CN103737006A - 一种钛银合金材料的制备方法 - Google Patents
一种钛银合金材料的制备方法 Download PDFInfo
- Publication number
- CN103737006A CN103737006A CN201310264502.0A CN201310264502A CN103737006A CN 103737006 A CN103737006 A CN 103737006A CN 201310264502 A CN201310264502 A CN 201310264502A CN 103737006 A CN103737006 A CN 103737006A
- Authority
- CN
- China
- Prior art keywords
- powder
- basic unit
- metal adhesive
- boron nitride
- cubic boron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种钛银合金材料的制备方法,属于材料制造技术领域,将钛银合金粉、铌粉与铝粉混入,压成片状体金属粘结剂;金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,然后向筒状加热块内注入近基层粉末,再向筒状加热块内注入远基层粉末;切削层粉末由碳氧化陶瓷粉末同立方氮化硼微粉制成;将加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。本发明生产出的刀具加工生铁СЧ21-40(GOST1412-79),在加工模式为v=205m/min,s=0.3mm/转,t=1.5-2.0mm,无冷却条件下,HB为220,寿命为60分钟。
Description
技术领域
本发明属于材料制造技术领域,是一种制备刃具材料的方法。
背景技术
现有的刃具材料制备方法主要是将几种金属材料混合加热,刃具在使用过程中易磨损,寿命短。
发明内容
本发明要解决的技术问题是提供一种超硬钛银合金材料的制备方法。
本发明解决技术问题的方案是通过以下步骤完成:
1、制备金属粘结剂
选取钛含量为30-75%的钛银合金粉,向钛银合金加入铌粉,铌粉重量为钛银合金重量的0.5-1%,再混入铝粉,铝粉重量为钛银合金重量的3-6%,压成片状体金属粘结剂;
2、前期准备
将片状体金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,切削层粉末在片状体金属粘结剂上面,然后向筒状加热块内注入近基层粉末,近基层粉末在切削层粉末上面,再向筒状加热块内注入远基层粉末,远基层粉末在近基层粉末上面;其中金属粘结剂与切削层粉末的重量比为1:4-6,切削层粉末由碳氧化陶瓷粉末(GOST 25003-81)BOK63同立方氮化硼微粉LPM 10/7按1:1比例均匀混合制成,近基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5-10%,钨纤维粉的质量占3-7%,余量是陶瓷粉末;远基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5-10%,钨纤维粉的质量占10-20%,余量是陶瓷粉末;
3、制备
将装有步骤2所述材料粉末的加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,保证金属粘结剂可以完全融化,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。
本发明生产出的刀具加工生铁СЧ21-40(GOST 1412-79),在加工模式为v=205 m/min,s=0.3 mm/转,t=1.5-2.0mm,无冷却条件下,HB为220,寿命为65分钟。
具体实施方式
1、选取钛含量为30%的钛银合金粉,向钛银合金加入铌粉,铌粉重量为钛银合金重量的0.5%,再混入铝粉,铝粉重量为钛银合金重量的3%,压成片状体金属粘结剂;将片状体金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,切削层粉末在片状体金属粘结剂上面,然后向筒状加热块内注入近基层粉末,近基层粉末在切削层粉末上面,再向筒状加热块内注入远基层粉末,远基层粉末在近基层粉末上面;其中金属粘结剂与切削层粉末的重量比为1:4,切削层粉末由碳氧化陶瓷粉末(GOST 25003-81)BOK63同立方氮化硼微粉LPM 10/7按1:1比例均匀混合制成,近基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占10%,钨纤维粉的质量占3%,余量是陶瓷粉末;远基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占10%,钨纤维粉的质量占10%,余量是陶瓷粉末;将装有上述材料粉末的加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,保证金属粘结剂可以完全融化,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。
2、选取钛含量为75%的钛银合金粉,向钛银合金加入铌粉,铌粉重量为钛银合金重量的0.75%,再混入铝粉,铝粉重量为钛银合金重量的6%,压成片状体金属粘结剂;将片状体金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,切削层粉末在片状体金属粘结剂上面,然后向筒状加热块内注入近基层粉末,近基层粉末在切削层粉末上面,再向筒状加热块内注入远基层粉末,远基层粉末在近基层粉末上面;其中金属粘结剂与切削层粉末的重量比为1: 6,切削层粉末由碳氧化陶瓷粉末(GOST 25003-81)BOK63同立方氮化硼微粉LPM 10/7按1:1比例均匀混合制成,近基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5%,钨纤维粉的质量占7%,余量是陶瓷粉末;远基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5%,钨纤维粉的质量占20%,余量是陶瓷粉末;将装有上述材料粉末的加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,保证金属粘结剂可以完全融化,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。
3、选取钛含量为50%的钛银合金粉,向钛银合金加入铌粉,铌粉重量为钛银合金重量的1%,再混入铝粉,铝粉重量为钛银合金重量的5%,压成片状体金属粘结剂;将片状体金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,切削层粉末在片状体金属粘结剂上面,然后向筒状加热块内注入近基层粉末,近基层粉末在切削层粉末上面,再向筒状加热块内注入远基层粉末,远基层粉末在近基层粉末上面;其中金属粘结剂与切削层粉末的重量比为1:5,切削层粉末由碳氧化陶瓷粉末(GOST 25003-81)BOK63同立方氮化硼微粉LPM 10/7按1:1比例均匀混合制成,近基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占7%,钨纤维粉的质量占5%,余量是陶瓷粉末;远基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占8%,钨纤维粉的质量占15%,余量是陶瓷粉末;将装有上述材料粉末的加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,保证金属粘结剂可以完全融化,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。
Claims (1)
1.一种钛银合金材料的制备方法,其特征在于由如下步骤完成:
(1)制备金属粘结剂
选取钛含量为30-75%的钛银合金粉,向钛银合金加入铌粉,铌粉重量为钛银合金重量的0.5-1%,再混入铝粉,铝粉重量为钛银合金重量的3-6%,压成片状体金属粘结剂;
(2)前期准备
将片状体金属粘结剂放入石墨材料制成的筒状加热块底部,向筒状加热块内注入切削层粉末,切削层粉末在片状体金属粘结剂上面,然后向筒状加热块内注入近基层粉末,近基层粉末在切削层粉末上面,再向筒状加热块内注入远基层粉末,远基层粉末在近基层粉末上面;其中金属粘结剂与切削层粉末的重量比为1:4-6,切削层粉末由碳氧化陶瓷粉末(GOST 25003-81)BOK63同立方氮化硼微粉LPM 10/7按1:1比例均匀混合制成,近基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5-10%,钨纤维粉的质量占3-7%,余量是陶瓷粉末;远基层由BOK63陶瓷粉末、立方氮化硼LPM10/7粉末与钨纤维粉混合制成,立方氮化硼粉末的质量占5-10%,钨纤维粉的质量占10-20%,余量是陶瓷粉末;
(3)制备
将装有步骤2所述材料粉末的加热块放入高温高压装置内,逐步加压使压力为30千帕,同时升温,保证金属粘结剂可以完全融化,自然冷却后金属粘结剂与材料粉末的合金形成刃具材料。