CN103773203A - 一种氯化聚醚散热涂料 - Google Patents

一种氯化聚醚散热涂料 Download PDF

Info

Publication number
CN103773203A
CN103773203A CN201410018939.0A CN201410018939A CN103773203A CN 103773203 A CN103773203 A CN 103773203A CN 201410018939 A CN201410018939 A CN 201410018939A CN 103773203 A CN103773203 A CN 103773203A
Authority
CN
China
Prior art keywords
parts
powder
penton
raw material
heat radiation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410018939.0A
Other languages
English (en)
Inventor
张庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoyi Amusement Equipment Co Ltd
Original Assignee
Wuhu Baoyi Amusement Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoyi Amusement Equipment Co Ltd filed Critical Wuhu Baoyi Amusement Equipment Co Ltd
Priority to CN201410018939.0A priority Critical patent/CN103773203A/zh
Publication of CN103773203A publication Critical patent/CN103773203A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氯化聚醚散热涂料，它是由下述重量份的原料组成的：氯化聚醚84-90、钼酸铵1-2、二丁基萘磺酸钠1-2、聚乙二醇辛基苯基醚0.6-1、天青石粉8-10、妥尔油1-2、2-硫醇基苯骈咪唑1-2、甲基丙烯酸异辛酯3-5、氟硼酸钠1-2、聚二甲基硅氧烷2-4、丙酸钙3-5、二辛脂5-7、复合填料6-10；本发明的粉末涂料涂层的弹性和柔韧性突出,具有耐水、耐冲击、耐腐蚀、摩擦系数小、耐磨损、噪音低等优异性能,可以提高机械的使用寿命和运行稳定性。

Description

一种氯化聚醚散热涂料
技术领域
    本发明主要涉及一种粉末涂料，尤其涉及一种氯化聚醚散热涂料。
背景技术
导热散热涂料被广泛的应用于电脑、笔记本电脑、LED 照明、通信、整流器，医疗及工业设备等有散热要求的领域，主要涂覆在散热器的表面。
目前生产的散热涂料一般多应用于CPU 等电子产品的元器件的散热及LED 灯具散热，对于涂刷的介质要求较高，对于较粗糙、疏松的物体表面附着力不强，使用效果不理想，适用范围较小。
发明内容
本发明目的就是提供一种氯化聚醚散热涂料。
本发明是通过以下技术方案实现的：
一种氯化聚醚散热涂料，其特征在于它是由下述重量份的原料组成的：
氯化聚醚84-90、钼酸铵1-2、二丁基萘磺酸钠1-2、聚乙二醇辛基苯基醚0.6-1、天青石粉8-10、妥尔油1-2、2-硫醇基苯骈咪唑1-2、甲基丙烯酸异辛酯3-5、氟硼酸钠1-2、聚二甲基硅氧烷2-4、丙酸钙3-5、二辛脂5-7、复合填料6-10；
所述的复合填料是由下述重量份的原料组成的：
叶腊石20-30、氟化锆2-3、高岭土30-40、木炭粉2-3、氟硼酸钠2-3、β-二酮0.2-0.4、聚丙烯酸异辛酯3-4、2-乙基-4甲基咪唑0.7-1；
将上述高岭土在600-700℃下煅烧2-3小时，出料冷却后与叶腊石、氟化锆混合研磨成粉；将上述木炭粉与聚丙烯酸异辛酯混合，100-130℃下搅拌分散3-5分钟，加入上述得到的粉料，搅拌至温度为60-80℃，加入剩余各原料，充分球磨，造粒，粒径为2-4μm，即得所述复合填料。
一种氯化聚醚散热涂料的制备方法，包括以下步骤：
将上述甲基丙烯酸异辛酯与丙酸钙、天青石粉混合，100-200转/分搅拌分散3-4分钟，加入妥尔油，充分搅拌分散，加入剩余各原料，混合均匀，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过120-160目筛，即得所述氯化聚醚散热涂料。
本发明的优点是：
    本发明的粉末涂料涂层的弹性和柔韧性突出,具有耐水、耐冲击、耐腐蚀、摩擦系数小、耐磨损、噪音低等优异性能,可以提高机械的使用寿命和运行稳定性。
具体实施方式
实施例1
一种氯化聚醚散热涂料，其特征在于它是由下述重量份（公斤）的原料组成的：
氯化聚醚90、钼酸铵2、二丁基萘磺酸钠2、聚乙二醇辛基苯基醚1、天青石粉10、妥尔油2、2-硫醇基苯骈咪唑1、甲基丙烯酸异辛酯5、氟硼酸钠1、聚二甲基硅氧烷2、丙酸钙3、二辛脂7、复合填料10；
所述的复合填料是由下述重量份的原料组成的：
叶腊石30、氟化锆3、高岭土40、木炭粉2、氟硼酸钠2、β-二酮0.4、聚丙烯酸异辛酯4、2-乙基-4甲基咪唑0.7；
将上述高岭土在700℃下煅烧2小时，出料冷却后与叶腊石、氟化锆混合研磨成粉；将上述木炭粉与聚丙烯酸异辛酯混合，130℃下搅拌分散5分钟，加入上述得到的粉料，搅拌至温度为80℃，加入剩余各原料，充分球磨，造粒，粒径为4μm，即得所述复合填料。
一种氯化聚醚散热涂料的制备方法，包括以下步骤：
将上述甲基丙烯酸异辛酯与丙酸钙、天青石粉混合，200转/分搅拌分散3分钟，加入妥尔油，充分搅拌分散，加入剩余各原料，混合均匀，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过160目筛，即得所述氯化聚醚散热涂料。
性能测试：
涂膜外观：平整光滑，无缩孔，无针孔；
正反冲测试：通过；
铅笔硬度测试：2H 无划伤；
弯曲硬度测试：0T 弯通过。

Claims (2)

1.一种氯化聚醚散热涂料，其特征在于它是由下述重量份的原料组成的：
氯化聚醚84-90、钼酸铵1-2、二丁基萘磺酸钠1-2、聚乙二醇辛基苯基醚0.6-1、天青石粉8-10、妥尔油1-2、2-硫醇基苯骈咪唑1-2、甲基丙烯酸异辛酯3-5、氟硼酸钠1-2、聚二甲基硅氧烷2-4、丙酸钙3-5、二辛脂5-7、复合填料6-10；
所述的复合填料是由下述重量份的原料组成的：
叶腊石20-30、氟化锆2-3、高岭土30-40、木炭粉2-3、氟硼酸钠2-3、β-二酮0.2-0.4、聚丙烯酸异辛酯3-4、2-乙基-4甲基咪唑0.7-1；
将上述高岭土在600-700℃下煅烧2-3小时，出料冷却后与叶腊石、氟化锆混合研磨成粉；将上述木炭粉与聚丙烯酸异辛酯混合，100-130℃下搅拌分散3-5分钟，加入上述得到的粉料，搅拌至温度为60-80℃，加入剩余各原料，充分球磨，造粒，粒径为2-4μm，即得所述复合填料。
2.一种如权利要求1所述的氯化聚醚散热涂料的制备方法，其特征在于包括以下步骤：
将上述甲基丙烯酸异辛酯与丙酸钙、天青石粉混合，100-200转/分搅拌分散3-4分钟，加入妥尔油，充分搅拌分散，加入剩余各原料，混合均匀，送入双螺杆挤出机，进行熔融、挤出和造粒，磨成细粉并过120-160目筛，即得所述氯化聚醚散热涂料。
CN201410018939.0A 2014-01-15 2014-01-15 一种氯化聚醚散热涂料 Pending CN103773203A (zh)