and preparation method thereof.
Background technology
Since modern age, along with being continuously increased of people's production activity, the various sewage of generation get more and more, and water pollution situation is increasingly severe, and in water, situation about exceeding standard often occurs in content of beary metal.At present in cultivation pool, before new input fry, need the water in former pool is carried out purified treatment, the harmful substances such as some of which heavy metal are made to be removed and build a suitable water environment, but current water body purification to process its effectiveness comparison poor, it is impossible to the heavy metal in water is effectively removed.
Summary of the invention
In order to make up the deficiencies in the prior art, the invention provides a kind of nano oxidized aluminium water purifying agent and preparation method thereof, the heavy metal in water can effectively be removed by this water purification agent, it is ensured that the safety and sanitation of water quality.
The technical solution adopted in the present invention is as follows:
A kind of nano oxidized aluminium water purifying agent, according to parts by weight, is made up of following components:
Nano aluminium oxide 2-6 part, Maifanitum 20-40 part, celestite 5-15 part, zeolite 25-40 part, perlite 10-25 part, Linesless charcoal 20-40 part.
Further, described water purification agent also includes iron ore, and described iron ore is 5-15 part by weight.
The preparation method of a kind of nano oxidized aluminium water purifying agent, it is characterised in that comprise the following steps:
(1) remove the corresponding parts by weight of other raw material components of nano aluminium oxide respectively, be dried after cleaning；
(2) raw material that step (1) obtains is carried out attrition grinding, be ground to 150-350 mesh；
(3) the raw material mix homogeneously after grinding, and make graininess；
(4) by nano alumina powder jointed dispersion in an aqueous medium, form the nano aluminium oxide dispersion liquid of decentralized, homogenization and stabilisation, nano aluminium oxide aqueous dispersions is uniformly sprayed on the granule that step (3) obtains thus obtains described water purification agent.
The present invention has a following beneficial effect:
Nano oxidized aluminium water purifying agent of the present invention and preparation method thereof, this water purification agent has stronger absorbability, the absorption to poisonous and harmful substances such as the heavy metals in pool can be completed, remove abnormal flavour in water, reduce the content of harmful substance in water, and owing to this water purification agent raw material containing a large amount of mineral so that while water purification, discharge the multiple mineral useful to fry growth and trace element, contribute to the healthy fast-growth of fry.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further:
Embodiment
1
According to the following parts by weight nano oxidized aluminium water purifying agent of configuration: nano aluminium oxide 3 parts, Maifanitum 30 parts, celestite 10 parts, 30 parts of zeolite, perlite 20 parts, 35 parts of Linesless charcoal.
The preparation method of above-mentioned nano oxidized aluminium water purifying agent, comprises the following steps:
(1) remove the corresponding parts by weight of other raw material components of nano aluminium oxide respectively, be dried after cleaning；
(2) raw material that step (1) obtains is carried out attrition grinding, be ground to 150 mesh；
(3) the raw material mix homogeneously after grinding, and make graininess；
(4) by nano alumina powder jointed dispersion in an aqueous medium, form the nano aluminium oxide dispersion liquid of decentralized, homogenization and stabilisation, nano aluminium oxide aqueous dispersions is uniformly sprayed on the granule that step (3) obtains thus obtains described water purification agent.
Embodiment
2
According to the following parts by weight nano oxidized aluminium water purifying agent of configuration: nano aluminium oxide 5 parts, Maifanitum 35 parts, celestite 10 parts, 30 parts of zeolite, perlite 15 parts, 40 parts of Linesless charcoal.
The preparation method of above-mentioned nano oxidized aluminium water purifying agent, comprises the following steps:
(1) remove the corresponding parts by weight of other raw material components of nano aluminium oxide respectively, be dried after cleaning；
(2) raw material that step (1) obtains is carried out attrition grinding, be ground to 200 mesh；
(3) the raw material mix homogeneously after grinding, and make graininess；
(4) by nano alumina powder jointed dispersion in an aqueous medium, form the nano aluminium oxide dispersion liquid of decentralized, homogenization and stabilisation, nano aluminium oxide aqueous dispersions is uniformly sprayed on the granule that step (3) obtains thus obtains described water purification agent.
Embodiment
3
According to the following parts by weight nano oxidized aluminium water purifying agent of configuration: nano aluminium oxide 6 parts, Maifanitum 30 parts, celestite 10 parts, 25 parts of zeolite, perlite 10 parts, 30 parts of Linesless charcoal, iron ore 10 parts.
The preparation method of above-mentioned nano oxidized aluminium water purifying agent, comprises the following steps:
(1) remove the corresponding parts by weight of other raw material components of nano aluminium oxide respectively, be dried after cleaning；
(2) raw material that step (1) obtains is carried out attrition grinding, be ground to 350 mesh；
(3) the raw material mix homogeneously after grinding, and make graininess；
(4) by nano alumina powder jointed dispersion in an aqueous medium, form the nano aluminium oxide dispersion liquid of decentralized, homogenization and stabilisation, nano aluminium oxide aqueous dispersions is uniformly sprayed on the granule that step (3) obtains thus obtains described water purification agent.
The nano oxidized aluminium water purifying agent of the present invention, there is stronger absorbability, the absorption to poisonous and harmful substances such as the heavy metals in water can be completed, remove abnormal flavour in water, reduce the content of harmful substance in water, and owing to this water purification agent raw material containing a large amount of mineral so that while water purification, discharge the multiple mineral useful to fry growth and trace element, contribute to the healthy fast-growth of fry.
Claims (3)
1. a nano oxidized aluminium water purifying agent, it is characterised in that according to parts by weight, be made up of following components:
Nano aluminium oxide 2-6 part, Maifanitum 20-40 part, celestite 5-15 part, zeolite 25-40 part, perlite 10-25 part, Linesless charcoal 20-40 part.
The nano oxidized aluminium water purifying agent of one the most according to claim 1, it is characterised in that described water purification agent also includes iron ore, described iron ore is 5-15 part by weight.
3. the preparation method of the nano oxidized aluminium water purifying agent described in a claim 1 or 2, it is characterised in that comprise the following steps: (1) removes the corresponding parts by weight of other raw material components of nano aluminium oxide respectively, is dried after cleaning；
(2) raw material that step (1) obtains is carried out attrition grinding, be ground to 150-350 mesh；
(3) the raw material mix homogeneously after grinding, and make graininess；
(4) by nano alumina powder jointed dispersion in an aqueous medium, form the nano aluminium oxide dispersion liquid of decentralized, homogenization and stabilisation, nano aluminium oxide aqueous dispersions is uniformly sprayed on the granule that step (3) obtains thus obtains described water purification agent.