CN103740072A - 一种聚碳酸酯复合物 - Google Patents

一种聚碳酸酯复合物 Download PDF

Info

Publication number
CN103740072A
CN103740072A CN201310583987.XA CN201310583987A CN103740072A CN 103740072 A CN103740072 A CN 103740072A CN 201310583987 A CN201310583987 A CN 201310583987A CN 103740072 A CN103740072 A CN 103740072A
Authority
CN
China
Prior art keywords
polycarbonate
polycarbonate compound
antioxidant
compound according
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310583987.XA
Other languages
English (en)
Inventor
张明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Baizhong Chemical Technology Co Ltd
Original Assignee
Qingdao Baizhong Chemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Baizhong Chemical Technology Co Ltd filed Critical Qingdao Baizhong Chemical Technology Co Ltd
Priority to CN201310583987.XA priority Critical patent/CN103740072A/zh
Publication of CN103740072A publication Critical patent/CN103740072A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚碳酸酯复合物，包括以下重量份的组分：聚碳酸酯50-100份；阻燃剂5-30份；促进剂0.5-0.8份；相容剂0-10份；填充剂1-30份；着色剂0-1份；抗氧化剂0.1-1份。制备方法为按比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。本发明的积极效果在于：加入各助剂及促进剂，使得聚碳酸酯阻燃效果好，填充剂的加入，使机械性能增强，相容剂的加入，增强了其塑型性。

Description

一种聚碳酸酯复合物
技术领域
本发明涉及一种聚碳酸酯复合物，具体涉及一种阻烯效果好的聚碳酸酯复合物及其制备方法。
背景技术
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的阻燃效果较差，从而限制了其在工程塑料方面的应用。
发明内容
为解决上述问题，本发明提供一种聚碳酸酯复合物。
一种聚碳酸酯复合物，包括以下重量份的组分：
聚碳酸酯 50-100份；
阻燃剂 5-30份；
促进剂 0.5-0.8份；
相容剂 0-10份；
填充剂 1-30份；
着色剂 0-1份；
抗氧化剂 0.1-1份。
进一步的，所述聚碳酸酯为脂肪族聚碳酸酯均聚物、硅氧烷聚碳酸酯嵌段共聚物、无规共聚聚丙烯改性聚碳酸酯中的一种或两种的组合。
进一步的，所述阻燃剂为磷-氮系阻燃剂三聚氰胺与磷酸三苯酯。
进一步的，所述促进剂为N-环已基-2-苯骈噻唑次磺酰胺。
进一步的，所述相容剂为马来酸酐接枝低密度聚乙烯。
进一步的，所述填充剂为碳酸钙、滑石粉、硅灰石、碳纤维、玻璃纤维中的至少一种。
本发明还公开了一种聚碳酸酯复合物的制备方法，具体步骤为：按比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。
本发明的积极效果在于：加入各助剂及促进剂，使得聚碳酸酯阻燃效果好，填充剂的加入，使机械性能增强，相容剂的加入，增强了其塑型性。
具体实施方式
下面结合实施例详细说明本发明的技术方案，但保护范围并不受此限制。
实施例1
一种聚碳酸酯复合物，包括以下重量份的组分：
脂肪族聚碳酸酯均聚物、硅氧烷聚碳酸酯嵌段共聚物 各50份；
三聚氰胺与磷酸三苯酯各15份；
N-环已基-2-苯骈噻唑次磺酰胺 0.5份；
马来酸酐接枝低密度聚乙烯 10份；
填充剂 30份；
着色剂 1份；
抗氧化剂 1份。
按上述比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。
实施例2
一种聚碳酸酯复合物，包括以下重量份的组分：
脂肪族聚碳酸酯均聚物、无规共聚聚丙烯改性聚碳酸酯中 各50份；
三聚氰胺与磷酸三苯酯 各10份；
N-环已基-2-苯骈噻唑次磺酰胺 0.8份；
马来酸酐接枝低密度聚乙烯 5份；
填充剂 10份；
着色剂 1份；
抗氧化剂 1份。
按上述比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。
实施例3
一种聚碳酸酯复合物，包括以下重量份的组分：
脂肪族聚碳酸酯均聚物、无规共聚聚丙烯改性聚碳酸酯中 各30份；
三聚氰胺与磷酸三苯酯 各15份；
N-环已基-2-苯骈噻唑次磺酰胺 0.8份；
马来酸酐接枝低密度聚乙烯 5份；
填充剂 20份；
着色剂 1份；
抗氧化剂 1份。
按上述比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。

Claims (7)

1.一种聚碳酸酯复合物，其特征在于：包括以下重量份的组分：
聚碳酸酯 50-100份；
阻燃剂 5-30份；
促进剂 0.5-0.8份；
相容剂 0-10份；
填充剂 1-30份；
着色剂 0-1份；
抗氧化剂 0.1-1份。
2.根据权利要求1所述的一种聚碳酸酯复合物，其特征在于：所述聚碳酸酯为脂肪族聚碳酸酯均聚物、硅氧烷聚碳酸酯嵌段共聚物、无规共聚聚丙烯改性聚碳酸酯中的一种或两种的组合。
3.根据权利要求1所述的一种聚碳酸酯复合物，其特征在于：所述阻燃剂为磷-氮系阻燃剂三聚氰胺与磷酸三苯酯。
4.根据权利要求1所述的一种聚碳酸酯复合物，其特征在于：所述促进剂为N-环已基-2-苯骈噻唑次磺酰胺。
5.根据权利要求1所述的一种聚碳酸酯复合物，其特征在于：所述相容剂为马来酸酐接枝低密度聚乙烯。
6.根据权利要求1所述的一种聚碳酸酯复合物，其特征在于：所述填充剂为碳酸钙、滑石粉、硅灰石、碳纤维、玻璃纤维中的至少一种。
7.根据权利要求1所述的一种聚碳酸酯复合物的制备方法，其特征在于：按比例称取各组分原料，将除着急剂和抗氧化剂外的各原料干燥后混合搅拌均匀得到混合物，将所得混合物从双螺杆挤出机的主加料口加入，将着急剂和抗氧化剂加入双螺杆挤出机的侧加料口加入，然后挤出、造粒，得到聚碳酸酯复合物。
CN201310583987.XA 2013-11-20 2013-11-20 一种聚碳酸酯复合物 Pending CN103740072A (zh)