CN103819131A - Diatomite floor and production method thereof - Google Patents
Diatomite floor and production method thereof Download PDFInfo
- Publication number
- CN103819131A CN103819131A CN201310724456.8A CN201310724456A CN103819131A CN 103819131 A CN103819131 A CN 103819131A CN 201310724456 A CN201310724456 A CN 201310724456A CN 103819131 A CN103819131 A CN 103819131A
- Authority
- CN
- China
- Prior art keywords
- diatomite
- floor
- making method
- production method
- diatomite floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a diatomite floor and a production method thereof. The diatomite floor is characterized in that the diatomite floor comprises the following components in percentage by weight: 150kg of diatomite, 100kg of PVC (Polyvinyl Chloride) material, 20kg of reinforcing agent CPE, 2kg of epoxidized soybean oil as a flow aid, 8kg of calcium stearate as a stabilizer and 10kg of K-123 as a processing aid. The production method of the diatomite floor comprises the preparing steps: die temperature increase, feeding, sizing, cutting, double-sided strickling, four-sided notching and UV (Ultraviolet) painting. The diatomite floor and the production method thereof have the advantages that firstly, by means of the UV painting, a painted surface is enabled to resist the scratching and the scribing and the long service life is ensured; secondly, the diatomite floor is produced by adopting a high-temperature polymerization one-time forming process, in addition to natural characteristics of diatomite, so that products resist dampness, mildew and burst, and the damage from insects can be effectively prevented; thirdly, no any glue is added in the production process of the diatomite floor, so that harmful substances such as formaldehyde, benzene and lead are eliminated and secondary pollution to bedrooms is avoided.
Description
Technical field
The invention belongs to interior decoration field, be specifically related to a kind of diatomite floor.
Background technology
Diatomite floor is a kind of take one-level diatomite, PVC as floor base material, through the one-time formed environmental protection of high temperature extrusion polymerization floor.
For example, application number is 201210585154.2 invention, a kind of production formula and preparation method of functional diatom ooze finishing material are disclosed, the present invention includes to be equipped with containing 60%～70% silicon-dioxide diatomite breeze and dry prepared diatomite breeze and quartz sand, nano titanium oxide, cohesiveness fillers etc., add formula materials to tell dispersion machine stir and high temperature five machine pigment are mixed and make required color diatom ooze with white diatom ooze powder.Product price of the present invention is cheap, and production cost is only 1/3 of other diatom ooze device materials, and product meets correlated quality standard.The technical problem of required solution is to provide a kind of inexpensive and can effectively remove airborne objectionable impurities and adjustable air humidity, sound insulation and noise reduction, fire protection flame retarding and diatom ooze finishing material production formula and the preparation method of several functions such as destatic.
But the disclosed technical scheme of foregoing invention can not solve shorter technical problem in existing diatom ooze floor work-ing life.
Summary of the invention
The technical problem to be solved in the present invention is to extend the work-ing life on diatom ooze floor.
For solving the problems of the technologies described above, the invention discloses a kind of diatom ooze floor and preparation method thereof, the composition on described diatomite floor is fire retardant diatomite, polymer PVC material, strengthening agent CPE material, glidant epoxy soybean oil, stablizer calcium stearate, Zinic stearas and processing aid K-123.
Further, the ratio of each composition on described diatomite floor is described diatomite 150kg, described polymer PVC material 100kg, described strengthening agent CPE20kg, described glidant epoxy soybean oil 2kg, described stablizer calcium stearate 8kg and described processing aid K-12310kg.
Further, the step order of described making method is that mould heats up, feed intake, and sizing, cutting, sands flat, fluting, japanning.
Further, described mould is warming up to 165 degrees Celsius.
Further, described in, sand flat as two-sided and sand flat.
Further, described fluting is four sides fluting.
Further, described japanning is UV japanning.
Compared to the prior art, its advantage is on a kind of diatomite of the present invention floor and preparation method thereof: the first, and by UV japanning, make lacquer painting anti-scratch, anti-zoned, guarantee long perfomance life.The second, described diatomite floor adopts high temperature polymerization one-time formed technique, diatomaceous natural characteristic in addition, and product is not afraid of tide, is not gone mouldy, not explosion and can effectively prevent from damaging by worms.The 3rd, any glue class is not added on described diatomite floor in process of production, therefore, not containing objectionable impuritiess such as formaldehyde, benzene, lead, can not produce secondary pollution to room.The 4th, described diatomite floor has advantages of fire protection flame retarding, insulation.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the present invention will be further described.
Fig. 1 is the making method process module figure on a kind of diatom ooze of the present invention floor and preparation method thereof.
Embodiment
For making the technical problem to be solved in the present invention, technical scheme and advantage clearer, further illustrate specific embodiments of the invention.
The invention discloses a kind of diatom ooze floor and preparation method thereof, the ratio of each composition on described diatomite floor is described diatomite 150kg, described polymer PVC material 100kg, described strengthening agent CPE20kg, described glidant epoxy soybean oil 2kg, described stablizer calcium stearate 8kg and described processing aid K-12310kg.
The making method on described diatomite floor, the step order of described making method is that mould is warming up to 165 degrees Celsius, feeds intake, sizing, cutting, two-sided sanding flat, four sides fluting and UV japanning.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of principle of the present invention and spirit; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (7)
1. a diatomite floor, is characterized in that, the composition on described diatomite floor is fire retardant diatomite, polymer PVC material, strengthening agent CPE material, glidant epoxy soybean oil, stablizer calcium stearate, Zinic stearas and processing aid K-123.
2. the making method on diatomite according to claim 1 floor, it is characterized in that, the ratio of each composition on described diatomite floor is described diatomite 150kg, described polymer PVC material 100kg, described strengthening agent CPE20kg, described glidant epoxy soybean oil 2kg, described stablizer calcium stearate 8kg and described processing aid K-12310kg.
3. the making method on diatomite according to claim 1 floor, is characterized in that, the step order of described making method is that mould heats up, feed intake, and sizing, cutting, sands flat, fluting, japanning.
4. the making method on diatomite according to claim 3 floor, is characterized in that, described mould is warming up to 165 degrees Celsius.
5. the making method on diatomite according to claim 4 floor, is characterized in that, described in sand flat as two-sided and sand flat.
6. the making method on diatomite according to claim 5 floor, is characterized in that, described fluting is four sides fluting.
7. the making method on diatomite according to claim 6 floor, is characterized in that, described japanning is UV japanning.