CN103817318A - 一种连铸高锰、高氧钢用塞棒身 - Google Patents

一种连铸高锰、高氧钢用塞棒身 Download PDF

Info

Publication number
CN103817318A
CN103817318A CN201410061043.0A CN201410061043A CN103817318A CN 103817318 A CN103817318 A CN 103817318A CN 201410061043 A CN201410061043 A CN 201410061043A CN 103817318 A CN103817318 A CN 103817318A
Authority
CN
China
Prior art keywords
continuous casting
stopper body
orders
oxygen steel
granularity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410061043.0A
Other languages
English (en)
Inventor
吴建湘
黄亚平
蒋永明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Safe Auspicious Fire-Resistant Co Ltd In Jiangsu
Original Assignee
Safe Auspicious Fire-Resistant Co Ltd In Jiangsu
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Safe Auspicious Fire-Resistant Co Ltd In Jiangsu filed Critical Safe Auspicious Fire-Resistant Co Ltd In Jiangsu
Priority to CN201410061043.0A priority Critical patent/CN103817318A/zh
Publication of CN103817318A publication Critical patent/CN103817318A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种连铸高锰、高氧钢用塞棒身，包括以下质量百分比的原料：碳耐火材料回收料50%~70%，鳞片石墨10%~20%，熔融石英5%~15%，α氧化铝微粉5%~15%，金属硅粉1%~5%，酚醛树脂5%~15%。棒身材料以含碳耐火材料回收料、炭素、氧化铝及熔融石英为主，极大地降低了产品制造成本。

Description

一种连铸高锰、高氧钢用塞棒身
技术领域
    本发明涉及耐火材料领域，具体是一种连铸高锰、高氧钢用塞棒身。
背景技术
随着钢铁工业的不断发展，国内外耐火材料行业也得到了长足的进步。铝碳耐火材料是上世纪80年代左右开始兴起的一种新型耐火材料。最初主要应用于钢包砖方面，后来逐渐地推广向连铸中间包方面。为钢铁行业连铸技术的飞速发展提供了不可或缺的技术支持。
连铸用铝碳耐火材料俗称为连铸三大件，主要由长水口、整体塞棒、浸入式水口组成。整体塞棒作为连铸三大件产品之一，在连铸过程中起到控流、截流等作用，其重要性不言而喻，可以说是保障连铸过程顺利进行的主要功能元件。
作为铝碳功能材料之一，整体塞棒材料设计一般都以Al2O3-C材料为主，由于对棒身使用要求相对较低，在不影响塞棒整体使用寿命的前提下，棒身也使用Al2O3-C材料造成了材料的浪费。
发明内容
本发明为了解决现有技术的问题，提供了一种耐高温的连铸高锰、高氧钢用塞棒身，降低了成本。
本发明包括以下质量百分比的原料：碳耐火材料回收料50%~70%，鳞片石墨10%~20%，熔融石英5%~15%，α氧化铝微粉5%~15%，金属硅粉1%~5%，液态酚醛树脂5%~15%。
所述液态酚醛树脂求在温度在20℃一下，粘度不低于400Pa。
所述的金属硅粉纯度在98%以上，粒度为200目，两种原料重量比为2：1。
所述的含碳耐火材料回收料为铝碳耐火材料废砖加工而成，粒度为24目、36目、80目、180目，以上四种重量比为2：2：1：2。
所述的鳞片石墨粒度为-100目，含量在95%以上；
所述熔融石英粒度为0.5~0.2mm、0.2~0mm。两种原料重量比为2：1；
所述α氧化铝微粉粒度为10μm以下，纯度在99%以上。
本发明有益效果在于：棒身采用含碳耐火材料回收料，制作成本比原有Al2O3-C质整体塞棒显著降低。
具体实施方式
本发明提供的棒身材料的原料组成为：含碳耐火材料回收料50%~70%，鳞片石墨10%~20%，熔融石英5%~15%，α氧化铝微粉5%~15%，金属硅粉1%~5%，酚醛树脂5%~15%。
所述的含碳耐火材料回收料为铝碳耐火材料废砖加工而成，粒度为24#、36#、80#、180目。以上四种重量比为2：2：1：2；
所述的鳞片石墨粒度为-100目，含量在95%以上；
所述的熔融石英粒度为0.5~0.2mm、0.2~0mm。两种原料重量比为2：1；
所述的α氧化铝微粉粒度为10μm以下，纯度在99%以上；
所述液态酚醛树脂求在温度在20℃一下，粘度不低于400Pa。所述的金属硅粉纯度在98%以上，粒度为200目，两种原料重量比为2：1。
该整体塞棒的制作方式如下：
将配制好的棒身材料放入混料机内混制均匀，然后将混制好的原料投入橡胶模具内，封口后在等静压机内压制成型，压力为120MPa。成型好的产品经烘干、烧成、加工，喷涂等工序后，即可包装发货。
下面通过具体实施例对本发明作进一步说明。
实施例1
一种连铸用整体塞棒身，棒身料采用如下原料配比：含碳耐火材料回收料：200kg，鳞片石墨：60kg，熔融石英：60kg，α氧化铝微粉：28kg，金属硅粉：12kg，酚醛树脂（液体）40kg。
各种原料均按所需粒度进行配比，含碳耐火材料回收料粒度为24目、36目、80目、180目，以上四种重量比为2：2：1：2；熔融石英粒度为0.5~0.2mm、0.2~0mm，两种原料重量比为2：1。
按照上述方案制作整体塞棒，制作成本比原有Al2O3-C质整体塞棒降低了25%。
实施例2
一种连铸用整体塞棒身，棒身料采用如下原料配比：含碳耐火材料回收料：225kg，鳞片石墨：55kg，熔融石英：50kg，α氧化铝微粉：20kg，金属硅粉：12kg，酚醛树脂（液体）38kg。
各种原料均按所需粒度进行配比，含碳耐火材料回收料粒度为24目、36目、80目、180目，以上四种重量比为2：2：1：2；熔融石英粒度为0.5~0.2mm、0.2~0mm，两种原料重量比为2：1。
按照上述方案制作整体塞棒，制作成本比原有Al2O3-C质整体塞棒降低了27.5%。
实施例3 
一种连铸用整体塞棒身，棒身料采用如下原料配比：含碳耐火材料回收料：225kg，鳞片石墨：55kg，熔融石英：50kg，α氧化铝微粉：20kg，金属硅粉：12kg，酚醛树脂（液体）38kg。
各种原料均按所需粒度进行配比，含碳耐火材料回收料粒度为24目、36目、80目、180目，以上四种重量比为2：2：1：2；熔融石英粒度为0.5~0.2mm、0.2~0mm，两种原料重量比为2：1。
按照上述方案制作整体塞棒，制作成本比原有Al2O3-C质整体塞棒降低了25%。
本发明具体应用途径很多，以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进，这些改进也应视为本发明的保护范围。

Claims (7)

1.一种连铸高锰、高氧钢用塞棒身，其特征在于包括以下质量百分比的原料：碳耐火材料回收料50%~70%，鳞片石墨10%~20%，熔融石英5%~15%，α氧化铝微粉5%~15%，金属硅粉1%~5%，液态酚醛树脂5%~15%。
2.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述液态酚醛树脂求在温度在20℃一下，粘度不低于400Pa。
3.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述的金属硅粉纯度在98%以上，粒度为200目，两种原料重量比为2：1。
4.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述的含碳耐火材料回收料为铝碳耐火材料废砖加工而成，粒度为24目、36目、80目、180目，以上四种重量比为2：2：1：2。
5.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述的鳞片石墨粒度为-100目，含量在95%以上。
6.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述熔融石英粒度为0.5~0.2mm、0.2~0mm，两种原料重量比为2：1。
7.根据权利要求1所述的连铸高锰、高氧钢用塞棒身，其特征在于：所述α氧化铝微粉粒度为10μm以下，纯度在99%以上。
CN201410061043.0A 2014-02-24 2014-02-24 一种连铸高锰、高氧钢用塞棒身 Pending CN103817318A (zh)