CN103864363A - 一种抗腐蚀保温砂浆及其制作方法 - Google Patents
一种抗腐蚀保温砂浆及其制作方法 Download PDFInfo
- Publication number
- CN103864363A CN103864363A CN201410046421.8A CN201410046421A CN103864363A CN 103864363 A CN103864363 A CN 103864363A CN 201410046421 A CN201410046421 A CN 201410046421A CN 103864363 A CN103864363 A CN 103864363A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- powder
- insulation mortar
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗腐蚀保温砂浆,其特征在于,由下列重量份的原料制成:水泥320-380、高岭土200-250、垃圾焚烧炉渣220-260、生石灰100-140、废玻璃渣210-260、粗沙140-190、玻璃纤维7-9、0.5-5mm木纤维9-12、木材锯末粉60-90、烟草秸秆60-80、聚乙烯醇缩乙醛3-7、助剂4-6;本发明制得的保温砂浆的导热系数低、保温性能稳定、抗压强度高、抗腐蚀、耐老化,适用于各种墙体保温。
Description
技术领域
本发明涉及保温砂浆技术领域,具体涉及一种抗腐蚀保温砂浆及其制作方法。
背景技术
近年来,工业生产过程产生的各种固废以及城市建设拆迁重造带来的固废等一直困扰着居民的生活环境,本发明将固废作为原材料添加到保温砂浆中,实现了废物的循环利用,减少了对环境的污染,符合可持续发展战略要求。
保温砂浆是以各种轻质材料为骨料,以水泥为胶凝料,掺和一些改性添加剂,经生产企业加水搅拌混合而制成的一种预拌干粉砂浆。不仅可以用于建筑外墙外保温,还可以用于外墙内保温,或者外墙内外同时保温,及屋顶的保温和地热的隔热层,为节能体系的设计提供一定的灵活性。具有施工方便、耐久性好、质轻、保温、绝热性好等优点。但现有的传统砂浆保温隔热材料,如聚笨颗粒保温砂浆、珍珠保温砂浆等,在使用过程中暴露出了许多缺陷,如表面空鼓、开裂、脱落、易霉变等,另外,大部分保温砂浆的孔隙率较高,故整体吸水率均很高,吸水后不仅会降低材料的强度,而且会大降低其保温性能。因此,一种新型耐老化、耐腐蚀、抗裂、防虫、除菌等多功能强度高的保温砂浆的需求迫在眉睫。
发明内容
本发明的目的就是提供一种抗腐蚀保温砂浆及其制作方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种抗腐蚀保温砂浆,其特征在于,由下列重量份的原料制成:水泥320-380、高岭土200-250、垃圾焚烧炉渣220-260、生石灰100-140、废玻璃渣210-260、粗沙140-190、玻璃纤维7-9、0.5-5mm木纤维9-12、木材锯末粉60-90、烟草秸秆60-80、聚乙烯醇缩乙醛3-7、助剂4-6。
所述的助剂由下列重量份原料制成:粉煤灰5-9、铝粉0.001-0.003、聚偏二氟乙烯1.3-3.1、碳化硅粉末2-4、钛白粉2-5、硅溶胶0.2-0.4、可再分散性乳胶粉0.2-0.7、香茅油3-6、冰片1-3、超微蜡粉0.7-0.9、葡萄藤4-7,其制备方法是将各物料粉碎加适量水搅拌30-40分钟,混匀,造粒,成球粒径在0.5-1mm,烘干即得。
所述的一种抗腐蚀保温砂浆的制备方法,其特征在于包括以下步骤:
(1)将木材锯末粉、烟草秸秆放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时,取出烘干脱水,粉碎;
(2)将高岭土、垃圾焚烧炉渣、生石灰一起于650-780℃下煅烧3-6小时后取出,加入木纤维、聚乙烯醇缩乙醛搅拌混匀;
(3)将步骤(1)、(2)反应物料、粗沙、玻璃纤维搅拌5-8分钟混匀,再与其它剩余成分投入搅拌机里搅拌混合20-30分钟,将搅拌好的物料用自动包装机包好即得。使用时加适量水混合搅拌均匀即可。
本发明有以下有益效果:本发明制得的保温砂浆的导热系数低、保温性能稳定、抗压强度高、抗腐蚀、耐老化,适用于各种墙体保温。
具体实施方式
所述的一种抗腐蚀保温砂浆,其特征在于,由下列重量份的原料制成:水泥320、高岭土210、垃圾焚烧炉渣220、生石灰100、废玻璃渣260、粗沙140、玻璃纤维7、0.5-5mm木纤维9、木材锯末粉90、烟草秸秆80、聚乙烯醇缩乙醛3、助剂4。
所述的助剂由下列重量份原料制成:粉煤灰7、铝粉0.001、聚偏二氟乙烯1.3、碳化硅粉末4、钛白粉2、硅溶胶0.2、可再分散性乳胶粉0.2、香茅油3、冰片3、超微蜡粉0.7、葡萄藤4,其制备方法是将各物料粉碎加适量水搅拌30-40分钟,混匀,造粒,成球粒径在0.5-1mm,烘干即得。
制作方法包括以下步骤:
(1)将木材锯末粉、烟草秸秆放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时,取出烘干脱水,粉碎;
(2)将高岭土、垃圾焚烧炉渣、生石灰一起于650-780℃下煅烧3-6小时后取出,加入木纤维、聚乙烯醇缩乙醛搅拌混匀;
(3)将步骤(1)、(2)反应物料、粗沙、玻璃纤维搅拌5-8分钟混匀,再与其它剩余成分投入搅拌机里搅拌混合20-30分钟,将搅拌好的物料用自动包装机包好即得。
通过上述实施例加工得到的保温砂浆的技术指标如下:
(1)导热系数(平均温度25±2℃):0.068W/(m·k);
(2)抗压强度(28d):287kPa;
(3)耐高温、和墙面紧密粘结、无缝。
Claims (2)
1.一种抗腐蚀保温砂浆,其特征在于,由下列重量份的原料制成:水泥320-380、高岭土200-250、垃圾焚烧炉渣220-260、生石灰100-140、废玻璃渣210-260、粗沙140-190、玻璃纤维7-9、0.5-5mm木纤维9-12、木材锯末粉60-90、烟草秸秆60-80、聚乙烯醇缩乙醛3-7、助剂4-6;所述的助剂由下列重量份原料制成:粉煤灰5-9、铝粉0.001-0.003、聚偏二氟乙烯1.3-3.1、碳化硅粉末2-4、钛白粉2-5、硅溶胶0.2-0.4、可再分散性乳胶粉0.2-0.7、香茅油3-6、冰片1-3、超微蜡粉0.7-0.9、葡萄藤4-7,其制备方法是将各物料粉碎加适量水搅拌30-40分钟,混匀,造粒,成球粒径在0.5-1mm,烘干即得。
2.根据权利要求1所述的一种抗腐蚀保温砂浆的制作方法,其特征在于包括以下步骤:
(1)将木材锯末粉、烟草秸秆放入1‰氯化铁和0.5‰氯化钙复合溶液中浸渍10-12小时,取出烘干脱水,粉碎;
(2)将高岭土、垃圾焚烧炉渣、生石灰一起于650-780℃下煅烧3-6小时后取出,加入木纤维、聚乙烯醇缩乙醛搅拌混匀;
(3)将步骤(1)、(2)反应物料、粗沙、玻璃纤维搅拌5-8分钟混匀,再与其它剩余成分投入搅拌机里搅拌混合20-30分钟,将搅拌好的物料用自动包装机包好即得。