CN103788431A - 一种无卤素橡塑发泡保温材料 - Google Patents

一种无卤素橡塑发泡保温材料 Download PDF

Info

Publication number
CN103788431A
CN103788431A CN201410017108.1A CN201410017108A CN103788431A CN 103788431 A CN103788431 A CN 103788431A CN 201410017108 A CN201410017108 A CN 201410017108A CN 103788431 A CN103788431 A CN 103788431A
Authority
CN
China
Prior art keywords
halogen
rubber
percent
agent
lagging material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410017108.1A
Other languages
English (en)
Other versions
CN103788431B (zh
Inventor
彭东保
雷红伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Du Kenxin materials (Wuhan) group Limited by Share Ltd
Original Assignee
DURKEE WUHAN INSULATION MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DURKEE WUHAN INSULATION MATERIAL Co Ltd filed Critical DURKEE WUHAN INSULATION MATERIAL Co Ltd
Priority to CN201410017108.1A priority Critical patent/CN103788431B/zh
Publication of CN103788431A publication Critical patent/CN103788431A/zh
Application granted granted Critical
Publication of CN103788431B publication Critical patent/CN103788431B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种无卤素橡塑发泡保温材料，涉及橡塑发泡保温材料领域，本发明的产品以重量百分比计，组分包括NBR13～30%，EVA13～30%，无卤阻燃剂24～40%，无卤增塑剂14～20%，发泡剂12～20%，填充剂2～25%，防老剂0.3～2%。本发明的目的在于提供一种无卤素橡塑发泡保温材料，其燃烧释放的有毒气体少，对人体的伤害小。

Description

一种无卤素橡塑发泡保温材料
技术领域
本发明涉及橡塑发泡保温材料领域，尤其涉及一种无卤素橡塑发泡保温材料。 
背景技术
近年来的火灾事故中，超过死亡数80%的人员致死原因与建筑材料燃烧产生的浓烟和毒气有关。随着越来越多的公共场所、大型建筑物投入使用，建筑物的防火以及燃烧时对人体的影响受到广泛重视。然而，传统的建筑材料中保温材料使用的是NBR/PVC体系橡塑发泡保温材料，其配方体系中含有PVC、氯化石蜡等含卤原料，当火灾发生时，其燃烧放出大量的有毒烟雾和腐蚀性卤酸，造成的人员伤亡远远大于火灾本身。 
发明内容
针对现有技术中存在的缺陷，本发明的目的在于提供一种无卤素橡塑发泡保温材料，其燃烧释放的有毒气体少，对人体的伤害小。 
为达到以上目的，本发明采取的技术方案是：一种无卤素橡塑发泡保温材料，以重量百分比计，包括如下组分： 
Figure DEST_PATH_GDA0000480043080000011
Figure DEST_PATH_GDA0000480043080000021
在上述技术方案的基础上，所述无卤阻燃剂为氢氧化铝，或氢氧化铝和氢氧化镁的混合物。 
在上述技术方案的基础上，所述无卤增塑剂为磷酸酯类增塑剂。 
在上述技术方案的基础上，所述无卤素增塑剂为磷酸三甲苯酯。 
在上述技术方案的基础上，所述发泡剂为偶氮二甲酰胺。 
在上述技术方案的基础上，填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物。 
在上述技术方案的基础上，防老剂为防老剂MB、防老剂DNP中的一种或两种的混合物。 
本发明的有益效果在于： 
1、本发明无卤素橡塑发泡保温材料，以NBR/EVA为主体材料，配合无卤阻燃剂、无卤发泡剂、增塑剂、填充剂、防老剂等，共同构成了本发明的配方体系，添加阻燃剂，其阻燃性较好。 
2、本发明的配方体系中不含卤素，其在燃烧时不会产生卤化氢气体，大大减少了保温材料燃烧造成的人员伤亡。 
具体实施方式
一种无卤素橡塑发泡保温材料，以重量百分比计，包括如下组分： 
Figure DEST_PATH_GDA0000480043080000022
其中，主体材料为NBR（丁腈橡胶）和EVA（乙烯-醋酸乙烯共聚物）；无卤阻燃剂为氢氧化铝和氢氧化镁的混合物或氢氧化铝；无卤增塑剂为磷酸酯类增塑剂，优选的无卤素增塑剂为磷酸三甲苯酯，其不含卤素，取代传统的氯化石蜡增塑剂，起到阻燃和增塑双重作用；发泡剂为偶氮二甲酰胺；填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物；防老剂为防老剂MB、防老剂DNP中的一种或两种的混合物。 
以下结合实施例对本发明作进一步详细说明。 
实施例1： 
一种无卤素橡塑发泡保温材料，包括以下组分： 
主体材料：NBR15kg、EVA13kg； 
无卤阻燃剂：氢氧化铝24kg； 
无卤增塑剂：磷酸三甲苯酯14kg； 
发泡剂：偶氮二甲酰胺12kg； 
填充剂：滑石粉11kg、陶土7kg、碳酸钙3.7kg； 
防老剂：防老剂MB0.3kg。 
本实施例无卤素橡塑发泡保温材料的制备方法：取上述组分原料，投入75L密炼机进行混炼，生成混炼胶；混炼胶经切片加入挤出机压出成型；成型产品输送进热空气烘箱进行硫化发泡；再经过冷却裁切制得最终成品。 
实施例2： 
一种无卤素橡塑发泡保温材料，包括以下组分： 
主体材料：NBR13kg、EVA13kg； 
无卤阻燃剂：氢氧化铝25kg、氢氧化镁14kg； 
无卤增塑剂：磷酸三甲苯酯20kg； 
发泡剂：偶氮二甲酰胺12kg； 
填充剂：滑石粉2.1kg； 
防老剂：防老剂MB0.6kg、防老剂DNP0.3kg。 
本实施例中，按上述组分称取原料，按实施例1的制备方法制得本实施例的无卤素橡塑发泡保温材料。 
实施例3： 
主体材料：NBR20kg、EVA18kg； 
无卤阻燃剂：氢氧化铝16kg、氢氧化镁14kg； 
无卤增塑剂：磷酸三甲苯酯17kg； 
发泡剂：偶氮二甲酰胺12kg； 
填充剂：滑石粉2.1kg； 
防老剂：防老剂MB0.6kg、防老剂DNP0.3kg。 
本实施例中，按上述组分称取原料，按实施例1的制备方法制得本实施例的无卤素橡塑发泡保温材料。 
按照国家防火标准《GB8624》测试上述三个实施例中制得的无卤素橡塑发泡保温材料的安全等级，结果如下表： 
测试项目 实施例1 实施例2 实施例3
密度(kg/m3) 48 47 47
氧指数 33 34 32
烟密度（等级） 40 35 42
产烟毒性（等级） ZA3 ZA3 ZA3
由上述测试结果可以得出，本发明阻燃型无铝塑橡塑发泡保温材料的氧指数较高，均大于27，属难燃材料；烟密度等级较低；产烟毒性均达到ZA3安全等级，因此对人体的伤害较小。 
本发明不局限于上述实施方式，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围之内。本说明书中未作详细描述的内容属于本领域专业技术人员公知的现有技术。 

Claims (7)

1.一种无卤素橡塑发泡保温材料，其特征在于，以重量百分比计，包括如下组分：
Figure FDA0000457040650000011
2.如权利要求1所述的无卤素橡塑发泡保温材料，其特征在于：所述无卤阻燃剂为氢氧化铝，或氢氧化铝和氢氧化镁的混合物。
3.如权利要求1所述的无卤素橡塑发泡保温材料，其特征在于：所述无卤增塑剂为磷酸酯类增塑剂。
4.如权利要求3所述的无卤素橡塑发泡保温材料，其特征在于：所述无卤素增塑剂为磷酸三甲苯酯。
5.如权利要求1所述的无卤素橡塑发泡保温材料，其特征在于：所述发泡剂为偶氮二甲酰胺。
6.如权利要求1所述的无卤素橡塑发泡保温材料，其特征在于：填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物。
7.如权利要求1所述的无卤素橡塑发泡保温材料，其特征在于：防老剂为防老剂MB、防老剂DNP中的一种或两种的混合物。
CN201410017108.1A 2014-01-15 2014-01-15 一种无卤素橡塑发泡保温材料 Active CN103788431B (zh)