CN103740157A - Oily filler - Google Patents
Oily filler Download PDFInfo
- Publication number
- CN103740157A CN103740157A CN201310740822.9A CN201310740822A CN103740157A CN 103740157 A CN103740157 A CN 103740157A CN 201310740822 A CN201310740822 A CN 201310740822A CN 103740157 A CN103740157 A CN 103740157A
- Authority
- CN
- China
- Prior art keywords
- weighting agent
- oiliness
- solution
- nitro
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an oily filler, comprising the following raw materials by in percentage by weight: 20-30% of keto-aldehyde resin solution, 20-44% of talcum powder, 20-44% of transparent powder, 5-10% of nitrocellulose liquid, 10-30% of solvent and 1-12% of mill base, wherein the keto-aldehyde resin solution is prepared by adding 60-80wt% of solid keto-aldehyde resin to the solvent; the nitrocellulose liquid is prepared by adding 20-40wt% of nitrocellulose to the solvent. The oily filler is convenient to use, fast in drying speed, good in filling property, and less in oil paint dosage, can be used in any climate, and especially is directly blade-coated on a substrate with wood grains at low temperature in winter, and a primer is not affected.
Description
Technical field
The present invention relates to a kind of weighting agent field, relate in particular to a kind of woodenware weighting agent.
Background technology
Weighting agent, is commonly referred to putty, is a kind of thick slurry coating material, is a kind of product that coating whitewashes front use.General adopt a small amount of paint base, auxiliary agent, mass filler and appropriate tinting pigment formulated, pigment used is mainly iron oxide red, carbon black, chrome yellow etc., filler is mainly calcium bicarbonate, talcum powder etc.Painting imposes on priming paint or is directly coated with and imposes on object, in order to remove rugged defect on coated article surface, as fills up part and has the working-surface of depression, also can strike off at all surfaces, requires that tack is good, does not crack in bake process.
At woodwork industry, producer, simultaneously in order to enhance productivity, saves time, and reduces paint application number of times, can be spraying weighting agent of blade coating before priming paint, to reach the effect of filling timber surface crack when producing solid wood furniture or stick-skin furniture.
As Chinese patent CN102732075A discloses a kind of woodenware putty, the component that comprises weight proportion: emulsion 0.02-0.15%, binding agent 0.03-0.1%, pH adjusting agent 0.04-0.2%, initiator 1.5-5%, mix monomer 4-6%, polyvinyl alcohol 11-14%, deionized water 18-25%, stopping composition 50-60%.Have and the advantage such as need not allocate, the storage time is long, sticking power is good.
But because current woodenware weighting agent contains aqueous substance more, especially some weighting agent can contain the water of 10-40%, while entering winter, blade coating is difficult to dry on timber, when particularly temperature drops to below 0 degree, moisture content is difficult to volatilization, easily cause parching, be unfavorable for polishing, in construction, coating priming paint is easy to the disadvantage that occurs that paint turns white and gets confused.
Synolac is the one oil modified polyester resin being formed by polyvalent alcohol, Tetra hydro Phthalic anhydride and lipid acid or oil (fatty acid triglyceride) condensation polymerization.By Synolac oil content, can be divided into long oil alkyd, medium oil alkyd, short oil-ity alcohol acid resin.Oiliness weighting agent take Synolac as base-material, has excellent fillibility, tinting strength, sticking power, as Chinese patent CN103232768A has announced the weighting agent of the soybean plants long oil class thixotropic Synolac of a kind of 4-6% of comprising.But the oiliness weighting agent that Synolac is base-material, rate of drying is unsatisfactory.
Summary of the invention
For above-mentioned technical problem, the invention provides a kind of oiliness weighting agent.
Oiliness weighting agent provided by the invention, mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
Preferably, described oiliness weighting agent, mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
More preferably, described oiliness weighting agent, mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
Preferably, described aldehyde ketone resin solution is the solution that 70wt% aldehyde ketone resin is dissolved in described solvent.
Preferably, the nitro-cotton that described nitro-cotton liquid is 30wt% is dissolved in the solution of described solvent.
Preferably, solvent is selected from any one or a few in pimelinketone, dimethylbenzene, N-BUTYL ACETATE, vinyl acetic monomer.
Preferably, described nitro-cotton is selected from any one in 1/2 second, 1/4 second, 1 second nitro-cotton.
Preferably, described talcous fineness is 700-1000 order.
Preferably, the molecular weight of described aldehyde ketone resin is 1000-2000, and more preferably, molecular weight is 1200-1500.
Preferably, the fineness of described transparent powder is 800-1000 order.
Preferably, described mill base is selected from any one in oil pastes or resin mill base.
Oiliness weighting agent provided by the invention, easy to use, fast drying, fillibility is good, paint consumption is few.Under any weather, all can use, especially during winter low temperature.Directly blade coating on the base material with wood grain, can not impact priming paint.
Embodiment
Oiliness weighting agent provided by the invention, mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
Below by specific embodiment, the present invention is carried out to detailed and concrete introduction, to better understand the present invention, but following examples do not limit the scope of the invention.
Embodiment 1
Oiliness weighting agent described in the present embodiment, mark meter by weight, comprises:
Wherein, 60% aldehyde ketone resin solution is the N-BUTYL ACETATE solution of 60wt% aldehyde ketone resin, the N-BUTYL ACETATE solution of 1/2 second nitro-cotton that described nitro-cotton liquid is 30wt%.
Embodiment 2
Oiliness weighting agent described in the present embodiment, mark meter by weight, comprises:
Wherein, 80% aldehyde ketone resin solution is the vinyl acetic monomer solution of 80wt% aldehyde ketone resin, the vinyl acetic monomer solution of 1/4 second nitro-cotton that nitro-cotton liquid is 30wt%.
Embodiment 3
Oiliness weighting agent described in the present embodiment, mark meter by weight, comprises:
Wherein, 70% aldehyde ketone resin solution is the vinyl acetic monomer solution of 70wt% aldehyde ketone resin, the vinyl acetic monomer solution of 1 second nitro-cotton that nitro-cotton liquid is 30wt%.
Embodiment 4
Oiliness weighting agent described in the present embodiment, mark meter by weight, comprises:
Wherein, 70% aldehyde ketone resin solution is the N-BUTYL ACETATE solution of 70wt% aldehyde ketone resin, the N-BUTYL ACETATE solution of 1/2 second nitro-cotton that nitro-cotton liquid is 30wt%.
Embodiment 5
Oiliness weighting agent described in the present embodiment, mark meter by weight, comprises:
Wherein, 70% aldehyde ketone resin solution is the vinyl acetic monomer solution of 70wt% aldehyde ketone resin, the vinyl acetic monomer solution of 1/2 second nitro-cotton that nitro-cotton liquid is 30wt%.
Oiliness weighting agent provided by the invention, easy to use, fast drying, fillibility be good, can save paint consumption more than 25%.Directly blade coating on the base material with wood grain, can not impact priming paint, and oiliness weighting agent is coated in woodenware surface, continues application polyurethane coating, and sticking power is 1 grade (with reference to GB/T9286).
And oiliness weighting agent of the present invention all can be used under any weather, especially during winter low temperature, than traditional water-based weighting agent and existing Synolac weighting agent, rate of drying is faster, and time of drying is shorter, therefore can effectively improve the production efficiency of the products such as furniture.
Above specific embodiments of the invention be have been described in detail, but it is just as example, the present invention is not restricted to specific embodiment described above.To those skilled in the art, any equivalent modifications that the present invention is carried out and alternative also all among category of the present invention.Therefore, equalization conversion and the modification done without departing from the spirit and scope of the invention, all should contain within the scope of the invention.
Claims (10)
1. an oiliness weighting agent, is characterized in that, mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
2. oiliness weighting agent according to claim 1, is characterized in that, described talcous fineness is 700-1000 order.
3. oiliness weighting agent according to claim 1, is characterized in that, the fineness of described transparent powder is 800-1000 order.
4. oiliness weighting agent according to claim 1, is characterized in that, described nitro-cotton is any one or a few in 1/2 second, 1/4 second, 1 second nitro-cotton.
5. oiliness weighting agent according to claim 1, is characterized in that, described solvent is any one or a few in dimethylbenzene, N-BUTYL ACETATE, vinyl acetic monomer.
6. oiliness weighting agent according to claim 1, is characterized in that, the molecular weight of described aldehyde ketone resin is 1000-2000.
7. oiliness weighting agent according to claim 6, is characterized in that, the molecular weight of described aldehyde ketone resin is 1200-1500.
8. oiliness weighting agent according to claim 1, is characterized in that, described oiliness weighting agent, and mark meter by weight, comprises:
Wherein, described aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
9. oiliness weighting agent according to claim 8, is characterized in that, described oiliness weighting agent, and mark meter by weight, comprises:
Wherein, described 70% aldehyde ketone resin solution is the solution that 60-80wt% aldehyde ketone resin is dissolved in described solvent, and the nitro-cotton that described nitro-cotton liquid is 20-40wt% is dissolved in the solution of described solvent.
10. according to the oiliness weighting agent described in claim 1-9 any one, it is characterized in that, described mill base is oil pastes or resin mill base.