CN103774430A - 一种全涤/棉织物抗菌防皱抗紫外线的整理方法 - Google Patents
一种全涤/棉织物抗菌防皱抗紫外线的整理方法 Download PDFInfo
- Publication number
- CN103774430A CN103774430A CN201310699214.8A CN201310699214A CN103774430A CN 103774430 A CN103774430 A CN 103774430A CN 201310699214 A CN201310699214 A CN 201310699214A CN 103774430 A CN103774430 A CN 103774430A
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- grams per
- agent
- preliminary drying
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种全涤/棉织物抗菌防皱抗紫外线的整理方法，包括将全涤/棉织物用整理浴液进行浸轧、预烘和焙烘处理，然后将全涤/棉织物用20~30克/升的纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，所述整理浴液由整理剂、催化剂、柔软剂、渗透剂以及PH调节剂组成，所述整理剂由30~50克/升的特氟隆CO以及10~20克/升的醚化树脂组成；所述催化剂为6~15克/升氯化镁或氯化铁；所述柔软剂为11~30克/升的低黄变氨基改性有机硅；所述渗透剂为2克/升的烷基硫酸酯钠；所述PH调节剂为0.5~5克/升的醋酸。通过在整理浴液加入低黄变氨基改性有机硅、烷基硫酸酯钠，大大提高了布料与特氟隆CO的结合性。
Description
技术领域
本发明涉及全涤/棉织物整理方法领域，尤其涉及一种抗菌防皱抗紫外线的全涤/棉织物整理方法。
背景技术
随着人们生活水平的不断提高和纺织工业技术的向前发展，只具有单一功能的纺
织织物已经不能满足市场的需求，多功能复合后进行整理的织物已越来越受到人们的欢迎。
市面上一般的整理方法一般仅仅能做到单一的整理功效，例如抗菌、防皱、或者单一的防紫外线，很难将三防一抗全部在一个整理方法内完成。
中国专利公开号为102851942A公开了一种防紫外线纯棉织物的整理方法，包括如下步骤：将棉织物在在含有防紫外线整理剂的浸渍液中浸轧处理，压力2.5～3kg/cm2，带液率60～70％，烘干后将织物在115～150℃之间恒温0.5～2小时。所述防紫外线整理剂由如下重量份的组分组成：氧化锌25～35份；沸石5～8份；2-(2′-羟基-5′-甲基苯基)苯并三唑20～23份；双(3，5-二叔丁基-4-羟基)苄基膦酸单乙酯15～25份；聚丙烯酸钠分散剂0.5～0.7份。本发明兼具两种防紫外线整理剂的优点，可和纯棉织物牢固结合，耐久性强，对纯棉织物有优良的防紫外作用，无毒安全。其技术方案具体介绍了一种防紫外线整理剂，具有很好的放紫外线的功效，但其不具备其他抗菌、防皱等功效，有待改进。
中国专利公开号为CN101942750A涉及一种纯棉织物抗皱的整理方法,由面料准备、预柔软、浸轧树脂、焙烘、水洗、后柔软、预缩工序依次组成,其主要技术特点是:浸轧树脂工序所使用的浸轧配方由以下浓度的组分组成:2D树脂为80～120g/L,乙二醛树脂为80～100g/L,二甲基脲为40g/L,有机酸活化的氯化镁为40g/L,强力保护剂为20～40g/L,渗透剂为1～2g/L,其余为水。本发明设计合理,其充分利用了两种树脂及两种催化剂的优点,经整理后的纯棉织物具有较高的平整度,较高的强力,优良的耐磨性及较低的甲醛含量等特点,用此面料制作的衣服具有穿着舒适、美观、穿着耐久性强的特点。其也仅仅具备防皱的功效，有待改进。
发明内容
本发明针对现有技术的不足，提供了一种方法简单，并且可有效将抗菌防皱抗紫外线的三种功能统一结合到一种布料上的涤/棉织物抗菌防皱抗紫外线的整理方法。
本发明的技术关键在于在整理浴液的配方中加入特氟隆CO、柔软剂：低黄变氨基改性有机硅、渗透剂：烷基硫酸酯钠，使特氟隆CO的特性更好的显现出来，使布料具有良好的防水、防油、防粘的特性，然后用纳米抗紫外线整理剂进行整理使其在具备三防的基础上又具备防紫外线的特性。其具体技术方案为：一种全涤/棉织物抗菌防皱抗紫外线的整理方法，包括将全涤/棉织物用整理浴液进行浸轧、预烘和焙烘处理，然后将全涤/棉织物用20~30克/升的纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，其特征在于所述整理浴液由整理剂、催化剂、柔软剂、渗透剂以及PH调节剂组成，所述整理剂由30~50克/升的特氟隆CO以及10~20克/升的醚化树脂组成；所述催化剂为6~15克/升氯化镁或氯化铁；所述柔软剂为11~30克/升的低黄变氨基改性有机硅；所述渗透剂为2克/升的烷基硫酸酯钠；所述PH调节剂为0.5~5克/升的醋酸。
作为优选，所述整理浴液进行浸轧、预烘和焙烘处理，浸渍时间为1~2分钟，预烘温度为120~130℃，时间2~3分钟，焙烘温度为160~180℃，时间为5~6分钟。
作为优选，所述整纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，浸渍时间为0.5~1分钟，预烘温度为120~130℃，时间1~3分钟，焙烘温度为160~180℃，时间为3~4分钟。
本发明的有益效果：本发明通过在整理浴液加入低黄变氨基改性有机硅、烷基硫酸酯钠，大大提高了布料与特氟隆CO的结合性，从而大大提高了布料的防水、防油、防粘的特性，然后用纳米抗紫外线整理剂进行二次整理，使其具备防紫外线的功能，是一种布料具备多种性能，大大提高了整理效率，应用广泛。
具体实施方式
实施例1：将任意一种机织物的平纹、斜纹、提花组织的全棉或涤棉织物，规格为180X160（小样机织物）用整理浴液进行浸轧、预烘和焙烘处理，然后将全棉或涤棉织物用20~30克/升的纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，所述整理浴液由整理剂、催化剂、柔软剂、渗透剂以及PH调节剂组成，所述整理剂由30~50克/升的特氟隆CO以及10~20克/升的醚化树脂组成；所述催化剂为6~15克/升氯化镁；所述柔软剂为11~30克/升的低黄变氨基改性有机硅；所述渗透剂为2克/升的烷基硫酸酯钠；所述PH调节剂为0.5~5克/升的醋酸。所述整理浴液进行浸轧、预烘和焙烘处理，浸渍时间为1~2分钟，预烘温度为120~130℃，时间2~3分钟，焙烘温度为160~180℃，时间为5~6分钟。所述整纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，浸渍时间为0.5~1分钟，预烘温度为120~130℃，时间1~3分钟，焙烘温度为160~180℃，时间为3~4分钟。
实施例2：整理CVC面料，将特氟隆CO改为40~50克/升，去掉醚化树脂，其他与实施例1相同。
整理后的面料防水、防油、防粘等级均大于等于6级，抗紫外线等级6级，具有良好的耐磨和耐洗性。
Claims (3)
1.一种全涤/棉织物抗菌防皱抗紫外线的整理方法，包括将全涤/棉织物用整理浴液进行浸轧、预烘和焙烘处理，然后将全涤/棉织物用20~30克/升的纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，其特征在于所述整理浴液由整理剂、催化剂、柔软剂、渗透剂以及PH调节剂组成，所述整理剂由30~50克/升的特氟隆CO以及10~20克/升的醚化树脂组成；所述催化剂为6~15克/升氯化镁或氯化铁；所述柔软剂为11~30克/升的低黄变氨基改性有机硅；所述渗透剂为2克/升的烷基硫酸酯钠；所述PH调节剂为0.5~5克/升的醋酸。
2.根据权利要求1所述的一种全涤/棉织物抗菌防皱抗紫外线的整理方法，其特征在于所述整理浴液进行浸轧、预烘和焙烘处理，浸渍时间为1~2分钟，预烘温度为120~130℃，时间2~3分钟，焙烘温度为160~180℃，时间为5~6分钟。
3.根据权利要求1所述的一种全涤/棉织物抗菌防皱抗紫外线的整理方法，其特征在于所述整纳米抗紫外线整理剂进行浸轧、预烘和焙烘处理，浸渍时间为0.5~1分钟，预烘温度为120~130℃，时间1~3分钟，焙烘温度为160~180℃，时间为3~4分钟。