CN103864364A - 一种粘胶纤维/硅藻土复合保温砂浆及其制作方法 - Google Patents

一种粘胶纤维/硅藻土复合保温砂浆及其制作方法 Download PDF

Info

Publication number
CN103864364A
CN103864364A CN201410046423.7A CN201410046423A CN103864364A CN 103864364 A CN103864364 A CN 103864364A CN 201410046423 A CN201410046423 A CN 201410046423A CN 103864364 A CN103864364 A CN 103864364A
Authority
CN
China
Prior art keywords
parts
thermal insulation
diatomite
insulation mortar
viscose
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410046423.7A
Other languages
English (en)
Other versions
CN103864364B (zh
Inventor
许盟凯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Municipal Cultural Relics and Ancient Construction Engineering Company
Original Assignee
ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd filed Critical ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd
Priority to CN201410046423.7A priority Critical patent/CN103864364B/zh
Publication of CN103864364A publication Critical patent/CN103864364A/zh
Application granted granted Critical
Publication of CN103864364B publication Critical patent/CN103864364B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种粘胶纤维/硅藻土复合保温砂浆，其特征在于，由下列重量份的原料制成：水泥300-340、硫脲废渣200-230、硅灰100-120、硅藻土200-250、铝矾土230-240、纤维素醚5-8、麦饭石150-180、粘胶纤维6-9、硫酸钠2-6、甲基硅醇钠2-5、助剂3-6；本发明将硫脲废渣加入保温砂浆的原料中，同时添加其它常规助剂，采用合适的生产工艺生产出来的保温砂浆，具有成本低、保温隔热性佳、防火和耐腐蚀性性能强、抗压强度高、绿色环保等优点，实现了变废为宝的循环经济效果，在我国建筑节能应用领域具有极大的市场空间和发展前景。

Description

一种粘胶纤维/硅藻土复合保温砂浆及其制作方法
技术领域
本发明涉及保温砂浆技术领域，具体涉及一种粘胶纤维/硅藻土复合保温砂浆及其制作方法。
背景技术
近年来，工业生产过程产生的各种固废以及城市建设拆迁重造带来的固废等一直困扰着居民的生活环境，本发明将固废作为原材料添加到保温砂浆中，实现了废物的循环利用，减少了对环境的污染，符合可持续发展战略要求。
 保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业加水搅拌混合而制成的一种预拌干粉砂浆。不仅可以用于建筑外墙外保温，还可以用于外墙内保温，或者外墙内外同时保温，及屋顶的保温和地热的隔热层，为节能体系的设计提供一定的灵活性。具有施工方便、耐久性好、质轻、保温、绝热性好等优点。但现有的传统砂浆保温隔热材料，如聚笨颗粒保温砂浆、珍珠保温砂浆等，在使用过程中暴露出了许多缺陷，如表面空鼓、开裂、脱落、易霉变等，另外，大部分保温砂浆的孔隙率较高，故整体吸水率均很高，吸水后不仅会降低材料的强度，而且会大降低其保温性能。因此，一种新型耐老化、耐腐蚀、抗裂、防虫、除菌等多功能强度高的保温砂浆的需求迫在眉睫。
发明内容
本发明的目的就是提供一种粘胶纤维/硅藻土复合保温砂浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种粘胶纤维/硅藻土复合保温砂浆，其特征在于，由下列重量份的原料制成：水泥300-340、硫脲废渣200-230、硅灰100-120、硅藻土200-250、铝矾土230-240、纤维素醚5-8、麦饭石150-180、粘胶纤维6-9、硫酸钠2-6、甲基硅醇钠2-5、助剂3-6。
所述的助剂由下列重量份原料制成：硅藻土4-9、聚苯醚0.03-0.05、碳纳米管0.05-0.35、聚氧乙烯醚0.01-0.03、硅酸钠0.15-0.4、三乙胺1.3-2.5、硅灰石粉1-3、乌洛托品0.01-0.03、樟脑0.05-0.3、柏木油1-3、花生壳3-5、三氯乙基磷酸酯1.2-2.3，其制备方法是将各物料粉碎加适量水搅拌30-40分钟，混匀，造粒，成球粒径在0.5-1mm，烘干即得。
所述的一种粘胶纤维/硅藻土复合保温砂浆的制备方法，其特征在于包括以下步骤：
（1）将麦饭石放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出烘干，粉碎至150-180目；
（2）将硫脲废渣、硅灰、硅藻土、铝矾土一起于650-750℃下煅烧3-6小时后取出粉碎，加入粘胶纤维搅拌混匀；
（3）将步骤（1）、（2）反应物料、纤维素醚搅拌5-8分钟混匀，再与其它剩余成分投入搅拌机里搅拌混合20-30分钟，将搅拌好的物料用自动包装机包好即得。使用时加适量水混合搅拌均匀即可。
本发明有以下有益效果：本发明将硫脲废渣加入保温砂浆的原料中，同时添加其它常规助剂，采用合适的生产工艺生产出来的保温砂浆，具有成本低、保温隔热性佳、防火和耐腐蚀性性能强、抗压强度高、绿色环保等优点，实现了变废为宝的循环经济效果，在我国建筑节能应用领域具有极大的市场空间和发展前景。
具体实施方式
所述的一种粘胶纤维/硅藻土复合保温砂浆，其特征在于，由下列重量份的原料制成：水泥310、硫脲废渣220、硅灰110、硅藻土230、铝矾土240、纤维素醚5、麦饭石150、粘胶纤维6、硫酸钠2、甲基硅醇钠5、助剂3。
所述的助剂由下列重量份原料制成：硅藻土9、聚苯醚0.03、碳纳米管0.35、聚氧乙烯醚0.01、硅酸钠0.15、三乙胺1.5、硅灰石粉1、乌洛托品0.01、樟脑0.05、柏木油3、花生壳5、三氯乙基磷酸酯1.2，其制备方法是将各物料粉碎加适量水搅拌30-40分钟，混匀，造粒，成球粒径在0.5-1mm，烘干即得。
制作方法包括以下步骤：
（1）将麦饭石放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出烘干，粉碎至150-180目；
（2）将硫脲废渣、硅灰、硅藻土、铝矾土一起于650-750℃下煅烧3-6小时后取出粉碎，加入粘胶纤维搅拌混匀；
（3）将步骤（1）、（2）反应物料、纤维素醚搅拌5-8分钟混匀，再与其它剩余成分投入搅拌机里搅拌混合20-30分钟，将搅拌好的物料用自动包装机包好即得。
通过上述实施例加工得到的保温砂浆的技术指标如下：
（1）导热系数（平均温度25±2℃）：0.071W/(m·k)；
（2）抗压强度（28d）：290kPa；
（3）干密度：345kg/m3；
（4）粘结强度：310kpa。

Claims (2)

1.一种粘胶纤维/硅藻土复合保温砂浆，其特征在于，由下列重量份的原料制成：水泥300-340、硫脲废渣200-230、硅灰100-120、硅藻土200-250、铝矾土230-240、纤维素醚5-8、麦饭石150-180、粘胶纤维6-9、硫酸钠2-6、甲基硅醇钠2-5、助剂3-6；所述的助剂由下列重量份原料制成：硅藻土4-9、聚苯醚0.03-0.05、碳纳米管0.05-0.35、聚氧乙烯醚0.01-0.03、硅酸钠0.15-0.4、三乙胺1.3-2.5、硅灰石粉1-3、乌洛托品0.01-0.03、樟脑0.05-0.3、柏木油1-3、花生壳3-5、三氯乙基磷酸酯1.2-2.3，其制备方法是将各物料粉碎加适量水搅拌30-40分钟，混匀，造粒，成球粒径在0.5-1mm，烘干即得。
2.根据权利要求1所述的一种粘胶纤维/硅藻土复合保温砂浆的制作方法，其特征在于包括以下步骤：
（1）将麦饭石放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时，取出烘干，粉碎至150-180目；
（2）将硫脲废渣、硅灰、硅藻土、铝矾土一起于650-750℃下煅烧3-6小时后取出粉碎，加入粘胶纤维搅拌混匀；
（3）将步骤（1）、（2）反应物料、纤维素醚搅拌5-8分钟混匀，再与其它剩余成分投入搅拌机里搅拌混合20-30分钟，将搅拌好的物料用自动包装机包好即得。
CN201410046423.7A 2014-02-10 2014-02-10 一种粘胶纤维/硅藻土复合保温砂浆及其制作方法 Active CN103864364B (zh)