CN103725220A - 一种高韧性聚酯亚胺胶带 - Google Patents
一种高韧性聚酯亚胺胶带 Download PDFInfo
- Publication number
- CN103725220A CN103725220A CN201410001749.8A CN201410001749A CN103725220A CN 103725220 A CN103725220 A CN 103725220A CN 201410001749 A CN201410001749 A CN 201410001749A CN 103725220 A CN103725220 A CN 103725220A
- Authority
- CN
- China
- Prior art keywords
- polyester
- film
- adhesive tape
- tenacity
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及胶带技术领域,尤其涉及一种高韧性聚酯亚胺胶带,它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:聚对苯二甲酸乙二醇酯8~40%,硫酸钡8~12%,二氧化铁15~20%,二乙二醇15~20%,甲基丙烯酸甲酯9~15%,丁苯胶乳5~10%,苯乙烯5~10%,可有效提高粘着力、韧性和耐温程度。
Description
技术领域
本发明涉及胶带技术领域,尤其涉及一种高韧性聚酯亚胺胶带。
背景技术
聚酰亚胺胶带以聚酰亚胺薄膜为基材,在电子电工行业可用于较高要求的H级电机和变压器线圈绝缘包扎,耐高温线圈端部包扎固定,测温热电阻保护,电容及电线缠结和其它在高温工作条件下的粘结绝缘等。
现有的聚酯亚胺薄膜,存在粘着力、韧性、耐温程度不够的缺点。
发明内容
本发明的目的在于针对现有技术的不足而提供一种高韧性聚酯亚胺胶带,可有效提高粘着力、韧性和耐温程度。
为实现上述目的,本发明采用如下技术方案。
一种高韧性聚酯亚胺胶带,它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 18~40%
硫酸钡 8~12%
二氧化铁 15~20%
二乙二醇 15~20%
甲基丙烯酸甲酯 9~15%
丁苯胶乳 5~10%
苯乙烯 5~10% 。
优选的,所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 35%
硫酸钡 12%
二氧化铁 18%
二乙二醇 15%
甲基丙烯酸甲酯 10%
丁苯胶乳 5%
苯乙烯 5% 。
另一优选的,所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 25%
硫酸钡 12%
二氧化铁 19%
二乙二醇 20%
甲基丙烯酸甲酯 14%
丁苯胶乳 6%
苯乙烯 4% 。
另一优选的,所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 30%
硫酸钡 10%
二氧化铁 20%
二乙二醇 18%
甲基丙烯酸甲酯 12%
丁苯胶乳 5%
苯乙烯 5% 。
进一步的,所述粘胶层所用粘胶剂的组成及重量份如下:
E-44环氧树脂 80~110
乙二铵 10~20
邻苯二甲酸二丁酯 16~18
水 150~180
丁晴橡胶 4~6
瓷粉 20~25
碳酸氢钠 1~3
710醇醚磷酸酯 5~8
过硫酸铵 2~4。
本发明有益效果为:本发明所述的一种高韧性聚酯亚胺胶带,可有效提高粘着力、韧性和耐温程度。
具体实施方式
下面结合实施方式对本发明作进一步的说明。
实施例一,本发明所述一种高韧性聚酯亚胺胶带,它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 35%
硫酸钡 12%
二氧化铁 18%
二乙二醇 15%
甲基丙烯酸甲酯 10%
丁苯胶乳 5%
苯乙烯 5% 。
进一步的,所述粘胶层所用粘胶剂的组成及重量份如下:
E-44环氧树脂 90
乙二铵 15
邻苯二甲酸二丁酯 18
水 160
丁晴橡胶 5
瓷粉 22
碳酸氢钠 1
710醇醚磷酸酯 5
过硫酸铵 2。
实施例二,本发明所述一种高韧性聚酯亚胺胶带,它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 25%
硫酸钡 12%
二氧化铁 19%
二乙二醇 20%
甲基丙烯酸甲酯 14%
丁苯胶乳 6%
苯乙烯 4% 。
进一步的,所述粘胶层所用粘胶剂的组成及重量份如下:
E-44环氧树脂 1000
乙二铵 17
邻苯二甲酸二丁酯 17
水 165
丁晴橡胶 6
瓷粉 22
碳酸氢钠 1
710醇醚磷酸酯 7
过硫酸铵 3。
实施例三,本发明所述一种高韧性聚酯亚胺胶带,它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 30%
硫酸钡 10%
二氧化铁 20%
二乙二醇 18%
甲基丙烯酸甲酯 12%
丁苯胶乳 5%
苯乙烯 5% 。
进一步的,所述粘胶层所用粘胶剂的组成及重量份如下:
E-44环氧树脂 95
乙二铵 17
邻苯二甲酸二丁酯 18
水 170
丁晴橡胶 5
瓷粉 24
碳酸氢钠 3
710醇醚磷酸酯 6
过硫酸铵 4。
上述一种高韧性聚酯亚胺胶带,可有效提高初粘力、粘着力、韧性和耐温程度。实施例一至实施例三所述的一种高韧性聚酯亚胺胶带,其产品参数如下表。
本发明所述一种高韧性聚酯亚胺胶带,具有优良绝缘性能,有耐高温低温、耐酸碱、耐溶剂、防辐射等特性,广泛应用于电子电器、半导体等行业,用于电器绝缘、变压器线圈及锂电池正负极耳的固定、PCB上锡过炉高温保护金手指等。
以上所述仅是本发明的较佳实施方式,故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰,均包括于本发明专利申请范围内。
Claims (5)
1.一种高韧性聚酯亚胺胶带,其特征在于:它包括作为基材的聚酯亚胺薄膜,聚酯亚胺薄膜的一面设有粘胶层,聚酯亚胺薄膜的另一面复合有聚酯膜,聚酯膜的另一面设有离型纸;所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 18~40%
硫酸钡 8~12%
二氧化铁 15~20%
二乙二醇 15~20%
甲基丙烯酸甲酯 9~15%
丁苯胶乳 5~10%
苯乙烯 5~10% 。
2.根据权利要求1所述的一种高韧性聚酯亚胺胶带,其特征在于:所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 35%
硫酸钡 12%
二氧化铁 18%
二乙二醇 15%
甲基丙烯酸甲酯 10%
丁苯胶乳 5%
苯乙烯 5% 。
3.根据权利要求1所述的一种高韧性聚酯亚胺胶带,其特征在于:所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 25%
硫酸钡 12%
二氧化铁 19%
二乙二醇 20%
甲基丙烯酸甲酯 14%
丁苯胶乳 6%
苯乙烯 4% 。
4.根据权利要求1所述的一种高韧性聚酯亚胺胶带,其特征在于:所述聚酯膜由以下重量百分比的原料制成:
聚对苯二甲酸乙二醇酯 30%
硫酸钡 10%
二氧化铁 20%
二乙二醇 18%
甲基丙烯酸甲酯 12%
丁苯胶乳 5%
苯乙烯 5% 。
5.根据权利要求1至4任一项所述的一种高韧性聚酯亚胺胶带,其特征在于:所述粘胶层所用粘胶剂的组成及重量份如下:
E-44环氧树脂 80~110
乙二铵 10~20
邻苯二甲酸二丁酯 16~18
水 150~180
丁晴橡胶 4~6
瓷粉 20~25
碳酸氢钠 1~3
710醇醚磷酸酯 5~8
过硫酸铵 2~4。