CN103839621A - 抗扭曲高柔性电缆 - Google Patents

抗扭曲高柔性电缆 Download PDF

Info

Publication number
CN103839621A
CN103839621A CN201410087293.1A CN201410087293A CN103839621A CN 103839621 A CN103839621 A CN 103839621A CN 201410087293 A CN201410087293 A CN 201410087293A CN 103839621 A CN103839621 A CN 103839621A
Authority
CN
China
Prior art keywords
parts
fine
polyvinyl chloride
high flexibility
cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410087293.1A
Other languages
English (en)
Other versions
CN103839621B (zh
Inventor
孙正兵
何守莉
何峰
蔡元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing South Flame-Resistant Electrical-Wire & Cable Factory
Original Assignee
Chongqing South Flame-Resistant Electrical-Wire & Cable Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing South Flame-Resistant Electrical-Wire & Cable Factory filed Critical Chongqing South Flame-Resistant Electrical-Wire & Cable Factory
Priority to CN201410087293.1A priority Critical patent/CN103839621B/zh
Publication of CN103839621A publication Critical patent/CN103839621A/zh
Application granted granted Critical
Publication of CN103839621B publication Critical patent/CN103839621B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗扭曲高柔性电缆，包括软铜导体、绝缘层、护套层。绝缘层采用新型的PVC/VF高柔性丁晴聚氯乙烯混合物材料，护套层采用新型的PVC/VF高柔性丁晴聚氯乙烯混合物和阻燃材料成分的设计，可使本发明应用在恶劣的户外环境下，具有良好的耐磨、耐腐蚀、耐油、耐气候大气老化性能等：并且在-40℃低温下弯曲可至电缆外径的8倍。

Description

抗扭曲高柔性电缆
技术领域
   本发明涉及电力电缆技术领域，具体涉及一种抗扭曲高柔性软电缆。
背景技术
电缆是电力传输的重要组成部分。由于电缆往往架设在较恶劣的环境中，因此电缆应具有良好的耐低温、耐腐蚀、防油及耐气候大气老化等性能。电缆的绝缘层和护套层对电缆的上述性能起着关键的影响。为了使电缆取得良好的抗扭曲、防油、防寒和耐气候大气老化等性能，护套层和绝缘层应在环境温度下保持高柔性，以减少扭曲时产生的内应力，防止电缆发生结构性破坏。而目前，国内电缆多采用TPU、TPV热塑性材料作为护套层材料，TPU材料价格高昂，做出的产品难以被市场接受；TPV与同类橡胶材料相比，存在耐热性、耐久性、耐磨性、弹回性、阻燃性差的缺点。因此，由于现有电缆绝缘层和护套层选材的局限，使得电缆往往不具有良好的耐扭曲、防油、防寒和耐气候大气老化等性能。
发明内容
本发明提供一种抗扭曲高柔性电缆，以解决现有电缆存在的耐扭曲、防油、防寒、耐气候大气老化等性能较差的问题。
为了解决上述技术问题，本发明采用如下技术方案：
一种抗扭曲高柔性电缆，包括包覆在聚丙烯带内的多根并排设置的软铜导体，每根软铜导体的外部均包覆有隔离层和绝缘层，在所述聚丙烯带外部包覆有护套层，其中，所述的绝缘层采用丁晴聚氯乙烯绝缘材料，所述的护套层采用丁晴聚氯乙烯阻燃护套材料。
其中，丁晴聚氯乙烯绝缘材料按以下重量份数的原料组成：丁晴橡胶40份，PVC树脂58份，氯化聚乙烯CPE28份，聚苯醚PPE37份，丁苯酯28份，碳酸钙10份，细滑石粉30份，氧化锌5份，PE蜡3份，石蜡5份，硬脂酸1份，防老剂RD0.5份，交联剂2份，助交联剂3.5份；
丁晴聚氯乙烯阻燃护套材料按以下重量份数的原料组成：丁晴橡胶50-80份，PVC树脂70-100份，CPE12-30份，PPE18-50份，丁苯酯10-30份，碳酸钙5-10份，细滑石粉8-20份，氧化锌1-8份，石蜡1-8份，防老剂1-5份，交联剂2份，助交联剂3.5份，阻燃剂10-30份。
本发明的有益效果：本发明关键在于所采用的通过配方研发的绝缘层材料和护套层材料，绝缘层采用丁晴聚氯乙烯绝缘材料；护套层采用丁晴聚氯乙烯阻燃护套材料，其抗张强度不小于10.0MPa，断裂伸长率不小于300%，抗撕强度不小于8N/mm，在-40℃下能满足低温性能试验，在-40℃低温下弯曲可至电缆外径的8倍。
综上，本发明抗扭曲高柔性电缆能够保持良好的耐扭曲、防油、防寒和耐气候大气老化性能，并保持较高的柔软度，可保证本电缆使用温度为-40℃-45℃。
附图说明
图1是本发明实施例的结构示意图。
具体实施方式
下面结合附图和具体实施方式对本发明作进一步详细的说明：
实施例一
如图1所示的抗扭曲高柔性电缆，包括包覆在聚丙烯带4内的四根并排设置的软铜导体1，每根软铜导体1的外部均包覆有隔离层2和绝缘层3，在聚丙烯带4外部包覆有护套层5，其中，绝缘层3采用丁晴聚氯乙烯绝缘材料，护套层5采用丁晴聚氯乙烯阻燃护套材料；
本实施例中，丁晴聚氯乙烯绝缘材料按以下重量份数的原料组成：丁晴橡胶40份，PVC树脂58份，氯化聚乙烯CPE28份，聚苯醚PPE37份，丁苯酯28份，碳酸钙10份，细滑石粉30份，氧化锌5份，PE蜡3份，石蜡5份，硬脂酸1份，防老剂RD0.5份，交联剂2份，助交联剂3.5份；
丁晴聚氯乙烯阻燃护套材料按以下重量份数的原料组成：丁晴橡胶50份，PVC树脂70份，CPE12份，PPE18份，丁苯酯10份，碳酸钙5份，细滑石粉8份，氧化锌1份，石蜡1份，防老剂1份，交联剂2份，助交联剂3.5份，阻燃剂10份。
上述交联剂为过氧化二异丙苯DCP，助交联剂为乙基三甲基氯化铵TATC，阻燃剂为无机阻燃剂AL(OH)3。
本电缆通过采用以上配比的绝缘层和护套层，使电缆抗张强度为10.0-16.3MPa，断裂伸长率为300-450%，抗撕强度为8-10N/mm，在-40℃下能满足低温性能试验。本抗扭曲高柔性电缆能够保持良好的耐扭曲、防油、防寒和耐气候大气老化性能，并保持较高的柔软度，可保证本电缆使用温度为-40℃-45℃。
实施例二
本实施例中电缆的结构与实施例一相同，在这里不再赘述，与实施例一不同的是，本实施例中丁晴聚氯乙烯绝缘材料按以下重量份数的原料组成：丁晴橡胶40份，PVC树脂58份，氯化聚乙烯CPE28份，聚苯醚PPE37份，丁苯酯28份，碳酸钙10份，细滑石粉30份，氧化锌5份，PE蜡3份，石蜡5份，硬脂酸1份，防老剂RD0.5份，交联剂2份，助交联剂3.5份；
丁晴聚氯乙烯阻燃护套材料按以下重量份数的原料组成：丁晴橡胶80份，PVC树脂100份，CPE30份，PPE50份，丁苯酯30份，碳酸钙10份，细滑石粉20份，氧化锌8份，石蜡8份，防老剂5份，交联剂2份，助交联剂3.5份，阻燃剂30份。
上述交联剂为过氧化二异丙苯DCP，助交联剂为乙基三甲基氯化铵TATC，阻燃剂为无机阻燃剂AL(OH)3。
本电缆通过采用以上配比的绝缘层和护套层，使电缆抗张强度为11.0-15.7MPa，断裂伸长率为320-480%，抗撕强度为8.6-11N/mm，在-40℃下能满足低温性能试验。本抗扭曲高柔性电缆能够保持良好的耐扭曲、防油、防寒和耐气候大气老化性能，并保持较高的柔软度，可保证本电缆使用温度为-40℃-45℃。

Claims (6)

1.一种抗扭曲高柔性电缆，包括包覆在聚丙烯带内的多根并排设置的软铜导体，每根软铜导体的外部均包覆有隔离层和绝缘层，在所述聚丙烯带外部包覆有护套层，其特征在于，所述的绝缘层采用丁晴聚氯乙烯绝缘材料，所述的护套层采用丁晴聚氯乙烯阻燃护套材料。
2.根据权利要求1所述的抗扭曲高柔性电缆，其特征在于，所述的丁晴聚氯乙烯绝缘材料按以下重量份数的原料组成：丁晴橡胶40份，PVC树脂58份，氯化聚乙烯CPE28份，聚苯醚PPE37份，丁苯酯28份，碳酸钙10份，细滑石粉30份，氧化锌5份，PE蜡3份，石蜡5份，硬脂酸1份，防老剂RD0.5份，交联剂2份，助交联剂3.5份。
3.根据权利要求1所述的抗扭曲高柔性电缆，其特征在于，所述的丁晴聚氯乙烯阻燃护套材料按以下重量份数的原料组成：丁晴橡胶50-80份，PVC树脂70-100份，氯化聚乙烯CPE12-30份，聚苯醚PPE18-50份，丁苯酯10-30份，碳酸钙5-10份，细滑石粉8-20份，氧化锌1-8份，石蜡1-8份，防老剂1-5份，交联剂2份，助交联剂3.5份，阻燃剂10-30份。
4.根据权利要求2或3所述的抗扭曲高柔性电缆，其特征在于，所述的交联剂为过氧化二异丙苯DCP。
5.根据权利要求2或3所述的抗扭曲高柔性电缆，其特征在于，所述的助交联剂为乙基三甲基氯化铵TATC。
6.根据权利要求3所述的抗扭曲高柔性电缆，其特征在于，所述的阻燃剂为无机阻燃剂AL(OH)3。
CN201410087293.1A 2014-03-11 2014-03-11 抗扭曲高柔性电缆 Expired - Fee Related CN103839621B (zh)