CN103756392A - Efficient crack paint - Google Patents
Efficient crack paint Download PDFInfo
- Publication number
- CN103756392A CN103756392A CN201410017008.9A CN201410017008A CN103756392A CN 103756392 A CN103756392 A CN 103756392A CN 201410017008 A CN201410017008 A CN 201410017008A CN 103756392 A CN103756392 A CN 103756392A
- Authority
- CN
- China
- Prior art keywords
- cab
- content
- mixed solution
- cotton
- nitro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to paint, in particular to efficient crack paint. The efficient crack paint is characterized by comprising mixed fatty acid resin, titanium dioxide, xylene, durene, butyl acetate, acetic ether, 2-butoxyethanol, butanone, a dispersing agent, nitro-cotton, CAB (cellulose acetate butyrate), gas-phase silicon dioxide, an anti-settling agent and an antifoaming agent. The efficient crack paint capable of simulating various cracks has the beneficial effects of simple preparation process, low probability of depainting, high simulation capability and low cost.
Description
Technical field
The present invention relates to a kind of paint, espespecially a kind of efficient strain indicating lacquer.
Background technology
Along with social development, people's quality of the life improves constantly, handicraft ornament becomes gradually people and shows one of important ornament of life taste, wherein artificial handicraft has occupied critical role, therefore the requirement of emulation paint is also improved day by day, spraying and dyeing repeatedly is generally all carried out artwork in artwork processing now, make it present various patterns or emulation texture, this paint vehicle need to be through repeatedly spraying, its adhesive ability is poor, easily fall paint, and spraying texture quality is poor, can not realize well emulation, destroy the attractive in appearance of artwork, be not durable, artwork manufacturing procedure complexity is various in addition, cost is high.
Summary of the invention
In order to address the above problem, the present invention aims to provide a kind of paint, espespecially a kind of efficient strain indicating lacquer.
Realize above-mentioned purpose, the technical solution used in the present invention is: a kind of efficient strain indicating lacquer, is characterized in that: include mixing-in fat acid resin, titanium dioxide, dimethylbenzene, durene, N-BUTYL ACETATE, vinyl acetic monomer, anti-plain boiled water, butanone, dispersion agent, nitro-cotton, CAB, Gas aerosil, anti-settling agent, defoamer.
Secondly, described titanium dioxide can be replaced with organic toner powder.
In addition, each component concentration is respectively:
The mixing-in fat acid resin of 20-25%;
The titanium dioxide of 5-10%;
The dimethylbenzene of 4%-6%
The durene of 18%-20%;
The N-BUTYL ACETATE of 4%-6%;
The vinyl acetic monomer of 4%-6%;
The anti-plain boiled water of 4%-6%;
The butanone of 4%-6%;
The dispersion agent of 0.3-0.5%;
The nitro-cotton of 10%-15%;
The CAB of 4%-5%;
The Gas aerosil of 8%-10%;
The anti-settling agent of 1.5%-2%;
The defoamer of 0.1%-0.4%.
Dress moreover, make flow process and be:
(1) first once add content to stir 5 minutes than the durene for the mixing-in fat acid resin of 20-25% and 15-20%, form mixed solution;
(2) then to adding content in described mixed solution than being the titanium dioxide of 5-10%, add again the dispersion agent of 0.3-0.5% and the anti-settling agent of 1.5%-2% to carry out rapid stirring even, form processing mixed solution, then described processing mixed solution is placed in shredder, processing mixed solution is ground and forms mill base, and mill base fineness is below 6 μ mc;
(3) again content than for the N-BUTYL ACETATE of the dimethylbenzene of 4%-6%, 4%-6%, the vinyl acetic monomer of 4%-6% adds the nitro-cotton of 10-15% to dissolve after mixing, formation nitro-cotton lysate after dissolving;
(4) to content, than the butanone that adds 4%-6% in the CAB for 4%-5%, dissolve and form CAB solvent more subsequently;
(5) finally described mill base, nitrocellulose solution, CAB solvent are added to content than stirring for the anti-plain boiled water of 4%-6%, then add content to stir and can form efficient strain indicating lacquer than the defoamer for the Gas aerosil of 8%-10% and 0.1%-0.4%.
Beneficial effect of the present invention is presented as: the present invention aims to provide the efficient strain indicating lacquer of a kind of energy emulation crackle of all kinds, and its manufacture craft is simple, is difficult for depainting, and its simulated force is strong, and cost is low.
Embodiment
Embodiment mono-:
An efficient strain indicating lacquer, is characterized in that: include mixing-in fat acid resin, titanium dioxide, dimethylbenzene, durene, N-BUTYL ACETATE, vinyl acetic monomer, anti-plain boiled water, butanone, dispersion agent, nitro-cotton, CAB, Gas aerosil, anti-settling agent, defoamer.
Secondly, described titanium dioxide can be replaced with organic toner powder.
In addition, each component concentration is respectively:
The mixing-in fat acid resin of 20-25%;
The titanium dioxide of 5-10%;
The dimethylbenzene of 4%-6%
The durene of 18%-20%;
The N-BUTYL ACETATE of 4%-6%;
The vinyl acetic monomer of 4%-6%;
The anti-plain boiled water of 4%-6%;
The butanone of 4%-6%;
The dispersion agent of 0.3-0.5%;
The nitro-cotton of 10%-15%;
The CAB of 4%-5%;
The Gas aerosil of 8%-10%;
The anti-settling agent of 1.5%-2%;
The defoamer of 0.1%-0.4%.
Dress moreover, make flow process and be:
(1) first once add content and stir 5 minutes than the durene that is 23% mixing-in fat acid resin and 18%, form mixed solution;
(2) then in described mixed solution, add content than the titanium dioxide that is 10%, add again the anti-settling agent of 0.5% dispersion agent and 2% to carry out rapid stirring even, form processing mixed solution, then described processing mixed solution is placed in shredder, processing mixed solution is ground and forms mill base, and mill base fineness is below 6 μ mc;
(3) again content than being to add the nitro-cotton of 10-15% to dissolve after 5% dimethylbenzene, 5% N-BUTYL ACETATE, 4% vinyl acetic monomer mix, after dissolving, form nitro-cotton lysate;
(4) subsequently again to content than being to add 4% butanone to dissolve in 5% CAB to form CAB solvent;
(5) finally add content to stir than the anti-plain boiled water that is 6% described mill base, nitrocellulose solution, CAB solvent, then add content to stir and can form efficient strain indicating lacquer than the defoamer for the Gas aerosil of 8%-10% and 0.3%.
Embodiment bis-:
An efficient strain indicating lacquer, is characterized in that: include mixing-in fat acid resin, titanium dioxide, dimethylbenzene, durene, N-BUTYL ACETATE, vinyl acetic monomer, anti-plain boiled water, butanone, dispersion agent, nitro-cotton, CAB, Gas aerosil, anti-settling agent, defoamer.
Secondly, described titanium dioxide can be replaced with organic toner powder.
In addition, each component concentration is respectively:
The mixing-in fat acid resin of 20-25%;
The titanium dioxide of 5-10%;
The dimethylbenzene of 4%-6%
The durene of 18%-20%;
The N-BUTYL ACETATE of 4%-6%;
The vinyl acetic monomer of 4%-6%;
The anti-plain boiled water of 4%-6%;
The butanone of 4%-6%;
The dispersion agent of 0.3-0.5%;
The nitro-cotton of 10%-15%;
The CAB of 4%-5%;
The Gas aerosil of 8%-10%;
The anti-settling agent of 1.5%-2%;
The defoamer of 0.1%-0.4%.
Dress moreover, make flow process and be:
(1) first once add content and stir 5 minutes than the durene that is 20% mixing-in fat acid resin and 20%, form mixed solution;
(2) then in described mixed solution, add content than the titanium dioxide that is 9%, add again the anti-settling agent of 0.5% dispersion agent and 2% to carry out rapid stirring even, form processing mixed solution, then described processing mixed solution is placed in shredder, processing mixed solution is ground and forms mill base, and mill base fineness is below 6 μ mc;
(3) again content than being to add the nitro-cotton of 10-15% to dissolve after 5% dimethylbenzene, 5% N-BUTYL ACETATE, 4% vinyl acetic monomer mix, after dissolving, form nitro-cotton lysate;
(4) subsequently again to content than being to add 4% butanone to dissolve in 5% CAB to form CAB solvent;
(5) finally add content to stir than the anti-plain boiled water that is 6% described mill base, nitrocellulose solution, CAB solvent, then add content to stir and can form efficient strain indicating lacquer than the defoamer for the Gas aerosil of 8%-10% and 0.3%.
The above, it is only preferred embodiment of the present invention, not technical scope of the present invention is imposed any restrictions, the technician of the industry, under the inspiration of the technical program, can make some distortion and revise, any modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical solution of the present invention.
Claims (4)
1. an efficient strain indicating lacquer, is characterized in that: include mixing-in fat acid resin, titanium dioxide, dimethylbenzene, durene, N-BUTYL ACETATE, vinyl acetic monomer, anti-plain boiled water, butanone, dispersion agent, nitro-cotton, CAB, Gas aerosil, anti-settling agent, defoamer.
2. a kind of efficient strain indicating lacquer according to claim 1, is characterized in that: described titanium dioxide can be replaced with organic toner powder.
3. a kind of efficient strain indicating lacquer according to claim 1, is characterized in that: each component concentration is respectively:
The mixing-in fat acid resin of 20-25%;
The titanium dioxide of 5-10%;
The dimethylbenzene of 4%-6%
The durene of 18%-20%;
The N-BUTYL ACETATE of 4%-6%;
The vinyl acetic monomer of 4%-6%;
The anti-plain boiled water of 4%-6%;
The butanone of 4%-6%;
The dispersion agent of 0.3-0.5%;
The nitro-cotton of 10%-15%;
The CAB of 4%-5%;
The Gas aerosil of 8%-10%;
The anti-settling agent of 1.5%-2%;
The defoamer of 0.1%-0.4%.
4. a kind of efficient strain indicating lacquer according to claim 1, is characterized in that: making flow process is:
(1) first once add content to stir 5 minutes than the durene for the mixing-in fat acid resin of 20-25% and 15-20%, form mixed solution;
(2) then to adding content in described mixed solution than being the titanium dioxide of 5-10%, add again the dispersion agent of 0.3-0.5% and the anti-settling agent of 1.5%-2% to carry out rapid stirring even, form processing mixed solution, then described processing mixed solution is placed in shredder, processing mixed solution is ground and forms mill base, and mill base fineness is below 6 μ mc;
(3) again content than for the N-BUTYL ACETATE of the dimethylbenzene of 4%-6%, 4%-6%, the vinyl acetic monomer of 4%-6% adds the nitro-cotton of 10-15% to dissolve after mixing, formation nitro-cotton lysate after dissolving;
(4) to content, than the butanone that adds 4%-6% in the CAB for 4%-5%, dissolve and form CAB solvent more subsequently;
(5) finally described mill base, nitrocellulose solution, CAB solvent are added to content than stirring for the anti-plain boiled water of 4%-6%, then add content to stir and can form efficient strain indicating lacquer than the defoamer for the Gas aerosil of 8%-10% and 0.1%-0.4%.