CN103818092B - A kind of production method of splash guard - Google Patents
A kind of production method of splash guard Download PDFInfo
- Publication number
- CN103818092B CN103818092B CN201310754837.0A CN201310754837A CN103818092B CN 103818092 B CN103818092 B CN 103818092B CN 201310754837 A CN201310754837 A CN 201310754837A CN 103818092 B CN103818092 B CN 103818092B
- Authority
- CN
- China
- Prior art keywords
- slab
- area
- fiberboard
- splash guard
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of production method of splash guard, comprise the following steps, first baffle plate is layered on fiberboard, polyvinyl acetate particle is sprayed into the second area of fiberboard by spray regime, above-mentioned fiberboard is sent into hot press and carry out hot pressing formation slab, after slab cooling, by the mode of drenching glue, phenolic resin glue is evenly drenched on slab is two-sided, slab is put into hot press and carries out hot-press gluing, adopt pulley type gluing method, melamine glue is coated at the double-faced uniform of slab, fast at least one deck melamine-impregnated bond paper is all sticked on the two sides of the slab after gluing, form water-proof sheet material, splash guard of the present invention is arranged by fixed position in edges of boards and plate and adds waterproof material, make user can according to size needs, cut randomly sheet material, also can ensure that blank perimeter can waterproof, and splash guard of the present invention maintains enough MORs and elastic modelling quantity.
Description
Technical field
The present invention relates to splash guard manufacturing technology field, particularly relate to a kind of production method of splash guard.
Background technology
The bath lavatory compartment of the locker of bath center, kitchen tools table top, dining table, desk, door leaf and public space, wash platform, reception counters, article placing cabinet, ceiling, desk and office cubicles etc. easily contact the place of water, the easy imbibition of common sheet material, causes sheet deformation to be bubbled.Therefore, should use water-proof sheet material in this place, common water-proof sheet material has melamine plate etc.
Melamine-impregnated bond paper is mated formation on particieboard, moist-proof board, medium density fibre board (MDF) or hardboard surface by melamine plate of the prior art, forms through hot pressing, and the surface after only having film paper to cover can waterproof.
In actual use, the surrounding of sheet material is also the position easily contacting water, can expand the softening phenomenon such as mouldy of bubbling of cracking, destroy attractive in appearance and reduce service life after the water suction of the periphery of sheet material.
The waterproof type of prior art to sheet material surrounding pastes layer protecting film.
But sheet material in use, due to the requirement of size, often can only use a part for sheet material, and the part play of oversize will be fallen, and play fall after the part of sheet material pasting protective film also fallen by play, expose plate core segment, very easily absorb water.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of production method of splash guard, and described production method comprises the steps:
Palm bark is cleaned, silt impurity is wherein cleaned up,
The palm bark cleaned up is put into jet drier and carries out drying, temperature controls at 50-60 DEG C, and drying time is 10 minutes, and relative air humidity is 15%-18%, and hot-air jet velocity controls at 13 meter per seconds,
At normal temperatures palm bark is rubbed by mechanical rubbing way, after making the corticole fiber opening of palm, becomes puffy,
Being spread out in an interleaved manner by palm bark after process paves in a mold, makes to interlock up and down and between the bark fiber of left and right,
With the quick roll-in of roll squeezer once, the fiberboard thickness after roll-in is 2.5-3cm, keeps puffy between bark fiber,
Be layered on fiberboard by the first baffle plate, fiberboard be distinguished into first area and second area, described first baffle plate covers described first area,
Be the polyvinyl acetate particle of 200 ~ 500 μm sprays into fiberboard second area by spray regime by diameter, make second area fill full polyvinyl acetate particle,
First baffle plate is removed, the second area second baffle of filling full polyvinyl acetate particle is covered,
Epoxy powder is spurted into the first area of fiberboard, described epoxy powder granular size is 100-150 μm,
Second baffle is removed,
Above-mentioned fiberboard is sent into hot press under the temperature conditions of 90-120 DEG C, carries out hot pressing formation slab,
After slab cooling, by the mode of drenching glue, phenolic resin glue is evenly drenched on slab is two-sided,
Slab is put into hot press and carries out hot-press gluing, hot pressing temperature is 120-130 DEG C, and the time is 30 seconds, and pressure is 20-25 handkerchief,
Slab is cooled naturally,
Adopt pulley type gluing method, evenly coat melamine glue on the two sides of slab,
Fast at least one deck melamine-impregnated bond paper is all sticked on the two sides of the slab after gluing,
After gelling is solid, carry out cutting edge process, shaping.
Preferably, described first area is four peripheries of plate, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm and and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
Preferably, with first area described in color mark.
The invention has the beneficial effects as follows: the production method of splash guard of the present invention, arranged by fixed position in edges of boards and plate and add waterproof material, make user can according to size needs, cut randomly sheet material, also can ensure that blank perimeter can waterproof, and splash guard of the present invention maintains enough MORs and elastic modelling quantity.
Detailed description of the invention
By describing technology contents of the present invention, structural feature in detail, being realized object and effect, be explained in detail below in conjunction with embodiment.
The production method of splash guard provided by the invention, described production method comprises the steps:
Palm bark is cleaned, silt impurity is wherein cleaned up,
The palm bark cleaned up is put into jet drier and carries out drying, temperature controls at 50-60 DEG C, and drying time is 10 minutes, and relative air humidity is 15%-18%, and hot-air jet velocity controls at 13 meter per seconds,
At normal temperatures palm bark is rubbed by mechanical rubbing way, after making the corticole fiber opening of palm, becomes puffy,
Being spread out in an interleaved manner by palm bark after process paves in a mold, makes to interlock up and down and between the bark fiber of left and right,
With the quick roll-in of roll squeezer once, the fiberboard thickness after roll-in is 2.5-3cm, keeps puffy between bark fiber,
Be layered on fiberboard by the first baffle plate, fiberboard be distinguished into first area and second area, described first baffle plate covers described first area,
Be the polyvinyl acetate particle of 200 ~ 500 μm sprays into fiberboard second area by spray regime by diameter, make second area fill full polyvinyl acetate particle,
First baffle plate is removed, the second area second baffle of filling full polyvinyl acetate particle is covered,
Epoxy powder is spurted into the first area of fiberboard, described epoxy powder granular size is 100-150 μm,
Second baffle is removed,
Above-mentioned fiberboard is sent into hot press under the temperature conditions of 90-120 DEG C, carries out hot pressing formation slab,
After slab cooling, by the mode of drenching glue, phenolic resin glue is evenly drenched on slab is two-sided,
Slab is put into hot press and carries out hot-press gluing, hot pressing temperature is 120-130 DEG C, and the time is 30 seconds, and pressure is 20-25 handkerchief,
Slab is cooled naturally,
Adopt pulley type gluing method, evenly coat melamine glue on the two sides of slab,
Fast at least one deck melamine-impregnated bond paper is all sticked on the two sides of the slab after gluing,
After gelling is solid, carry out cutting edge process, shaping.
Described first area is four peripheries of plate, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
Preferably, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm and and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
Preferably, with first area described in color mark, to cut time easy to use.
The production method of splash guard of the present invention, arranged by fixed position in edges of boards and plate and add waterproof material, make user can according to size needs, cut randomly sheet material, also can ensure that blank perimeter can waterproof, and splash guard of the present invention maintains enough MORs and elastic modelling quantity.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or the conversion of equivalent flow process, or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (6)
1. a production method for splash guard, is characterized in that, described production method comprises the steps:
Palm bark is cleaned, silt impurity is wherein cleaned up,
The palm bark cleaned up is put into jet drier and carries out drying, temperature controls at 50-60 DEG C, and drying time is 10 minutes, and relative air humidity is 15%-18%, and hot-air jet velocity controls at 13 meter per seconds,
At normal temperatures palm bark is rubbed by mechanical rubbing way, after making the corticole fiber opening of palm, becomes puffy,
Being spread out in an interleaved manner by palm bark after process paves in a mold, makes to interlock up and down and between the bark fiber of left and right,
With the quick roll-in of roll squeezer once, the fiberboard thickness after roll-in is 2.5-3cm, keeps puffy between bark fiber,
Be layered on fiberboard by the first baffle plate, fiberboard be distinguished into first area and second area, described first baffle plate covers described first area,
Be the polyvinyl acetate particle of 200 ~ 500 μm sprays into fiberboard second area by spray regime by diameter, make second area fill full polyvinyl acetate particle,
First baffle plate is removed, the second area second baffle of filling full polyvinyl acetate particle is covered,
Epoxy powder is spurted into the first area of fiberboard, described epoxy powder granular size is 100-150 μm,
Second baffle is removed,
Above-mentioned fiberboard is sent into hot press under the temperature conditions of 90-120 DEG C, carries out hot pressing formation slab,
After slab cooling, by the mode of drenching glue, phenolic resin glue is evenly drenched on slab is two-sided,
Slab is put into hot press and carries out hot-press gluing, hot pressing temperature is 120-130 DEG C, and the time is 30 seconds, and pressure is 20-25 kPa,
Slab is cooled naturally,
Adopt pulley type gluing method, evenly coat melamine glue on the two sides of slab,
Fast at least one deck melamine-impregnated bond paper is all sticked on the two sides of the slab after gluing,
After gelling is solid, carry out cutting edge process, shaping.
2. the production method of splash guard according to claim 1, is characterized in that, described first area is four peripheries of plate, and width is the region of 5-10cm.
3. the production method of splash guard according to claim 2, is characterized in that, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm.
4. the production method of splash guard according to claim 2, is characterized in that, described first area also comprises and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
5. the production method of splash guard according to claim 2, is characterized in that, described first area also comprises and spaced set parallel below with upper, and width is the region of 5-10cm and and spaced set parallel with limit, left and right, and width is the region of 5-10cm.
6. the production method of splash guard according to any one of claim 1 to 5, is characterized in that, with first area described in color mark.