CN103849192A - Paint containing silver ion antibacterial agent and red phosphorus - Google Patents
Paint containing silver ion antibacterial agent and red phosphorus Download PDFInfo
- Publication number
- CN103849192A CN103849192A CN201210509649.7A CN201210509649A CN103849192A CN 103849192 A CN103849192 A CN 103849192A CN 201210509649 A CN201210509649 A CN 201210509649A CN 103849192 A CN103849192 A CN 103849192A
- Authority
- CN
- China
- Prior art keywords
- paint
- red phosphorus
- silver ion
- flame retardant
- antibacterial agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a paint containing a silver ion antibacterial agent and red phosphorus. The paint is characterized by comprising the following components: a paint component, a silver ion antibacterial agent, red phosphorus, antimony oxide, and zinc borate. A silver ion antibacterial agent, a high-efficient red phosphorus flame retardant having a good smoke-suppressing property, an antimony oxide flame retardant auxiliary agent, and a zinc borate flame retardant auxiliary agent are added, and thus the antibacterial property and flame retardant property of the paint are both effectively improved.
Description
Technical field
The invention belongs to chemical technology field, be specifically related to a kind of paint with germ resistance and flame retardancy.
Background technology
Paint is one of indispensable material in Household fit-up and decoration process.Present paint is on the market of a great variety, but these paint majorities just have protection, decoration function, and function ratio is more single.Along with the increase of people to paint functional requirement, existing paint can not meet people's needs, expects to have the paint of new function to occur.
Summary of the invention
The present invention aims to provide a kind of paint with germ resistance and flame retardancy.
Particularly, paint of the present invention is a kind of paint that contains silver ion antimicrobial agent and red phosphorus, it is characterized in that, comprises following component: paint ingredients, silver ion antimicrobial agent, red phosphorus, weisspiessglanz and zinc borate.
Wherein, the mass fraction of each component is preferably: paint ingredients 50-80 part, silver ion antimicrobial agent 2-5 part, red phosphorus 2-10 part, weisspiessglanz 5-10 part and zinc borate 8-15 part, more preferably: paint ingredients 60-75 part, silver ion antimicrobial agent 3-4 part, red phosphorus 5-8 part, weisspiessglanz 7-9 part and zinc borate 10-12 part, be particularly preferably: 11 parts of 70 parts of paint ingredientss, 4 parts of silver ion antimicrobial agents, 7 parts, red phosphorus, 8 parts of weisspiessglanzs and zinc borates.
Fire retardant claims again incombustible agent, flame-proofing agent or fireproofing agent, is a kind of for improving the special auxiliary chemicals of flammable inflammable material combustionproperty, is widely used in the fire-retardant processing of all kinds of finishing materials.Material after fire retardant processing, in the time being subject to extraneous burning things which may cause a fire disaster attack, can effectively stoping, delays or stop flame transmission, thereby reach fire-retardant effect.
Any burning is limited at shorter time institute's liberated heat, if can absorb a part of heat that burning things which may cause a fire disaster is emitted in the shorter time, flame temperature will reduce so, be radiated burning surface and act on the heat that the flammable molecule having gasified is cracked into free radical and will reduce, combustion reactions will obtain inhibition to a certain extent.Under hot conditions, there is strong thermo-negative reaction in fire retardant, absorbs the part heat that burning is emitted, and reduces the temperature on combustiblematerials surface, effectively suppresses the generation of inflammable gas, stops spreading of burning.
Fire retardant mainly comprises inorganic combustion inhibitor, halogenated flame retardant (organic chloride and organic bromide), phosphorus flame retardant (red phosphorus, phosphoric acid ester and halogenated phosphate etc.) and nitrogenated flame retardant etc.Because halogen flame discharges a large amount of cigarettes and toxic gas in the time burning, environment and human health are worked the mischief, therefore,, along with the raising of people to safety and environmental requirement, do not use or use less the halogen flames such as chloride, bromine to become inexorable trend.
Red phosphorus is a kind of well inorganic combustion inhibitor, common retardant synergist in while or red phosphorus/magnesium hydroxide flame retardant system.The flame retarding efficiency of red phosphorus is high, consumption is few, the amount of being fuming is low, toxicity is little, has use range very widely.Especially the good flame retardation effect to oxygen-containing polymers, slightly poor to PE, PP flame retardant of plastic effect, but while using with magnesium hydroxide, red phosphorus combustion inhibitor simultaneously, can produce synergistic effect and play good flame retardant effect.
Explosive shortcoming when common red phosphorus combustion inhibitor has the moisture absorption, easy coloring, frictional impact, develop at present the red phosphorus combustion inhibitor of particle microcapsule coated, it is to make it to become capsule at a red phosphorus particulate outer cladding skim, this capsule can not break adding man-hour, but when material catches fire, discharge fire retardant thereby this tunic but can melt immediately and reach fire-retardant object.Therefore Novel red phosphorus fire retardant has overcome above several shortcomings, and its flame retardant effect and common red phosphorus combustion inhibitor basic identical, microcapsule coated method has also improved the dispersing property of red phosphorus in resin in addition.
Flame retardant effect when weisspiessglanz, zinc borate use is separately not remarkable, in the time being used in conjunction with other fire retardant, can obviously improve flame retardant effect, therefore also has the title of fire retarding synergist or flame retardant.
Antiseptic-germicide is to have antibacterial and material or product bactericidal property.Silver ion antimicrobial agent is the most frequently used antiseptic-germicide, the fine powdered that is white in color, and heat resisting temperature can reach more than 1300 ℃.The Antibacterial Mechanism of silver ion antimicrobial agent: silver ions contact reacts causes the total composition of microorganism to destroy or produce dysfunction.In the time that micro-silver ions arrives microorganism cells film, electronegative because of the latter, rely on coulombic force, both are firmly adsorbed, silver from entering in born of the same parents in penetration cell wall, and with SH radical reaction, make protein coagulating, destroy the activity of cell synthetic enzyme, cell is lost division growth ability and death.Silver ions can also destroy microorganisms electric transmission system, respiratory system and substance delivery system.
The paint ingredients using in the present invention can adopt conventional on the market common paint, the general kind of fancy paint has phenolic paint, alkyd paint, pyroxylin(e)finish, urethane (PU polyester) paint, Polyester Paint, acrylic paint etc. at present, wherein polyurethane paint is that current upholstery uses extensively, one of paint kind that consumption is maximum.
The present invention is applied to silver ion antimicrobial agent and red phosphorus combustion inhibitor and weisspiessglanz, the zinc borate flame retardant efficient, smoke-suppressing is good in paint, has effectively improved germ resistance and the flame resistivity of paint.
Embodiment
Describe the present invention in detail below in conjunction with embodiment; but the following examples are only preferably embodiment of the present invention; protection scope of the present invention is not limited to this; any be familiar with those skilled in the art the present invention disclose technical scope in; be equal to replacement or changed according to technical scheme of the present invention and inventive concept thereof, within all should being encompassed in protection scope of the present invention.
Embodiment 1
After the polyurethane paint of buying on market 50 mass parts, silver ion antimicrobial agent 2 mass parts, red phosphorus 5 mass parts, weisspiessglanz 5 mass parts and zinc borate 10 mass parts are mixed, be painted on wood furniture.After dried coating film, carry out flame resistance test.Result shows, this paint has satisfied flame retardancy.
Embodiment 2
After the polyurethane paint of buying on market 70 mass parts, silver ion antimicrobial agent 4 mass parts, red phosphorus 7 mass parts, weisspiessglanz 8 mass parts and zinc borate 11 mass parts are mixed, be painted on wood furniture.After dried coating film, carry out flame resistance test.Result shows, this paint has satisfied flame retardancy.
Claims (4)
1. a paint that contains silver ion antimicrobial agent and red phosphorus, is characterized in that, comprises following component: paint ingredients, silver ion antimicrobial agent, red phosphorus, weisspiessglanz and zinc borate.
2. paint according to claim 1, is characterized in that, the mass fraction of each component is: paint ingredients 50-80 part, silver ion antimicrobial agent 2-5 part, red phosphorus 2-10 part, weisspiessglanz 5-10 part and zinc borate 8-15 part.
3. paint according to claim 2, is characterized in that, the mass fraction of each component is: paint ingredients 60-75 part, silver ion antimicrobial agent 3-4 part, red phosphorus 5-8 part, weisspiessglanz 7-9 part and zinc borate 10-12 part.
4. paint according to claim 2, is characterized in that, the mass fraction of each component is: 11 parts of 70 parts of paint ingredientss, 4 parts of silver ion antimicrobial agents, 7 parts, red phosphorus, 8 parts of weisspiessglanzs and zinc borates.