CN103865148A - Compound polyethylene metallized film for capacitor and preparation method of film - Google Patents
Compound polyethylene metallized film for capacitor and preparation method of film Download PDFInfo
- Publication number
- CN103865148A CN103865148A CN201410075469.1A CN201410075469A CN103865148A CN 103865148 A CN103865148 A CN 103865148A CN 201410075469 A CN201410075469 A CN 201410075469A CN 103865148 A CN103865148 A CN 103865148A
- Authority
- CN
- China
- Prior art keywords
- film
- low density
- density polyethylene
- parts
- capacitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a compound polyethylene metallized film for a capacitor. The film is characterized by being prepared from the following raw materials in parts by weight: 200 parts of low density polyethylene, 20-23 parts of metallocene linear low density polyethylene, 1-2 parts of diphenylmethane diisocyanate, 4-5 parts of isobornyl acrylate, 1-2 parts of phenyl glycidyl ether, 2-3 parts of aromatic polyurethane acrylate and 5-6 parts of assistant. The technical process is simple, and the thin film capacitor prepared is less in contact resistance, so that the product is good in characteristic. The assistant is added to enhance the barrier property and the air impermeability of the film, so that the film has good pressure resistance and impact resistance, and meanwhile, the film has the characteristics of high heat sealing strength and good heat sealing performance, and is breakdown resistant, flame retardant and long in service life.
Description
Technical field
The present invention relates to field of capacitor manufacture, particularly capacitor metalized film of a kind of composite polyethylene and preparation method thereof.
Background technology
Film capacitor is to work as electrode with tinsel, by itself and poly-ethyl ester, and polypropylene, the plastics films such as polystyrene or polycarbonate, from two ends are overlapping, are wound into the electrical condenser of structure cylindraceous; In the middle of all plastics film electric capacity, the characteristic of polypropylene (PP) electric capacity and polystyrene (PS) electric capacity is the most remarkable, certainly the price of these two kinds of electrical condensers is also higher, the film quality of electrical condenser directly affects work-ing life and the product performance of electrical condenser, the demand of capacitor film is large, kind is many, adopt the film of single raw material production to be difficult to adapt to the requirement in market, but every kind of raw material has its weak point, so the film of producing is difficult to meet the demand of various situations.
Summary of the invention
The object of this invention is to provide capacitor metalized film of a kind of composite polyethylene and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The capacitor metalized film of a kind of composite polyethylene, is made up of the raw material of following weight part: Low Density Polyethylene 200, metallocene linear-low density polyethylene 20-23, '-diphenylmethane diisocyanate 1-2, isobornyl acrylate 4-5, phenyl glycidyl ether 1-2, aromatic urethane acrylate 2-3, auxiliary agent 5-6;
Described auxiliary agent is made up of the raw material of following weight part: metallocene linear-low density polyethylene 12-15, calcium zinc stabilizer 2-3, cyanuric acid zinc 1-2,2-ethylhexyl diphenyl phosphate 5-6, linden ashes 1-2, nanometer jade powder 0.3-0.4, phosphorous acid ester 8-10, polyisobutene 2-3,, Flos Rosae Rugosae quintessence oil 0.1-0.2; Metallocene linear-low density polyethylene is heated to molten state by preparation method, then, adds nanometer jade powder, linden ashes, stirs 10-15 minute, finally adds other composition, and dispersed with stirring is even, cooling, and granulation to obtain final product.
The capacitor metalized film of composite polyethylene of the present invention, made by following concrete steps:
(1) by Low Density Polyethylene, metallocene linear-low density polyethylene, '-diphenylmethane diisocyanate, isobornyl acrylate heating and melting, add again auxiliary agent and all the other remaining components fully to stir, send into forcing machine melting, filtration, and then by forcing machine extruding sheet melt, filter >1200 order, the temperature of described forcing machine is 220-260 ℃;
(2) the sheet melt of step (1) being made makes slab after by sharp cooling roll and air raining chamber cooling and shaping, carries out successively longitudinal stretching, cross directional stretch, alligatoring face corona treatment;
(3) rolling, ageing treatment, ageing treatment for the second time for the first time;
(4) vacuum-evaporation metalized film, alligatoring face forms metal layer.
Complete processing of the present invention is simple, and little with the film capacitor contact resistance of its making, thereby makes product performance good; Add auxiliary agent, strengthened barrier and the resistance to air loss of film, there is good resistance to pressure and shock-resistance, there is the feature that heat seal strength is high, heat sealability is good simultaneously, anti-breakdown, fire-retardant, long service life.
Embodiment
Below by specific examples, the present invention is described in detail.
The capacitor metalized film of a kind of composite polyethylene, by following weight part (kilogram) raw material make: Low Density Polyethylene 200, metallocene linear-low density polyethylene 20, '-diphenylmethane diisocyanate 1, isobornyl acrylate 4, phenyl glycidyl ether 1, aromatic urethane acrylate 2, auxiliary agent 5;
Described auxiliary agent by following weight part (kilogram) raw material make: metallocene linear-low density polyethylene 12, calcium zinc stabilizer 2, cyanuric acid zinc 1,2-ethylhexyl diphenyl phosphate 5, linden ashes 2, nanometer jade powder 0.3, phosphorous acid ester 8, polyisobutene 2, Flos Rosae Rugosae quintessence oil 0.1; Metallocene linear-low density polyethylene is heated to molten state by preparation method, then, adds nanometer jade powder, linden ashes, stirs 10-15 minute, finally adds other composition, and dispersed with stirring is even, cooling, and granulation to obtain final product.
The capacitor metalized film of composite polyethylene of the present invention, made by following concrete steps:
(1) by Low Density Polyethylene, metallocene linear-low density polyethylene, '-diphenylmethane diisocyanate, isobornyl acrylate heating and melting, add again auxiliary agent and all the other remaining components fully to stir, send into forcing machine melting, filtration, and then by forcing machine extruding sheet melt, filter >1200 order, the temperature of described forcing machine is 220-260 ℃;
(2) the sheet melt of step (1) being made makes slab after by sharp cooling roll and air raining chamber cooling and shaping, carries out successively longitudinal stretching, cross directional stretch, alligatoring face corona treatment;
(3) rolling, ageing treatment, ageing treatment for the second time for the first time;
(4) vacuum-evaporation metalized film, alligatoring face forms metal layer.
The technical indicator of the metallized film of the embodiment of the present invention is as follows:
(1) lateral shrinkage≤0.2%, longitudinal contraction rate≤2.5%
(2) transverse tensile strength >=15Mpa, longitudinal tensile strength >=12Mpa;
(3) minimum break-down voltage 589Vv/um.
Claims (2)
1. the capacitor metalized film of composite polyethylene, it is characterized in that, made by the raw material of following weight part: Low Density Polyethylene 200, metallocene linear-low density polyethylene 20-23, '-diphenylmethane diisocyanate 1-2, isobornyl acrylate 4-5, phenyl glycidyl ether 1-2, aromatic urethane acrylate 2-3, auxiliary agent 5-6;
Described auxiliary agent is made up of the raw material of following weight part: metallocene linear-low density polyethylene 12-15, calcium zinc stabilizer 2-3, cyanuric acid zinc 1-2,2-ethylhexyl diphenyl phosphate 5-6, linden ashes 1-2, nanometer jade powder 0.3-0.4, phosphorous acid ester 8-10, polyisobutene 2-3,, Flos Rosae Rugosae quintessence oil 0.1-0.2; Metallocene linear-low density polyethylene is heated to molten state by preparation method, then, adds nanometer jade powder, linden ashes, stirs 10-15 minute, finally adds other composition, and dispersed with stirring is even, cooling, and granulation to obtain final product.
2. the capacitor metalized film of composite polyethylene according to claim 1, is characterized in that, is made up of following concrete steps:
(1) by Low Density Polyethylene, metallocene linear-low density polyethylene, '-diphenylmethane diisocyanate, isobornyl acrylate heating and melting, add again auxiliary agent and all the other remaining components fully to stir, send into forcing machine melting, filtration, and then by forcing machine extruding sheet melt, filter >1200 order, the temperature of described forcing machine is 220-260 ℃;
(2) the sheet melt of step (1) being made makes slab after by sharp cooling roll and air raining chamber cooling and shaping, carries out successively longitudinal stretching, cross directional stretch, alligatoring face corona treatment;
(3) rolling, ageing treatment, ageing treatment for the second time for the first time;
(4) vacuum-evaporation metalized film, alligatoring face forms metal layer.