CN103739984A - 一种塑料窗框pvc型材 - Google Patents
一种塑料窗框pvc型材 Download PDFInfo
- Publication number
- CN103739984A CN103739984A CN201310657803.XA CN201310657803A CN103739984A CN 103739984 A CN103739984 A CN 103739984A CN 201310657803 A CN201310657803 A CN 201310657803A CN 103739984 A CN103739984 A CN 103739984A
- Authority
- CN
- China
- Prior art keywords
- parts
- section bar
- stearate
- pvc
- ranges
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种塑料窗框PVC型材,其组成成份以质量份数表示法为:PVC100份;二氧化钛5-8份;硬脂酸钙0.4-1.2份;UV-531为0.5-1.5份;双酚A为0.2-0.6份;CPE6-10份;氧化聚乙烯蜡0.1-0.13份;三碱式硫酸铅为3-6份;二碱式亚磷酸铅为2-4份;改性剂1-3份;轻质碳酸钙10-15份;硬脂酸钡1-2份;硬脂酸铅0.6-1.2份;产品硬度110-120HRR,拉伸强度45-50MPa;拉伸伸长率140-150%,弯曲强度65-70MPa;维卡软化点92-95℃,氧指数45-55%;产品耐光照、难燃,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于塑料材料领域,尤其涉及一种塑料窗框PVC型材。
背景技术
PVC型材是由PVC树脂添加各种功能助剂后,经过高温挤出成型的工业和生活用PVC产品;按性能可分为硬质和软质两种。硬质PVC型材多用于建筑方面,如制作PVC门窗,PVC地板,PVC管材等;软质PVC型材用于PVC软管,输电电缆等,添加了功能助剂的PVC型材具有抗老化,抗紫外线,耐腐蚀,强度高,价格便宜,保温及隔热性能好,可以部分替代铝型材,钢材等;PVC,全名为Polyvinylchlorid,主要成份为聚氯乙烯,另外加入其他成分来增强其耐热性,韧性,延展性等。这种表面膜的最上层是漆,中间的主要成分是聚氯乙烯,最下层是背涂粘合剂。它是当今世界上深受喜爱、颇为流行并且也被广泛应用的一种合成材料。
PVC可分为软PVC和硬PVC。其中硬PVC大约占市场的2/3,软PVC占1/3。软PVC一般用于地板、天花板以及皮革的表层,但由于软PVC中含有柔软剂,容易变脆,不易保存,所以其使用范围受到了局限。硬PVC不含柔软剂,因此柔韧性好,易成型,不易脆,无毒无污染,保存时间长,因此具有很大的 开发应用价值;PVC型材产品经历了导入期和高速发展期,从时间上看,可以分别定义为二十世纪80年代-90年代中期和1995年-2002年左右。2003年以后,PVC型材行业进入了转型期。在产品的导入期:生产商普遍追求低造价,简化了门窗型材断面,配方中大量填充碳酸钙,导致产品性能很低,很多质量问题的出现影响了产品的推广,随着社会城市化、科技化、人性化的发展,设计一种硬度高,弯曲强度和伸长率高的PVC型材以满足市场需求,是非常必要的。
发明内容
解决的技术问题:
本申请针对现有塑料窗框PVC型材硬度低、弯曲强度和伸长率低等技术问题,提供一种塑料窗框PVC型材。
技术方案:
一种塑料窗框PVC型材,由下列原料组成,以质量份数表示法为:PVC100份;二氧化钛5-8份;硬脂酸钙0.4-1.2份;UV-531为0.5-1.5份;双酚A为0.2-0.6份;CPE6-10份;氧化聚乙烯蜡0.1-0.13份;三碱式硫酸铅为3-6份;二碱式亚磷酸铅为2-4份;改性剂1-3份;轻质碳酸钙10-15份;硬脂酸钡1-2份;硬脂酸铅0.6-1.2份。
作为本发明的一种优选技术方案:所述塑料窗框PVC型材,其组成成分,以质量份数表示法为:其组成成份以质量份数表示法为:PVC100份;二氧化钛6份;硬脂酸钙0.8份;UV-531为1份;双酚A为0.4份;CPE8份;氧化聚乙烯蜡0.1份;三碱式硫酸铅为4份;二碱式亚磷酸铅为3份;改性剂2份;轻质碳酸钙12份;硬脂酸钡1.5份;硬脂酸铅0.8份。
作为本发明的一种优选技术方案:所述改性剂采用ACR。
有益效果:
本发明所述一种塑料窗框PVC型材采用以上技术方案与现有技术相比,具有以下技术效果:1、产品硬度110-120HRR,拉伸强度45-50MPa;2、拉伸伸长率140-150%,弯曲强度65-70MPa;3、维卡软化点92-95℃,氧指数45-55%;4、产品耐光照、难燃,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种塑料窗框PVC型材,其组成成份以质量份数表示法为:PVC100份;二氧化钛5份;硬脂酸钙0.4份;UV-531为0.5份;双酚A为0.2份;CPE6份;氧化聚乙烯蜡0.1份;三碱式硫酸铅为3份;二碱式亚磷酸铅为2份;ACR改性剂1份;轻质碳酸钙10份;硬脂酸钡1份;硬脂酸铅0.6份。
产品硬度110HRR,拉伸强度45MPa;拉伸伸长率140%,弯曲强度65MPa;维卡软化点92℃,氧指数45%。
实施例2:
一种塑料窗框PVC型材,其组成成份以质量份数表示法为:PVC100份;二氧化钛8份;硬脂酸钙1.2份;UV-531为1.5份;双酚A为0.6份;CPE10份;氧化聚乙烯蜡0.13份;三碱式硫酸铅为6份;二碱式亚磷酸铅为4份;ACR改性剂3份;轻质碳酸钙15份;硬脂酸钡2份;硬脂酸铅1.2份。
产品硬度115HRR,拉伸强度48MPa;拉伸伸长率145%,弯曲强度67MPa;维卡软化点94℃,氧指数50%。
实施例3:
一种塑料窗框PVC型材,其特征在于:其组成成份以质量份数表示法为:PVC100份;二氧化钛6份;硬脂酸钙0.8份;UV-531为1份;双酚A为0.4份;CPE8份;氧化聚乙烯蜡0.1份;三碱式硫酸铅为4份;二碱式亚磷酸铅为3份;ACR改性剂2份;轻质碳酸钙12份;硬脂酸钡1.5份;硬脂酸铅0.8份。
产品硬度120HRR,拉伸强度50MPa;拉伸伸长率150%,弯曲强度70MPa;维卡软化点95℃,氧指数55%。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (3)
1.一种塑料窗框PVC型材,其特征在于:其组成成份以质量份数表示法为:PVC100份;二氧化钛5-8份;硬脂酸钙0.4-1.2份;UV-531为0.5-1.5份;双酚A为0.2-0.6份;CPE6-10份;氧化聚乙烯蜡0.1-0.13份;三碱式硫酸铅为3-6份;二碱式亚磷酸铅为2-4份;改性剂1-3份;轻质碳酸钙10-15份;硬脂酸钡1-2份;硬脂酸铅0.6-1.2份。
2.根据权利要求1所述的一种塑料窗框PVC型材,其特征在于:其组成成份以质量份数表示法为:PVC100份;二氧化钛6份;硬脂酸钙0.8份;UV-531为1份;双酚A为0.4份;CPE8份;氧化聚乙烯蜡0.1份;三碱式硫酸铅为4份;二碱式亚磷酸铅为3份;改性剂2份;轻质碳酸钙12份;硬脂酸钡1.5份;硬脂酸铅0.8份。
3.根据权利要求1所述的一种塑料窗框PVC型材,其特征在于:所述改性剂采用ACR。