CN103757793A - Method for weaving bamboo fiber filament and tencel interwoven fabric - Google Patents
Method for weaving bamboo fiber filament and tencel interwoven fabric Download PDFInfo
- Publication number
- CN103757793A CN103757793A CN201410008128.2A CN201410008128A CN103757793A CN 103757793 A CN103757793 A CN 103757793A CN 201410008128 A CN201410008128 A CN 201410008128A CN 103757793 A CN103757793 A CN 103757793A
- Authority
- CN
- China
- Prior art keywords
- interwoven fabric
- fabric
- tencel interwoven
- tencel
- bamboo fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method for weaving a bamboo fiber filament and tencel interwoven fabric is characterized by comprising the following steps of performing beaming on a tencel interwoven fabric; performing filament sizing and axis combining procedures on the tencel interwoven fabric after beaming; pulling out heald and reeds after axis combining; feeding the tencel interwoven fabric into a weaving machine, and inspecting and dyeing the fabric; and performing an after-treatment procedure on the fabric. The original antibiosis and bacteriostasis effect of bamboos is kept; and moreover, the bamboo fiber filament and tencel interwoven fabric has characteristics of high wet absorption breathability, softness, high draping, high uvioresistant effect, easiness in neatening, high dyeing performance, high wear resistance, avoidance of fuzz balls and the like. Compared with a common product, the bamboo fiber filament and tencel interwoven fabric has the advantages that bamboo fibers are high in cost, but have antibiosis and bacteriostasis effects, and are smooth, and the perspiration speed is quite high.
Description
Technical field
The present invention relates to a kind of fabric of field of textiles, particularly relate to the weaving method of a kind of nandina long filament and tencel interwoven fabric.
Background technology
In the production process of beamhouse, long filament brute force is low, filoplume is many due to this kind, has brought many difficulties to warping and sizing, particularly often occurs the phenomenon that broken end stops.After deliberation, this problem is because existing size mixing technology is not suitable for starching this kind of long filament, and the speed of a motor vehicle of warping machines, tension force and detector sensitivity all need to carry out adjustment again according to the characteristic of this kind of long filament.
So first we reduce the speed of a motor vehicle of warping, and accordingly tension in Warping is adjusted, and the sensitivity (30%) surveyed of the filoplume of suitably loweing, reduced the mistakenly stop of little filoplume.In the sizing stage, be mainly to have adjusted formula of size, strengthens the use amount of PVA-205, improves the rate of sizing, makes filoplume paste volt.
Weaving workshop, because our frequent woven kind is generally that warp thread is the kind of viscose filament yarn, its weaving process is applied to this kind, can often occur that warp end break and weft yarn introduce difficult problem, and often occur the residual defects such as looped weft.
So, we are by increasing the definition of opening, increase Filling Insertion Time, the problem that will suitably strengthen the problem solution wefting insertion of jet amount for the weft yarn of sky silk class, for the disconnected problem of warp, we are by using the reed that porter is less instead, but increase yarn reed enters several ways and goes to be solved, in addition temperature will be controlled to 26～28 ℃, relative humidity will be controlled at 60%～65%, also can reduce cracked ends.
It bamboo fibre be Hebei Jigao Fiber Co.,Ltd to utilize the bamboo of Sichuan Province China widespread production be raw material, the tencel cellulose fiber that utilizes bamboo pulp to produce through patented technology for raw material." nandina " fiber can natural degradation in soil, and to environment without any pollution.It has kept original antibacterial, the bacteriostasis of bamboo, also has that sucting wet air permeability is good, soft, fabric fall is good, uvioresistant is effective simultaneously, easily arranges the characteristics such as dyeability is good, wear-resisting, phozy ball.Compare with mill run, nandina fiber cost is higher, but it has antibacterial, biocidal property, speed smooth, perspire is also fast especially, and its product mostly is expensive goods.
It silk adopts solvent spining technology to produce, and is the more popular in the world high-grade textile raw material of environmental protection, and resource is abundanter.It had both had the good hygroscopicity of viscose, had overcome again the defect of common viscose fiber brute force low (especially wet too low by force), and the wet strength of day silk is higher than cotton fiber, and had good washing DIMENSIONAL STABILITY.Fabric sheen is graceful, and feel is soft and smooth comfortable.Have the unique sense of touch as real silk, elegant drapability is good.
The design of warp-wise nandina long filament and broadwise tencel interwoven fabric is just in keep with the theory of environmental protection, the quality level of nandina series of products can reach advanced international level at present, and interweaving product is still had a uniqueness through preliminary internet retrieval, is a kind of high value added product.
Summary of the invention
Technical problem underlying to be solved by this invention is, overcomes the above-mentioned defect that prior art exists, and the weaving method of a kind of nandina long filament and tencel interwoven fabric is provided, and this product in design, is done warp-wise by nandina long filament to use, and broadwise is used a day silk.And axle processes employ dislocation pendulum reed method, effectively improved the dyeing quality of cloth cover.
The technical solution adopted for the present invention to solve the technical problems is:
The weaving method of a kind of nandina long filament and tencel interwoven fabric, it is characterized in that, its weaving process process step is as follows: first through warping, tencel interwoven fabric after warping enters slurry silk axle operation, and through drawing to combine, draw reed operation again after axle, then enter loom, perching, dyeing process, finally enter finishing process.
Novelty of the present invention is as follows:
(1) radially raw material adopts the bamboo filament of 118D/30F;
(2) broadwise bamboo filament interweaves with a day slub yarn for the numb blending of silk;
(3) warping (TWN-e warping machines) → slurry silk (a KSX slurry silk machine) → and axle (KB30-e warp rebeaming machine) → weave process route of (the jet silk loom of ZAX9100);
(4) when bamboo fibre is starched silk, adopt low-tension, heavily coating.The elongation that slurry Si Keyong is permitted 1%-2%.
The invention has the beneficial effects as follows, this product in design, is done warp-wise by nandina long filament and is used, and broadwise is used a day silk.And axle processes employ dislocation pendulum reed method, effectively improved the dyeing quality of cloth cover.
Accompanying drawing explanation
Below in conjunction with drawings and Examples, the present invention is further described.
Fig. 1 is process chart of the present invention.
Number in the figure explanation:
1 warping
2 slurry silks
3 and axle
4 draw the comprehensive reed of drawing
5 looms
6 perching
7 dyeing
8 rear arrangements
The specific embodiment
The weaving method of a kind of nandina long filament and tencel interwoven fabric, it is characterized in that, its weaving process process step is as follows: first through warping 1, tencel interwoven fabric after warping enters slurry silk 2 axle 3 operations, and through drawing to combine, draw reed 4 operations again after axle, then enter loom 5, perching 6, dyeing 7 operations, finally enter rear arrangement 8 operations.
Technological difficulties of the present invention are as follows:
(1), bamboo wood material makes molecular crystalline degree after pulp spinning than the people Si Gao of Cotton Pulp, cause the rigidity of silk large, but brute force is not high, lower than people's silk 5%, bamboo long filament filoplume is more, warping, the slurry silk difficulty of weaving front preparatory process are larger.
(2), bamboo long filament is to warm and humid more responsive when weaving, when relative humidity is low, brute force, elasticity, the ABRASION RESISTANCE of silk are relatively good, but can not be too low, too low meeting causes the increase of broken end.
(3), bamboo long filament good luster, hygroscopicity is strong, extensibility is large, not resistance to highly basic, grey cloth is ecru.So, in dyeing and printing process, be noted that pre-treatment preferably used loose formula equipment.
The above, it is only preferred embodiment of the present invention, not the present invention is done to any pro forma restriction, any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical solution of the present invention.
In sum, the present invention is in structural design, use practicality and cost benefit, meet industry development completely required, and the structure disclosing is also to have unprecedented innovative structure, there is novelty, creativeness, practicality, the regulation that meets relevant patent of invention important document, therefore mention application in accordance with the law.
Claims (1)
1. the weaving method of a nandina long filament and tencel interwoven fabric, it is characterized in that, its weaving process process step is as follows: first through warping (1), tencel interwoven fabric after warping enters slurry silk (2) axle (3) operation, and through drawing to combine, draw reed (4) operation again after axle, then enter loom (5), perching (6), dyeing (7) operation, finally enter rear arrangement (8) operation.