CN103834482A - Cleaning solution and cleaning technology using it - Google Patents
Cleaning solution and cleaning technology using it Download PDFInfo
- Publication number
- CN103834482A CN103834482A CN201210480766.5A CN201210480766A CN103834482A CN 103834482 A CN103834482 A CN 103834482A CN 201210480766 A CN201210480766 A CN 201210480766A CN 103834482 A CN103834482 A CN 103834482A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- pure water
- toughened glass
- scavenging solution
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a cleaning solution. The cleaning solution can remove strippable glue on the surface of glass, and comprises 5-20mass% of fatty acid polyoxyethylene ether, 5-20mass% of polyethylene glycol, and the balance pure water. The invention also discloses a cleaning technology using the cleaning solution. The cleaning solution and the cleaning technology can effectively remove residual strippable glue, and enables the surface of the cleaned toughened glass to be bright and clean and have no scratches or watermarks, and can mitigate the labor intensity for removing the strippable glue. The cleaning solution has the advantages of harmlessness to human bodies, less bad smell, non-inflammability and no danger.
Description
Technical field
The present invention relates to a kind ofly for cleaning the scavenging solution of toughened glass surface peelable glue, also relate to the cleaning for cleaning toughened glass surface peelable glue.
Background technology
In general, conventionally use during fabrication cheap, to be easy to manufacture acrylic resin for the display window of the electronic products such as mobile phone.But, touch-screen is installed in recent years on the display window of the electronic products such as mobile phone, use existing acrylic resin can not meet the needs of product innovation, its concrete reason is as follows: 1. acrylic resin is thermo-labile, and is easy to occur cut; 2. the transmittance of display window is lower than the transmittance of glass; 3. in order to make picture distinctness, need to improve brightness, thereby cause battery consumption too much too fast.But but there are not the problems referred to above in toughened glass, is therefore widely used in the manufacture of all touch-screens.But the existing toughened glass course of processing is too complicated, long in time limit, and manual engineering is more, causes its productivity lower, and cost is higher.
The toughened glass manufacturing engineering of prior art is as follows: after former sheet glass warehouse-in, whether check that the raw sheet of warehouse-in is on glass has cut or other foreign matters, be contained under the state on carrier loader at former sheet glass, it is cut and is cut apart, make just tool profile of glass port, its outer casing thickness is in the scope of 0.5 millimeter to 2 millimeters; Use the outside within the scope of 0.5 millimeter to 2 millimeters, glass port right side that sander polishing is split to form by former sheet glass, and removed, on the glass port that completes edging, punch, the hole breaking into is for installing button or camera; The outline of the glass port after edging, processes the engineering of chamfer, polish hole inner face and sharp processing.In addition, the aftertreatment engineerings such as surface finish, washing and thermal treatment tempering are carried out on the two sides of the glass port after sharp processing, thereby complete manufacture and the production of glass port.
According to existing technology, the process in processing for the glass port of touch-screen and portable terminal computer, need to first cut former sheet glass, then cuts apart glass port, next edging flash trimming, and this just makes whole engineering waste a lot of materials, and the duration is lengthened.Meanwhile, there is no a protective membrane due on glass in manufacturing processed, cut, foreign matter and the fingerprint etc. that generate in order to remove glass surface; also need to carry out in addition surface finish; make engineering more loaded down with trivial details, bruting process needs manual processing in addition, thereby causes operating rate and production efficiency to reduce.
Therefore there is the working method at brushing peelable glue on glass: at raw sheet brushing peelable glue on glass; The dry former sheet glass that scribbles peelable glue; By dried former sheet glass according to the certain specification unit of cutting into glass; By unit glass edging or punching, groove processed; Remove described unit peelable glue on glass; Described in tempering, remove the unit glass after peelable glue; Wash the unit glass after unit glass and the described washing of check after described tempering; Peelable glue is by gel in drying stage, and the peelable glue of gel, removing photoresist in layer stage, is peeled off from unit is on glass because the solution that removes photoresist makes peelable glue, and removes.Normally used peelable glue comprises 80%~90% epoxy resin by its weight percent meter, 10%~20% pigment, additive and solvent.
Summary of the invention
The invention provides a kind of scavenging solution, this scavenging solution can be removed the peelable glue of glass surface, and its moiety is: the aliphatic acid polyethenoxy ether that mass percent is 5-20%, the polyoxyethylene glycol of 5-20% and the pure water of surplus.
The moiety of scavenging solution is preferably the aliphatic acid polyethenoxy ether of 8-15%, the polyoxyethylene glycol of 8-15% and the pure water of surplus.
The moiety of scavenging solution is 10% aliphatic acid polyethenoxy ether more preferably, 10% polyoxyethylene glycol and the pure water of surplus.
The moiety of scavenging solution is 12% aliphatic acid polyethenoxy ether more preferably, 12% polyoxyethylene glycol and the pure water of surplus.
The present invention also provides a kind of cleaning that uses aforementioned scavenging solution, comprises the following steps:, by put into the rinse bath that aforementioned scavenging solution is housed with the toughened glass of peelable glue, at 50-60 ℃ of temperature, to clean 5 minutes; It is that the rinse bath that pure water is housed of 55-65 ℃ cleans that the toughened glass cleaning through scavenging solution is put into temperature; To spray by pure water spray groove through the toughened glass cleaning; By the toughened glass through pure water spray by following temperature: 50-55 ℃, 55-65 ℃, 60-70 ℃, 65-75 ℃ are equipped with cleaning in the rinse bath of pure water; To be 70-80 ℃ of slow kerve by temperature through cleaned toughened glass, toughened glass is dried by ultraviolet ray.
In aforementioned cleaning, rinse bath is in swinging condition, so that scavenging solution and pure water complete the cleaning to toughened glass.
In aforementioned cleaning, when toughened glass enters water, water resistance value is greater than 12M Ω.
The invention has the beneficial effects as follows: scavenging solution of the present invention can effectively be removed remaining peelable glue, make toughened glass any surface finish, no marking, watermark after cleaning, alleviated the labour intensity of removing peelable glue.This scavenging solution is harmless, and unpleasant odor is little, nonflammable, without dangerous.
The peelable glue that adopts above-mentioned cleaning to clean toughened glass surface effectively stops toughened glass surface to occur cut, watermark, reduce the disqualification rate of product, production efficiency and product quality are improved, simultaneously without polishing for removing cut, shortened man-hour, reduce production cost, saved starting material.
Embodiment
The first embodiment
The moiety of scavenging solution is 10% aliphatic acid polyethenoxy ether, 10% polyoxyethylene glycol and the pure water of surplus.At 40 ℃, prepare the scavenging solution of mentioned component, seal stand-by.
Just put into the toughened glass of peelable glue the rinse bath that aforementioned scavenging solution is housed, at 55 ℃ of temperature, clean 5 minutes; It is that the rinse bath that pure water is housed of 60 ℃ cleans that the toughened glass cleaning through scavenging solution is put into temperature; To spray by pure water spray groove through the toughened glass cleaning; By the toughened glass through pure water spray by following temperature: cleaning in 55 ℃, 60 ℃, 65 ℃, the 70 ℃ rinse baths that pure water is housed; To be 75 ℃ of slow kerves by temperature through cleaned toughened glass, toughened glass is dried by ultraviolet ray.
The second embodiment
The moiety of scavenging solution is 12% aliphatic acid polyethenoxy ether, 12% polyoxyethylene glycol and the pure water of surplus.Prepare at normal temperatures the scavenging solution of mentioned component, seal stand-by.
Just put into the toughened glass of peelable glue the rinse bath that aforementioned scavenging solution is housed, at 60 ℃ of temperature, clean 5 minutes; It is that the rinse bath that pure water is housed of 65 ℃ cleans that the toughened glass cleaning through scavenging solution is put into temperature; To spray by pure water spray groove through the toughened glass cleaning; By the toughened glass through pure water spray by following temperature: cleaning in 60 ℃, 65 ℃, 70 ℃, the 75 ℃ rinse baths that pure water is housed; To be 80 ℃ of slow kerves by temperature through cleaned toughened glass, toughened glass is dried by ultraviolet ray.
The toughened glass peelable glue scavenging solution of the invention described above and washing lotion technique, thus can be used for carrying out mechanical workout and need to before processing, apply glass surface the toughened glass of peelable glue.
Above content is in conjunction with concrete optimal technical scheme further description made for the present invention, can not assert that specific embodiment of the invention is confined to these explanations.For general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deduction or replace, all should be considered as belonging to protection scope of the present invention.
Claims (7)
1. a scavenging solution, this scavenging solution can be removed the peelable glue of glass surface, it is characterized in that its moiety is: the aliphatic acid polyethenoxy ether that mass percent is 5-20%, the polyoxyethylene glycol of 5-20% and the pure water of surplus.
2. according to the scavenging solution of claim 1, it is characterized in that moiety is preferably the aliphatic acid polyethenoxy ether of 8-15%, the polyoxyethylene glycol of 8-15% and the pure water of surplus.
3. according to the scavenging solution of claim 2, it is characterized in that moiety more preferably 10% aliphatic acid polyethenoxy ether, 10% polyoxyethylene glycol and the pure water of surplus.
4. according to the scavenging solution of claim 2, it is characterized in that moiety more preferably 12% aliphatic acid polyethenoxy ether, 12% polyoxyethylene glycol and the pure water of surplus.
5. right to use requires a cleaning for the scavenging solution of 1-4, it is characterized in that comprising the following steps:, by put into the rinse bath that aforementioned scavenging solution is housed with the toughened glass of peelable glue, at 50-60 ℃ of temperature, cleaning 5 minutes; It is that the rinse bath that pure water is housed of 55-65 ℃ cleans that the toughened glass cleaning through scavenging solution is put into temperature; To spray by pure water spray groove through the toughened glass cleaning; By the toughened glass through pure water spray by following temperature: 50-55 ℃, 55-65 ℃, 60-70 ℃, 65-75 ℃ are equipped with cleaning in the rinse bath of pure water; To be 70-80 ℃ of slow kerve by temperature through cleaned toughened glass, toughened glass is dried by ultraviolet ray.
6. according to the cleaning of claim 5, rinse bath is in swinging condition, so that scavenging solution and pure water complete the cleaning to toughened glass.
7. according to the cleaning of claim 5, when toughened glass enters water, water resistance value is greater than 12M Ω.